Abstract:The problem of uncontrolled oxygen contamination of intermetallic TiAl ingots is considered for the application of crucibles and molds based on traditional oxide ceramics. A synthesized Ti-45.9Al-8Nb (at %) alloy is solidified in alternative oxygen-free crucibles made of high-purity aluminum nitride (99.99% AlN) upon holding at 1670°C for 5, 12, and 25 min and subsequent quenching in a high-purity argon atmosphere. The initial material and the solidified ingots are studied by scanning electron microscopy, optical microscopy, X-ray diffraction, electron-probe microanalysis, and gas-content chemical analysis. The key features of the interaction of the TiAl-Nb melt with AlN ceramics are revealed. Partial thermal dissociation of the crucible material according to the reaction AlN → Al + N and the reaction of atomic nitrogen with the melt lead to the formation of a solid 6.4-μm-thick TiN coating on the ingot surface and provide perfect wettability of the crucible by the melt and easy removal of solidified casting items from the mold. The TiN coating serves as a diffusion barrier that hinders the diffusion of nitrogen and residual oxygen from the pores in the crucible toward the melt. As a result, no oxide particles are detected in the ingots. However, few single microprecipitates of two nitride phases ((Ti,Al)xNy, NbN) are detected in the near-bottom region, 300 μm thick, in the alloy after holding at 1670°C for 25 min. The total oxygen contamination in a two-phase α2 + γ ingot does not exceed 1100 wt ppm, which is 1.5–2 times lower than that obtained in the experiments performed with modern advanced oxide crucibles made of yttrium ceramics Y2O3. AlN is shown to be a promising crucible material that can be considered as an alternative to oxide ceramics in the metallurgy of TiAl intermetallics.

Chemical compatibility of a TiAl-Nb melt with oxygen-free crucible ceramics made of aluminum nitride

Anti-corrosion AlN ceramic crucible with excellent thermal shock resistance for induction melting of TiAl alloy

The Durability of Various Crucible Materials for Aluminum Nitride Crystal Growth by Sublimation

Crucible Materials for Growth of Aluminum Nitride Crystals

Preparation of a (Ca,Sr,Ba)ZrO3 Crucible by Slip Casting for the Vacuum Induction Melting of NiTi Alloy

Oxidation Resistance of TiAl-Inconel625 Graded Alloying Layer

The Study on Interaction Mechanisms Between Ti48al2cr2nb Alloy and Y2o3 Ceramic Crucibles with Good Thermal Shock Resistance: Assessing a Novel, Cost-Effective Approach to the Preparation of High-Performance Tial Alloys

Initial Oxidation Behavior in Air of TiAl-2Nb and TiAl-8Nb Alloys Produced by Electron Beam Melting

High-Temperature Oxidation of NbTi-Bearing Refractory Medium- and High-Entropy Alloys

Preparation and application evaluation of La2O3-doped Y2O3 crucible materials for melting TiAl alloys

Reaction of a Molten Cr-Si-Base Alloy with Ceramics and a High Entropy Oxide

Interaction Between CA6-MA Crucible and Molten Wrought Ni-based Superalloys

High-Temperature Wettability and Interactions between Y-Containing Ni-Based Alloys and Various Oxide Ceramics

Investigation on the Microstructure and High-Temperature Properties of AlN Coating Through Oxygen Addition

Interaction between CA 6 -MA crucible and molten wrought Ni-based superalloys

In-situ Synthesis of TiN and its Effects on Fe-12Cr-6Al in Laser Powder Bed Fusion

Isothermal Oxidation Resistance of As-cast NiAl and NiAl-(Cr, Mo) Eutectic Alloys at 1000°C

Interactions between TiAl alloys and yttria refractory material in casting process

The Influence of Al and Nb on the Low Oxygen Pressure Pre-Oxidation Behavior of Fe-35Ni-20Cr-xAl-yNb Alloys at 1000 °C

High-Temperature Oxidation Resistance of High-Nb TiAl-Based Alloy