Abstract:To reveal the refinement mechanism of Ti2AlC particle by in -situ Y2O3 in the liquid region and the improvement mechanisms of refined Ti2AlC in solid-state phase transformation process, Ti-46Al-8 Nb-2.6 C-xY alloys were prepared. Microstructures were observed by SEM, XRD and TEM, and the mechanical properties were examined. Calculated results indicated that the phase boundary energy of in -situ Y2O3 combined with TiC was low in the liquid region. TiC particle was formed initially, followed by Y2O3 particle. The Y2O3 particle moved to the surface of TiC particle to inhibit its growth, which left small -sized TiC nucleation substrate for the formation of Ti2AlC. The orientation relationship was [2200]Ti2AlC//[066]Y2O3. A stepped atomic diffusion zone was formed in the interface of Y2O3 and Ti2AlC to inhibit lateral and longitudinal growth of Ti2AlC. As Y increased from 0.02 to 0.1 at%, the average aspect ratio of Ti2AlC particles decreased from 7.7 to 3.4, the Ti2AlC content with the aspect ratio of 1-5 increased from 13.7 to 91.3%. The lamellar colony size and lamellar spacing reduced from 47.5 to 26.0 mu m and 0.74 to 0.58 mu m, respectively. Both Y2O3 and refined Ti2AlC served as heterogeneous nucleation sites and inhibited the lateral thickening rate of gamma lath. The Y -type YAl2 phase was formed as Y content exceeded 0.1 at%. The compressive strength and Vickers hardness were improved from 1801 to 2201 MPa and 443.2 to 464.5 HV, respectively. However, the subsequent decrease in strength was caused by the embrittlement of grain boundary after the precipitation of YAl2 phase. The significant refinement of Ti2AlC and lamellar colony by insitu Y2O3 and the precipitation strengthening of Ti2AlC contributed to the mechanical properties.

The Study on Interaction Mechanisms Between Ti48al2cr2nb Alloy and Y2o3 Ceramic Crucibles with Good Thermal Shock Resistance: Assessing a Novel, Cost-Effective Approach to the Preparation of High-Performance Tial Alloys

Interactions between TiAl alloys and yttria refractory material in casting process

Microstructure formation and interface characteristics of directionally solidified TiAl-Si alloys in alumina crucibles with a new Y 2 O 3 skull-aided technology

Preparation and application evaluation of La2O3-doped Y2O3 crucible materials for melting TiAl alloys

Improvement and Application of Y2O3 Directional Solidification Crucible

Evaluation of Yttria Applicability as a Crucible for Induction Melting of TiAl Alloy

Interface interaction during the preparation of TiAl-(Nb, V) quaternary intermetallic single crystals by directional solidification based on Y2O3 doped BaZrO3/Al2O3 composite ceramic mold

High Temperature Tensile Properties and Fracture Behavior of Y2O3-bearing Ti-48Al-2Cr-2Nb Alloy

Study of Interfacial Reaction Between TiAl Alloys and Four Ceramic Molds

Interfacial reactions between titanium–copper melt and crucible oxides

A novel potential ceramic material for melting Ti6Al4V alloy: A solid solution of BaZrO3 and CaZrO3

Effect of Nano Y2O3 Addition on Microstructure and Room Temperature Tensile Properties of Ti–48Al–2Cr–2Nb Alloy

High-Temperature Wettability and Interactions between Y-Containing Ni-Based Alloys and Various Oxide Ceramics

Enhanced thermal shock resistance of ZrO2-reinforced Al2O3–CaAl12O19 composites prepared from ferrotitanium slag: Crack propagation resistance mechanisms

Thermal Shock Resistance of Nanocrystalline and Ultrafine-Grained W-Y2O3-Ti Alloys

Performance of BaZrO3/Y2O3 dual-phase refractory applied to TiAl alloy melting

Sintering behavior and thermal shock resistance of aluminum titanate (Al2TiO5)-toughened MgO-based ceramics

Anti-corrosion AlN ceramic crucible with excellent thermal shock resistance for induction melting of TiAl alloy

High-temperature performance in Al2O3–Cr2O3 refractories: Effect of Al2TiO5

Refining Ti2AlC in the Liquid Region and Improving the Microstructure and Mechanical Properties of Ti-46Al-8 Nb-2.6 C Alloy by Adding Y

Application of zirconia ceramic moulds for investment casting of TiAl alloys