Abstract:Electron beam heat source has certain advantages in processing some special high-performance materials because of its high energy efficiency and the ability to use its own high scanning rates to maintain a high temperature environment in a vacuum environment. However, defects formation hinders further application of Electron Beam Additive Manufacturing (EBAM). Unstable melt pools will lead to some processing stability related defects, such as smoking, spatter, lower adhesion, high surface roughness, high residual stress and deformation, and element evaporation, which in turn cause defects at the microstructural level such as porosity, anisotropy and heterogeneity of microstructure, cracks, and dislocations. Moreover, the defect formation process of EBAM in high preheating temperature and high vacuum environment is more complex and difficult to fully understand. Therefore, establishing the relationship between defects formation mechanisms and processing stability is of great significance to control defects and improve properties. Based on electron beam-material interaction factors, this paper systematically described these defects formation mechanisms in Selective Electron Beam Melting (SEBM) and Electron Beam Freeform Fabrication (EBF 3 ) technology. The underlying causes of the effect of defects on the anisotropy of tensile and fatigue properties and the heterogeneity of microhardness were discussed. In addition, some in-process control methods were summarised to control defects in terms of the factors affecting the melt pool dynamics, including control of thermal process conditions during deposition, powder modification and in-situ wire alloying, and in-process online assistance. It can be stressed that these methods will be further research points for EBAM in the future and can drive the need for further applications of EBAM technology to refine additive manufacturing in the special high performance materials field.

The Application of Electron-Beam Welding in Pellet Mold Preparation

Technology Research of Direct Metal Forming Based on Electron Beam

Direct Metal Part Forming of 316L Stainless Steel Powder by Electron Beam Selective Melting

A Review of the Development of Electron Beam Powder Bed Fusion Technology

Modeling and numerical study of the molten pool dynamics during scanning electron beam welding of aluminum alloys: Physical mechanism, prediction and parameter selection

Effects of Electron Beam Local Post-Weld Heat-Treatment on the Microstructure and Properties of 30crmnsini2a Steel Welded Joints

Numerical Investigation on Molten Pool Dynamics and Defect Formation in Electron Beam Welding of Aluminum Alloy

PRODUCED THREE-DIMENSIONAL METAL PARTS BY ELECTRON BEAM SELECTIVE MELTING

Electron beam machining of microsystem products

Selective Electron Beam Melting Technique and Its Application

Preparation method of composite filling layer and method for welding titanium and stainless steel by adopting electronic beam

Dissimilar Welding and Joining of Cemented Carbides

A Surface Quality Optimization Strategy Based on a Dedicated Melt-Pool Control Via the Dashed-Scan Contouring Technique in Electron Beam Powder Bed Fusion

Electron beam pressurizing connection method for aluminum alloy and particle-reinforced aluminum matrix composite material

The Applications of the Electron Beam Machining Technology in Research of Materials Science

Reduction of Residual Stress and Deformation in Electron Beam Welding by Using Multiple Beam Technique

Electron beam metal additive manufacturing: Defects formation and in-process control

Microstructures and Formation of Electron Beam Welding Joint of QCr0.8 and 1Cr21ni5ti

Investigation on electron beam welding of dissimilar wrought/selective laser melting AISI 304 stainless steel plates

The Development of Electron Beam and Laser Hybrid Selective Melting Equipment

Numerical investigation of the impact of thermoelectric effect on electron beam welding of dissimilar materials