Abstract:The growth stress induced by thermally grown oxide (TGO) is one of the main reasons for the failure of thermal barrier coatings (TBCs). In this study, the failure behavior of TBCs was examined based on different growth modes of TGO. A TBC thermo-mechanical model with a simplified sinusoidal interface morphology was established by the secondary development of a numerical simulation. The plasticity and creep behavior of materials were considered. Based on the subroutine development, the non-uniform growth of the TGO layer was realized. Cohesive elements were also applied to the TC/TGO interface. The stress distribution and evolution at the TC/TGO interface were investigated. Then, the cracking behavior near the interface was studied. The results show that lateral growth causes the off-valley site to replace the previous off-peak site as a vulnerable site. The non-uniform growth accelerates damage in the off-valley site, which leads to a change in the failure behavior. These results will provide significant guidance for understanding the TBC failure and the development of advanced TBCs.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the failure behavior of thermal barrier coatings (TBCs) caused by the growth of thermally grown oxides (TGO) during service. Specifically, the paper focuses on the influence of different growth modes of TGO on the failure behavior of TBCs. Through numerical simulation, the influence of the uniform and non - uniform growth (including lateral growth) of TGO on the stress distribution and crack propagation behavior of TBCs was studied. ### Main problems: 1. **The influence of TGO growth stress on TBCs failure**: - The growth stress of thermally grown oxides (TGO) is one of the main reasons for the failure of TBCs. TGO is formed at high temperatures, and due to the diffusion of oxygen elements and the chemical reaction with aluminum elements in the bonding layer, the growth of the TGO layer occurs. - The growth of TGO not only increases the thickness of the coating but also introduces significant growth stresses. These stresses will lead to stress concentration at the coating interface, thus causing the generation and propagation of cracks. 2. **The influence of different TGO growth modes on the failure behavior of TBCs**: - By establishing a finite - element model, the paper considered different growth modes of TGO (uniform growth, non - uniform growth, lateral growth) and studied the influence of these growth modes on the stress distribution and crack propagation behavior of TBCs. - Special attention was paid to the growth rate differences of TGO in different regions (peak regions and valley regions), and how this difference affects the stress distribution and crack propagation behavior of the coating. ### Specific objectives: - **Understand the influence of TGO growth modes on the stress distribution of TBCs**: - Through numerical simulation, study the stress distribution characteristics of TGO under different growth modes, especially the influence of the growth rate difference of TGO in peak regions and valley regions on the stress distribution of the coating. - **Analyze the influence of TGO growth modes on crack propagation behavior**: - By introducing cohesive elements to simulate the delamination behavior of the coating interface, study the crack initiation and propagation behavior under different TGO growth modes. - Analyze the influence of lateral growth on crack propagation behavior, especially how lateral growth accelerates the crack propagation in the valley region, leading to the early failure of the coating. ### Research methods: - **Numerical simulation**: - A finite - element model with four levels (top coating, bonding layer, TGO layer, and substrate) was established using ABAQUS software. - The plastic and creep behaviors of materials were considered, and the non - uniform growth and lateral growth of TGO were realized through subroutine development. - Cohesive elements were introduced to simulate the delamination behavior of the coating interface, and the quadratic nominal stress criterion was used to describe the crack initiation and propagation behavior. ### Expected results: - **A more comprehensive understanding of the influence of TGO growth modes on the failure mechanism of TBCs**: - Through numerical simulation, obtain detailed data on the stress distribution and crack propagation behavior of the coating under different TGO growth modes. - Provide important guidance for understanding the failure mechanism of TBCs and theoretical support for the development of more advanced TBCs systems. In summary, this paper aims to systematically study the influence of different growth modes of TGO on the failure behavior of TBCs through numerical simulation, and provide a scientific basis for improving the performance and life of TBCs.

Comprehensive Understanding of the Effect of TGO Growth Modes on Thermal Barrier Coating Failure Based on a Simulation

Effect of Thermal Growth Oxide Composition and Morphology on Local Stresses in Thermal Barrier Coatings

Modeling 3D TGO dynamic growth and stresses and the resulting modes of buckling failure in thermal barrier coatings

Effects of TGO growth on the stress distribution and evolution of three-dimensional cylindrical thermal barrier coatings based on finite element simulations

Model construction and effect of thermally grown oxide dynamic growth on distribution of thermal barrier coatings

TGO stress growth for Pt-modified aluminide bond coats during high temperature oxidation

Construction of three-dimensional dynamic growth TGO (thermally grown oxide) model and stress simulation of 8YSZ thermal barrier coating

Influence of non-uniform feature of thermally grown oxide thickness on the local stress state and cracking behavior in TBC

Vertical Stress State Analysis and Fatigue Life Prediction of Thermal Barrier Coating Considering TGO with Nonuniform Thickness

Chemo-thermo-mechanical modeling of EB-PVD TBC failure subjected to isothermal and cyclic thermal exposures

Study of stress-driven cracking behavior and competitive crack growth in functionally graded thermal barrier coatings

Numerical Analysis of stress evolution in thermal barrier coating system during two-stage growth of heterogeneous oxide

Analysis On Stress Distribution Of Thermal Barrier Coating System With Thermal Gradient Mechanical Fatigue

Effects of TGO growth on the interface stress distribution based on 3D pores in TBC ceramics layer

Effect of Interface Curvature on Local Growth Behavior and Stress of Thermal Barrier Coatings

Effect of the thermally grown oxide and interfacial roughness on stress distribution in environmental barrier coatings

Influence factors of high temperature oxidation for Pt-modified-aluminide bond coatings

Thermomechanical and Thermal Gradient Mechanical Fatigue Lifetime of Thermal Barrier Coating Systems

Thermal shock behaviors and failure mechanisms of EB-PVD thermal barrier coatings using radiant heating

Cross-scale modeling and elasto-plastic mechanical properties of TBC with 3D hill-like interface

Phase-Field Modeling of Thermally-Grown Oxide and Damage Evolution in Environmental Barrier Coatings