Analysis On Stress Distribution Of Thermal Barrier Coating System With Thermal Gradient Mechanical Fatigue

Yang Zhou,Chen Guo-Feng,Li Chang-Peng,Luo Jian-Bin

DOI: https://doi.org/10.11933/j.issn.1007-9289.20170913001

2018-01-01

China surface engineering

Abstract:The thermal barrier coatings systems (TBCs) were deposited on the IN738 nickel-based superalloy substrate, and the stress distribution and evolution under the thermal gradient cyclic loading and the thermal gradient mechanical fatigue were evaluated for the TBCs respectively. The stress distribution at the thermally growth oxidation (TGO) was analyzed by the finite element analysis method to predict the failure behavior of the TBCs under different loading conditions. The results show that the peak region of the TGO is subject to the major axial tensile stress during the heating process under the thermal cyclic loading. The fatigue crack started from the peak regions and TBCs fails with the delamination between the layers. The thermal cyclic associated with strain loading leads to the alteration of the characteristic and the amplitude of the axial stress. Under the thermal gradient cyclic loading, the crack normal to the interface propagates primarily in the metallic bond coat parallel to the interface by the combined effect of the remarkably increasing axial stress and radial tensile stress, hence the spallation of the ceramic layer occurrs. The comparative analysis of the thermal mechanical loading with in-phase and out-of-phase demonstrated that the TBCs will be more likely to fail due to the tensile mean stress in a cycle in the opposite phase.