Abstract:Oxygen activation is a key step in the catalytic oxidation of formaldehyde (HCHO) at room temperature. In this study, we synthesized a carbon/Co3O4 nanocomposite (C-Co3O4) as a solution to the insufficient capability of pristine Co3O4 (P-Co3O4) to activate oxygen for the first time. Oxygen activation was improved via carbon preventing the agglomeration of Co3O4 nanoparticles, resulting in small particles (approximately 7.7 nm) and more exposed active sites (oxygen vacancies and Co3+). The removal efficiency of C-Co3O4 for 1 ppm of HCHO remained above 90%, whereas P-Co3O4 was rapidly deactivated. In static tests, the CO2 selectivity of C-Co3O4 was close to 100%, far exceeding that of P-Co3O4 (42%). Various microscopic analyses indicated the formation and interaction of a composite structure between the C and Co3O4 interface. The carbon composite caused a disorder on the surface lattice of Co3O4, constructing more oxygen vacancies than P-Co3O4. Consequently, the surface reducibility of C-Co3O4 was improved, as was its ability to continuously activate oxygen and H2O into reactive oxygen species (ROS). We speculate that accelerated production of ROS helped rapidly degrade intermediates such as dioxymethylene, formate, and carbonate into CO2. In contrast, carbonate accumulation on P-Co3O4 surfaces containing less ROS may have caused P-Co3O4 inactivation. Compared with noble nanoparticles, this study provides a transition metal-based nanocomposite for HCHO oxidation with high efficiency, high selectivity, and low cost, which is meaningful for indoor air purification.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.est.1c00490?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.est.1c00490</a>.Additional detail information including catalyst characterizations, low-concentration HCHO removal efficiency in different relative humidities, Co K-edge k3χ spectra, TG curves, N2 adsorption–desorption isotherms, SEM, TEM images and, EDS mapping, CV curves, and changes of surface OH and H2O peak intensity during in situ DRIFTS studies (<a class="ext-link" href="/doi/suppl/10.1021/acs.est.1c00490/suppl_file/es1c00490_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Pt/NiCo2O4 nanowire arrays on Ni foam as catalysts for efficient formaldehyde oxidation at room temperature

Hierarchical Ni−Al Hydrotalcite Supported Pt Catalyst for Efficient Catalytic Oxidation of Formaldehyde at Room Temperature

Electrospinning synthesis of Co 3 O 4 porous nanofiber monolithic catalysts for the room-temperature indoor catalytic oxidation of formaldehyde at low concentrations

Pt-Promoted Tungsten Carbide Nanostructures on Mesoporous Pinewood-Derived Activated Carbon for Catalytic Oxidation of Formaldehyde at Low Temperatures

Catalytic performance and mechanism of bismuth molybdate nanosheets decorated with platinum nanoparticles for formaldehyde decomposition at room temperature

The practical utility of ternary nickel-cobalt-manganese oxide-supported platinum catalysts for room-temperature oxidative removal of formaldehyde from the air

MnCo-Layered double hydroxides nanosheets supported Pd nanoparticles for complete catalytic oxidation of formaldehyde at room temperature

Facet- and defect-engineered Pt/Fe2O3 nanocomposite catalyst for catalytic oxidation of airborne formaldehyde under ambient conditions

Exceptional formaldehyde oxidation at room temperature on Co single-atom functionalized TiO 2 nanowires via highly effective O 2 activation

A CuNi Alloy-Carbon Layer Core-Shell Catalyst for Highly Efficient Conversion of Aqueous Formaldehyde to Hydrogen at Room Temperature

Deactivation and Regeneration of Pt/Tio2 Nanosheet-Type Catalysts with Exposed (001) Facets for Room Temperature Oxidation of Formaldehyde

Improved Oxygen Activation over a Carbon/Co 3 O 4 Nanocomposite for Efficient Catalytic Oxidation of Formaldehyde at Room Temperature

Efficient Decomposition of Formaldehyde on Ni−Al Hydrotalcite/AlOOH Nanocomposites Decorated with Pt Nanoparticles at Ambient Temperature

Fluorescent light enhanced graphitic carbon nitride/ceria with ultralow-content platinum catalyst for oxidative decomposition of formaldehyde at ambient temperature

Insights into High-Performance Monolith Catalysts of Co3O4 Nanowires Grown on Nickel Foam with Abundant Oxygen Vacancies for Formaldehyde Oxidation

Enhanced Catalytic Activity Of Hierarchically Macro-/Mesoporous Pt/Tio2 Toward Room-Temperature Decomposition Of Formaldehyde

Alkali-Modified Non-Precious Metal 3D-Nico2o4 Nanosheets for Efficient Formaldehyde Oxidation at Low Temperature

Efficiently catalytic purification of indoor formaldehyde upon Co-N sites derived from ZIF-67 carbonization

Graphene Oxide/fe2o3 Nanoplates Supported Pt for Enhanced Room-Temperature Oxidation of Formaldehyde

Highly dispersed Fe-Ce mixed oxide catalysts confined in mesochannels toward low-temperature oxidation of formaldehyde

Catalytic oxidation of formaldehyde on nano-Co 3 O 4 , 2 DCo 3 O 4 , and 3 DCo 3 O 4 catalysts