Improved Oxygen Activation over a Carbon/Co 3 O 4 Nanocomposite for Efficient Catalytic Oxidation of Formaldehyde at Room Temperature

Rong Li,Yu Huang,Dandan Zhu,Wingkei Ho,Junji Cao,Shuncheng Lee

DOI: https://doi.org/10.1021/acs.est.1c00490

2021-03-04

Abstract:Oxygen activation is a key step in the catalytic oxidation of formaldehyde (HCHO) at room temperature. In this study, we synthesized a carbon/Co3O4 nanocomposite (C-Co3O4) as a solution to the insufficient capability of pristine Co3O4 (P-Co3O4) to activate oxygen for the first time. Oxygen activation was improved via carbon preventing the agglomeration of Co3O4 nanoparticles, resulting in small particles (approximately 7.7 nm) and more exposed active sites (oxygen vacancies and Co3+). The removal efficiency of C-Co3O4 for 1 ppm of HCHO remained above 90%, whereas P-Co3O4 was rapidly deactivated. In static tests, the CO2 selectivity of C-Co3O4 was close to 100%, far exceeding that of P-Co3O4 (42%). Various microscopic analyses indicated the formation and interaction of a composite structure between the C and Co3O4 interface. The carbon composite caused a disorder on the surface lattice of Co3O4, constructing more oxygen vacancies than P-Co3O4. Consequently, the surface reducibility of C-Co3O4 was improved, as was its ability to continuously activate oxygen and H2O into reactive oxygen species (ROS). We speculate that accelerated production of ROS helped rapidly degrade intermediates such as dioxymethylene, formate, and carbonate into CO2. In contrast, carbonate accumulation on P-Co3O4 surfaces containing less ROS may have caused P-Co3O4 inactivation. Compared with noble nanoparticles, this study provides a transition metal-based nanocomposite for HCHO oxidation with high efficiency, high selectivity, and low cost, which is meaningful for indoor air purification.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.est.1c00490?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.est.1c00490</a>.Additional detail information including catalyst characterizations, low-concentration HCHO removal efficiency in different relative humidities, Co K-edge k3χ spectra, TG curves, N2 adsorption–desorption isotherms, SEM, TEM images and, EDS mapping, CV curves, and changes of surface OH and H2O peak intensity during in situ DRIFTS studies (<a class="ext-link" href="/doi/suppl/10.1021/acs.est.1c00490/suppl_file/es1c00490_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

environmental sciences,engineering, environmental

What problem does this paper attempt to address?

This paper aims to solve the problem of insufficient oxygen activation ability in the catalytic oxidation process of formaldehyde (HCHO) at room temperature. Specifically, by synthesizing carbon/cobaltosic oxide nanocomposites (C - Co₃O₄), the paper has for the first time solved the problem of insufficient ability of pure cobaltosic oxide (P - Co₃O₄) in activating oxygen. The addition of carbon prevents the aggregation of Co₃O₄ nanoparticles, thus forming smaller particles (about 7.7 nm) and more exposed active sites (oxygen vacancies and Co³⁺). These improvements have increased the removal efficiency of 1 ppm formaldehyde by C - Co₃O₄, making its CO₂ selectivity close to 100% in static tests, far exceeding the performance of P - Co₃O₄ (42%). In addition, the paper also explores how the carbon composite can construct more oxygen vacancies by causing the disorder of the surface lattice of Co₃O₄, thereby improving its surface reducibility and the ability to continuously activate oxygen and water to generate reactive oxygen species (ROS). The study speculates that the rapidly generated ROS helps to quickly degrade intermediate products such as dimethoxymethane, formate and carbonate into CO₂. In contrast, the P - Co₃O₄ surface may be deactivated due to carbonate accumulation because of fewer ROS. Overall, this study provides an efficient, highly selective and low - cost transition - metal - based nanocomposite for indoor formaldehyde oxidation, which is of great significance for air purification.

Improved Oxygen Activation over a Carbon/Co 3 O 4 Nanocomposite for Efficient Catalytic Oxidation of Formaldehyde at Room Temperature

Catalytic Ozonation of Formaldehyde with an Oxygen-Vacancy-Rich MnOx/γ-Al2O3 Catalyst at Room Temperature

Synergetic Molecular Oxygen Activation and Catalytic Oxidation of Formaldehyde over Defective MIL-88B(Fe) Nanorods at Room Temperature

Formaldehyde Oxidation over Co@N-Doped Carbon at Room Temperature: Tunable Co Size and Intensified Surface Electron Density

Highly exposed metal atomic active sites in Al2O3/CoNC: Modify reaction pathways by coupling oxygen species

Exceptional formaldehyde oxidation at room temperature on Co single-atom functionalized TiO 2 nanowires via highly effective O 2 activation

Cobalt Nanoparticles Encapsulated in Porous Nitrogen-Doped Carbon: Oxygen Activation and Efficient Catalytic Removal of Formaldehyde at Room Temperature

Catalytic Oxidation of Formaldehyde on Ultrathin Co3O4 Nanosheets at Room Temperature: Effect of Enhanced Active Sites Exposure on Reaction Path

Improved oxygen activation over metal–organic-frameworks derived and zinc-modulated Co@NC catalyst for boosting indoor gaseous formaldehyde oxidation at room temperature

Facet- and defect-engineered Pt/Fe2O3 nanocomposite catalyst for catalytic oxidation of airborne formaldehyde under ambient conditions

Catalytic oxidation of formaldehyde on nano-Co 3 O 4 , 2 DCo 3 O 4 , and 3 DCo 3 O 4 catalysts

Oxygen vacancy–engineered δ-MnO /activated carbon for room-temperature catalytic oxidation of formaldehyde

Electrospinning synthesis of Co 3 O 4 porous nanofiber monolithic catalysts for the room-temperature indoor catalytic oxidation of formaldehyde at low concentrations

Surface Lattice Oxygen Activation by Nitrogen-Doped Manganese Dioxide as an Effective and Longevous Catalyst for Indoor HCHO Decomposition

Oxygen vacancy-rich K-Mn3O4@CeO2 catalyst for efficient oxidation degradation of formaldehyde at near room temperature

The Catalytic and Adsorptive Synergistic Effect of Oxygen-Vacancy-Rich MnO x /C Catalysts for HCHO Oxidation at Room Temperature

Complete oxidation of formaldehyde over a Pd/CeO2 catalyst at room temperature: tunable active oxygen species content by non-thermal plasma activation

Promotion of Formaldehyde Oxidation over Ag Catalyst by Fe Doped MnO X Support at Room Temperature

Efficient MnOx supported on coconut shell activated carbon for catalytic oxidation of indoor formaldehyde at room temperature

Progress in Research on Catalysts for Catalytic Oxidation of Formaldehyde

Insights into High-Performance Monolith Catalysts of Co3O4 Nanowires Grown on Nickel Foam with Abundant Oxygen Vacancies for Formaldehyde Oxidation