Abstract:Oxygen activation is a key step in the catalytic oxidation of formaldehyde (HCHO) at room temperature. In this study, we synthesized a carbon/Co3O4 nanocomposite (C-Co3O4) as a solution to the insufficient capability of pristine Co3O4 (P-Co3O4) to activate oxygen for the first time. Oxygen activation was improved via carbon preventing the agglomeration of Co3O4 nanoparticles, resulting in small particles (approximately 7.7 nm) and more exposed active sites (oxygen vacancies and Co3+). The removal efficiency of C-Co3O4 for 1 ppm of HCHO remained above 90%, whereas P-Co3O4 was rapidly deactivated. In static tests, the CO2 selectivity of C-Co3O4 was close to 100%, far exceeding that of P-Co3O4 (42%). Various microscopic analyses indicated the formation and interaction of a composite structure between the C and Co3O4 interface. The carbon composite caused a disorder on the surface lattice of Co3O4, constructing more oxygen vacancies than P-Co3O4. Consequently, the surface reducibility of C-Co3O4 was improved, as was its ability to continuously activate oxygen and H2O into reactive oxygen species (ROS). We speculate that accelerated production of ROS helped rapidly degrade intermediates such as dioxymethylene, formate, and carbonate into CO2. In contrast, carbonate accumulation on P-Co3O4 surfaces containing less ROS may have caused P-Co3O4 inactivation. Compared with noble nanoparticles, this study provides a transition metal-based nanocomposite for HCHO oxidation with high efficiency, high selectivity, and low cost, which is meaningful for indoor air purification.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.est.1c00490?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.est.1c00490</a>.Additional detail information including catalyst characterizations, low-concentration HCHO removal efficiency in different relative humidities, Co K-edge k3χ spectra, TG curves, N2 adsorption–desorption isotherms, SEM, TEM images and, EDS mapping, CV curves, and changes of surface OH and H2O peak intensity during in situ DRIFTS studies (<a class="ext-link" href="/doi/suppl/10.1021/acs.est.1c00490/suppl_file/es1c00490_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Complete oxidation of formaldehyde over a Pd/CeO2 catalyst at room temperature: tunable active oxygen species content by non-thermal plasma activation

Efficient activation of Pd/CeO2 catalyst by non-thermal plasma for complete oxidation of indoor formaldehyde at room temperature

Catalytic Ozonation of Formaldehyde with an Oxygen-Vacancy-Rich MnOx/γ-Al2O3 Catalyst at Room Temperature

High surface area Au/CeO 2 catalysts for low temperature formaldehyde oxidation

Highly dispersed Fe-Ce mixed oxide catalysts confined in mesochannels toward low-temperature oxidation of formaldehyde

Efficient elimination of formaldehyde over Pt/Fe3O4 catalyst at room temperature

Mechanistic Study on Formaldehyde Removal over Pd/TiO2 Catalysts: Oxygen Transfer and Role of Water Vapor

Pt/MnOx–CeO2 catalysts for the complete oxidation of formaldehyde at ambient temperature

Oxygen vacancy-rich K-Mn3O4@CeO2 catalyst for efficient oxidation degradation of formaldehyde at near room temperature

Plasma-catalytic Oxidation of Diluted Formaldehyde over Cu-Ce Oxide Catalysts

Complete oxidation of formaldehyde at room temperature over Ag-loaded octahedral molecular sieve synthesized from solvent-free route

Complete Oxidation of Formaldehyde at Room Temperature Using Tio2 Supported Metallic Pd Nanoparticles

Progress in Research on Catalysts for Catalytic Oxidation of Formaldehyde

Fluorescent light enhanced graphitic carbon nitride/ceria with ultralow-content platinum catalyst for oxidative decomposition of formaldehyde at ambient temperature

Facet- and defect-engineered Pt/Fe2O3 nanocomposite catalyst for catalytic oxidation of airborne formaldehyde under ambient conditions

Ozone catalytic oxidation of low-concentration formaldehyde over ternary Mn-Ce-Ni oxide catalysts modified with FeOx

Two-step hydrothermal synthesis of highly active MnOx-CeO2 for complete oxidation of formaldehyde

Regulation of Mixed Ag Valence State by Non-Thermal Plasma for Complete Oxidation of Formaldehyde

Removal of Formaldehyde Using Highly Active Pt/TiO2 Catalysts Without Irradiation

Improved Oxygen Activation over a Carbon/Co 3 O 4 Nanocomposite for Efficient Catalytic Oxidation of Formaldehyde at Room Temperature

Formaldehyde Ambient-Temperature Decomposition over Pd/Mn 3 O 4 -MnO Driven by Active Sites' Self-Tandem Catalysis