Catalytic oxidation of formaldehyde on nano-Co 3 O 4 , 2 DCo 3 O 4 , and 3 DCo 3 O 4 catalysts

Bingyang Bai,Junhua Li

2014-01-01

Abstract:Introduction Formaldehyde (HCHO) emitted from the widely used building and decorative materials is becoming a major indoor pollutant in airtight buildings, and it could cause serious and hazardous effects on human health. Thus it is essential for human health to remove indoor formaldehyde [1]. Currently, the catalytic materials used in HCHO catalytic oxidation are mainly oxide-supported precious metals [2]. Noble metal catalysts are superior, but the high cost is prohibitive. Metal oxide catalysts are cheap, exhibit sufficient activity and are more practical. Co3O4 is widely used in catalytic field [3], however, the Co3O4 with the different structures and the same components for HCHO oxidation is seldom reported. In this work, nano-Co3O4, 2D-Co3O4, and 3D-Co3O4 are prepared, and their HCHO catalytic activities are evaluated. Materials and Methods SBA-15 (p6mm) and KIT-6 (ia3d) mesoporous silica were synthesized under acidic conditions using tetraethoxysilane as the silica source and Pluronic P123 as the structuredirecting agent [4]. Nano-Co3O4 was prepared by the precipitation method [5]. In a typical synthesis of 2D-Co3O4 or 3D-Co3O4, 3.0 g of SBA-15 or KIT-6 molecular sieve was added to a Co(NO3)2·6H2O ethanol solution (0.84 mol/L, 30 ml). The samples were evaporated to dryness at 80 °C. The products were calcined at 200 °C for 6 h. The above steps about casting and evaporating were repeated. Finally, the materials were calcined at 450 °C for 6 h. The SBA-15 and KIT-6 hard templates were removed using a 2 mol/L NaOH solution. Centrifugal separation was used to eliminate sodium silicate, and the samples were dried at 100 °C. The obtained powder was 2D-Co3O4 or 3D-Co3O4. Results and Discussion