Abstract:Introduction Formaldehyde (HCHO) emitted from the widely used building and decorative materials is becoming a major indoor pollutant in airtight buildings, and it could cause serious and hazardous effects on human health. Thus it is essential for human health to remove indoor formaldehyde [1]. Currently, the catalytic materials used in HCHO catalytic oxidation are mainly oxide-supported precious metals [2]. Noble metal catalysts are superior, but the high cost is prohibitive. Metal oxide catalysts are cheap, exhibit sufficient activity and are more practical. Co3O4 is widely used in catalytic field [3], however, the Co3O4 with the different structures and the same components for HCHO oxidation is seldom reported. In this work, nano-Co3O4, 2D-Co3O4, and 3D-Co3O4 are prepared, and their HCHO catalytic activities are evaluated. Materials and Methods SBA-15 (p6mm) and KIT-6 (ia3d) mesoporous silica were synthesized under acidic conditions using tetraethoxysilane as the silica source and Pluronic P123 as the structuredirecting agent [4]. Nano-Co3O4 was prepared by the precipitation method [5]. In a typical synthesis of 2D-Co3O4 or 3D-Co3O4, 3.0 g of SBA-15 or KIT-6 molecular sieve was added to a Co(NO3)2·6H2O ethanol solution (0.84 mol/L, 30 ml). The samples were evaporated to dryness at 80 °C. The products were calcined at 200 °C for 6 h. The above steps about casting and evaporating were repeated. Finally, the materials were calcined at 450 °C for 6 h. The SBA-15 and KIT-6 hard templates were removed using a 2 mol/L NaOH solution. Centrifugal separation was used to eliminate sodium silicate, and the samples were dried at 100 °C. The obtained powder was 2D-Co3O4 or 3D-Co3O4. Results and Discussion

Comparison of the performance for oxidation of formaldehyde on nano-Co3O4, 2D-Co3O4, and 3D-Co3O4 catalysts

Catalytic oxidation of formaldehyde on nano-Co 3 O 4 , 2 DCo 3 O 4 , and 3 DCo 3 O 4 catalysts

Structure and Catalytic Activity of 3D Macro/mesoporous Co3O4 for CO Oxidation Prepared by a Facile Self-Sustained Decomposition of Metal–organic Complexes

An in Situ Dealloying and Oxidation Route to Co3O4 Nanosheets and Their Ambient‐Temperature CO Oxidation Activity

Catalytic Performance and Reaction Mechanism of NO Oxidation over Co3O4 Catalysts

Synthesis Of Nanostructure Lamno3 And Lacoo3 Catalysts And Their Catalytic Activity In Oxidation Reaction

Three-dimensionally ordered macroporous Au/CeO 2-Co 3O 4 catalysts with nanoporous walls for enhanced catalytic oxidation of formaldehyde

Ordered Crystalline Mesoporous Oxides As Catalysts for CO Oxidation

Active yet extremely durable Co3O4 spheroids of different texture without/with Au deposition for CO oxidation

Catalytic Decomposition of N<SUB>2</SUB>O on Ordered Crystalline Metal Oxides

Influence of preparation method on catalytic performance of three-dimensionally ordered macroporous NiO–CuO for CO oxidation

A Review of Co3O4-based Catalysts for Formaldehyde Oxidation at Low Temperature: Effect Parameters and Reaction Mechanism

Promotion of oxygen vacancies and metal-support interaction over 3DOM Au/CeO 2 catalyst for CO oxidation

Theoretical Studies of CO Oxidation with Lattice Oxygen on Co3O4 Surfaces

Enhanced CO oxidation performance over hierarchical flower-like Co 3 O 4 based nanosheets via optimizing oxygen activation and CO chemisorption

A comparison of NiO–CuO–CeO2 composite catalysts prepared via different methods for CO oxidation

High Combustion Activity of CH4 and Catalluminescence Properties of CO Oxidation over Porous Co3O4 Nanorods

Decoration of CeO 2 Nanoparticles on Cu/Co Bimetallic Oxide and Their Catalytic Performance

Mesoporous Co‐Al Oxide Nanosheets As Highly Efficient Catalysts for CO Oxidation

Low Temperature CO Oxidation and CH4 Combustion over Co3O4 Nanosheets

Synthesis of Three-Dimensional Ordered Mesoporous MnO2 and Its Catalytic Performance in Formaldehyde Oxidation