Abstract:Oxygen activation is a key step in the catalytic oxidation of formaldehyde (HCHO) at room temperature. In this study, we synthesized a carbon/Co3O4 nanocomposite (C-Co3O4) as a solution to the insufficient capability of pristine Co3O4 (P-Co3O4) to activate oxygen for the first time. Oxygen activation was improved via carbon preventing the agglomeration of Co3O4 nanoparticles, resulting in small particles (approximately 7.7 nm) and more exposed active sites (oxygen vacancies and Co3+). The removal efficiency of C-Co3O4 for 1 ppm of HCHO remained above 90%, whereas P-Co3O4 was rapidly deactivated. In static tests, the CO2 selectivity of C-Co3O4 was close to 100%, far exceeding that of P-Co3O4 (42%). Various microscopic analyses indicated the formation and interaction of a composite structure between the C and Co3O4 interface. The carbon composite caused a disorder on the surface lattice of Co3O4, constructing more oxygen vacancies than P-Co3O4. Consequently, the surface reducibility of C-Co3O4 was improved, as was its ability to continuously activate oxygen and H2O into reactive oxygen species (ROS). We speculate that accelerated production of ROS helped rapidly degrade intermediates such as dioxymethylene, formate, and carbonate into CO2. In contrast, carbonate accumulation on P-Co3O4 surfaces containing less ROS may have caused P-Co3O4 inactivation. Compared with noble nanoparticles, this study provides a transition metal-based nanocomposite for HCHO oxidation with high efficiency, high selectivity, and low cost, which is meaningful for indoor air purification.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.est.1c00490?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.est.1c00490</a>.Additional detail information including catalyst characterizations, low-concentration HCHO removal efficiency in different relative humidities, Co K-edge k3χ spectra, TG curves, N2 adsorption–desorption isotherms, SEM, TEM images and, EDS mapping, CV curves, and changes of surface OH and H2O peak intensity during in situ DRIFTS studies (<a class="ext-link" href="/doi/suppl/10.1021/acs.est.1c00490/suppl_file/es1c00490_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Insights into High-Performance Monolith Catalysts of Co3O4 Nanowires Grown on Nickel Foam with Abundant Oxygen Vacancies for Formaldehyde Oxidation

Interface-Enhanced Oxygen Vacancies of CoCuOx Catalysts In Situ Grown on Monolithic Cu Foam for VOC Catalytic Oxidation

Logical Formulation and In-Situ Assembly of MnCo2O4@MnO2 Nanoflower Arrays on Nickel Foam As Monolithic Catalyst for Formaldehyde Degradation at Indoor Temperature

Efficacious destruction of typical aromatic hydrocarbons over CoMn/Ni foam monolithic catalysts with boosted activity and water resistance

Mesoporous Co3O4 Nanoparticles with Enriched Oxygen Defects for Efficient NO Oxidation

Exceptional formaldehyde oxidation at room temperature on Co single-atom functionalized TiO 2 nanowires via highly effective O 2 activation

NaBH4 reduced Mn-doped cobalt tetroxide R-MnxCo3-xO4 catalysts with plentiful oxygen vacancies for HCHO oxidation at low temperature

Improved Oxygen Activation over a Carbon/Co 3 O 4 Nanocomposite for Efficient Catalytic Oxidation of Formaldehyde at Room Temperature

Hollow and porous NiCo2O4 nanospheres for enhanced methanol oxidation reaction and oxygen reduction reaction by oxygen vacancies engineering

Structure-induced Hollow Co3O4 Nanoparticles with Rich Oxygen Vacancies for Efficient CO Oxidation

Co-doped cryptomelane-type manganese oxide in situ grown on a nickel foam substrate for high humidity ozone decomposition

Oxygen Vacancy Engineering of Co3 O4 Nanocrystals Through Coupling with Metal Support for Water Oxidation.

Enhancing Oxygen Activation Ability by Composite Interface Construction over a 2D Co3O4-Based Monolithic Catalyst for Toluene Oxidation

Pt/NiCo2O4 nanowire arrays on Ni foam as catalysts for efficient formaldehyde oxidation at room temperature

Multi-vacancy Co3O4 on nickel foam synthesized via a one-step hydrothermal method for high-efficiency electrocatalytic benzyl alcohol oxidation

Temperature-dependent Reaction Pathways of CO Oxidation and the Application As Monolithic Catalysts for Co3O4 Nanorods

Redox-Induced In Situ Growth of MnO2 with Rich Oxygen Vacancies over Monolithic Copper Foam for Boosting Toluene Combustion

Highly exposed metal atomic active sites in Al2O3/CoNC: Modify reaction pathways by coupling oxygen species

New Insight into the Enhanced Activity of Ordered Mesoporous Nickel Oxide in Formaldehyde Catalytic Oxidation Reactions

Highly Efficient Nano-octahedral Au/γ-Fe2O3 Catalyst Synthesized by Dealloying Combined with Calcination for Low-Temperature CO Oxidation

Engineering oxygen vacancies via amorphization in conjunction with W-doping as an approach to boosting catalytic properties of Pt/Fe-W-O for formaldehyde oxidation