Alkali-Modified Non-Precious Metal 3D-Nico2o4 Nanosheets for Efficient Formaldehyde Oxidation at Low Temperature

Yongchao Huang,Wenjie Fan,Bei Long,Haibo Li,Weitao Qiu,Fengyi Zhao,Yexiang Tong,Hongbing Ji

DOI: https://doi.org/10.1039/c5ta09370h

IF: 11.9

2016-01-01

Journal of Materials Chemistry A

Abstract:We developed new, low-cost and high-performance alkali-promoted 3D-NiCo2O4 nanosheets for efficient catalytic HCHO oxidation at low temperature.

What problem does this paper attempt to address?

Pt/NiCo2O4 nanowire arrays on Ni foam as catalysts for efficient formaldehyde oxidation at room temperature

Min Wu,Jiawei Ye,Bei Cheng,Jiaguo Yu,Liuyang Zhang

DOI: https://doi.org/10.1016/j.apsusc.2022.155183

IF: 6.7

2023-01-15

Applied Surface Science

Abstract:Catalytic oxidation of formaldehyde (HCHO) at room temperature is a low-cost and efficient solution for indoor HCHO removal. In this work, NiCo2O4 nanowires were in-situ synthesized on nickel foam (NF) by a simple hydrothermal reaction and then decorated with platinum nanoparticles (NPs). The Pt/NiCo2O4-NF catalyst exhibited excellent HCHO oxidation capacity at ambient temperature, realizing a conversion rate of 90 % within 60 min. The nickel foam substrate prevents the aggregation of NiCo2O4 nanowire arrays. It also enables the growth of large-area and aligned nanowires, contributing to the uniform dispersion of Pt NPs. Moreover, due to the unique redox property and high reactivity of NiCo2O4, numerous surface oxygen vacancies and active oxygen species are generated together with Pt by NaBH4 reduction, which is beneficial to the adsorption and oxidation of HCHO. Moreover, the hierarchical macro-/mesoporous structure of Pt/NiCo2O4-NF facilitates the diffusion of gaseous reactants and provides easily accessible active sites. In contrast with nanosized catalysts, the three-dimensional (3D) Pt/NiCo2O4-NF catalyst possesses high machinability and practicability. This work may shed light on the fabrication of 3D hierarchical catalysts for oxidative HCHO removal and indoor air purification.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films
Hierarchical Ni−Al Hydrotalcite Supported Pt Catalyst for Efficient Catalytic Oxidation of Formaldehyde at Room Temperature

Zhaoxiong Yan,Zhihua Xu,Lin Yue,Ling Shi,Linyong Huang

DOI: https://doi.org/10.1016/s1872-2067(18)63143-2

2018-01-01

Abstract:Catalytic oxidation at room temperature is recognized as the most promising method for formaldehyde (HCHO) removal. Pt-based catalysts are the optimal catalyst for HCHO decomposition at room temperature. Herein, flower-like hierarchical Pt/NiAl-LDHs catalysts with different [Ni2+]/[Al3+] molar ratios were synthesized via hydrothermal method followed by NaBH4 reduction of Pt precursor at room temperature. The flower-like hierarchical Pt/NiAl-LDHs were composed of interlaced nanoplates and metallic Pt nanoparticles (NPs) approximately 3–4 nm in diameter were loaded on the surface of the Pt/NiAl-LDHs with high dispersion. The as-prepared Pt/NiAl21 nanocomposite was highly efficient in catalyzing oxidation of HCHO into CO2 at room temperature. The high activity of the hierarchical Pt/NiAl21 nanocomposite was maintained after seven recycle tests, suggesting the high stability of the catalyst. Based on in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) studies, a reaction mechanism was put forward about HCHO decomposition at room temperature. This work provides new insights into designing and fabricating high-performance catalysts for efficient indoor air purification.
Hierarchical nanostructures self-assembled from δ-MnO 2 ultrathin nanosheets and Mn 3 O 4 octahedrons for efficient room-temperature HCHO oxidation

Lifang Qi,Yao Le,Chao Wang,Rui Lei,Tian Wu

DOI: https://doi.org/10.1039/d0nj05515h

IF: 3.3

2021-01-01

New Journal of Chemistry

Abstract:Self-assembling ultrathin active δ-MnO 2 nanosheets and Mn 3 O 4 octahedrons into hierarchical texture enhances room-temperature formaldehyde oxidation at a low-level of Pt.

chemistry, multidisciplinary
An in Situ Dealloying and Oxidation Route to Co3O4 Nanosheets and Their Ambient‐Temperature CO Oxidation Activity

Caixia Xu,Yunqing Liu,Ce Zhou,Lin Wang,Haoran Geng,Yi Ding

DOI: https://doi.org/10.1002/cctc.201000275

IF: 4.5

2011-01-01

ChemCatChem

Abstract:Co3O4 nanosheets are straightforwardly fabricated through an in situ dealloying and oxidation process of etching CoAl alloy in alkaline solutions. X-ray diffraction and electron spectroscopy characterizations demonstrate the formation of a Co3O4 nanostructure with an intricate hierarchical nanosheet morphology comprising interconnected nanoslices with the diameter as small as 6 nm. Upon calcination in O-2 atmosphere, these novel Co3O4 nanosheets exhibit excellent catalytic activity toward CO oxidation in normal feed gas at ambient temperature. Catalytic tests reveal the strong influence of calcination temperature on the resultant catalytic activities, whereby 300 degrees C is found to be preferable possibly due to an optimum balance between the surface area and the amount of active species as compared with 200 and 450 degrees C. Moreover, Co3O4 nanosheets showed good time-on-stream catalytic stability; CO conversion at T-50 (the temperature for 50% CO conversion) reduced to 37% after 20 h, and at T-100 (the temperature for full CO conversion) the conversion only decreased to about 90% after 15 h.
MnO2-decorated N-doped Carbon Nanotube with Boosted Activity for Low-Temperature Oxidation of Formaldehyde.

Shuai Peng,Xixian Yang,James Strong,Binoy Sarkar,Qiang Jiang,Feng Peng,Defei Liu,Hailong Wang

DOI: https://doi.org/10.1016/j.jhazmat.2020.122750

IF: 13.6

2020-01-01

Journal of Hazardous Materials

Abstract:Low-temperature oxidative degradation of formaldehyde (HCHO) using non-noble metal catalysts is challenging. Herein, novel manganese dioxide (MnO2)/N-doped carbon nanotubes (NCNT) composites were prepared with varying MnO2 content. The surface properties and morphologies were analyzed using X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM) and transmission electron microscope (TEM). Comparing with MnO2/carbon nanotubes (CNTs) catalyst, the 40% MnO2 /NCNT exhibited much better activity and selectivity for HCHO oxidation, mineralizing 95% of HCHO (at 100 ppm) into CO2 at 30 degrees C at a gas hourly space velocity (GHSV) of 30,000 mL h(-1) g(-1). Density functional theory (DFT) calculation was used to analyze the difference in the catalytic activity of MnO2 with CNTs and NCNT carrier. It was confirmed that the oxygen on NCNT was more active than CNTs, which facilitated the regeneration of MnO2. This resulted in remarkably boosted activity for HCHO oxidation. The present work thus exploited an inexpensive approach to enhance the catalytic activity of transition metal oxides via depositing them on a suitable support.
Exceptional formaldehyde oxidation at room temperature on Co single-atom functionalized TiO 2 nanowires via highly effective O 2 activation

Lijuan Liu,Guohua Jing,Cibin Xu,Xiaowei Zhang,Xuehong Zhang,Lingyun Guo,Zhiwei Huang,Xiaomin Wu,Huawang Zhao,Chung-Shin Yuan,Huazhen Shen,Wenjie Xia

DOI: https://doi.org/10.1016/j.apcatb.2023.123634

IF: 24.319

2023-12-30

Applied Catalysis B Environmental

Abstract:O 2 activation is vital for catalyzing the oxidation of formaldehyde (HCHO). Despite the high O 2 activation capabilities demonstrated by noble metal catalysts, their practical application is impeded by their exorbitant cost. Herein, Co single atoms were successfully incorporated into titanium dioxide nanowires (TiO 2 -NWs). Furthermore, the key step in the HCHO catalytic oxidation process was elucidated through in situ diffuse reflectance infrared Fourier transform spectroscopy (in situ DRIFTS) and density functional theory (DFT) calculations. Finally, the intricate O 2 activation mechanism was explored, revealing the catalyst's exceptional performance in ambient HCHO oxidation. Notably, it outperformed commercial TiO 2 (TiO 2 -P25) by 13.3 times and Co-supported TiO 2 -P25 by 1.9 times. Co single atoms facilitated the conversion of O 2 into superoxide (O 2 - ), significantly reducing the reaction barrier of dioxymethylene to formate. This superior O 2 activation was attributed to the active nature and unsaturated electronic configuration of Co single atoms. This study provides a novel, cost-effective strategy for creating HCHO elimination catalysts with accessible nonnoble transition metals.

chemistry, physical,engineering, chemical, environmental
A CuNi Alloy-Carbon Layer Core-Shell Catalyst for Highly Efficient Conversion of Aqueous Formaldehyde to Hydrogen at Room Temperature

Zining Zhou,Yun Hau Ng,Shengju Xu,Siyuan Yang,Qiongzhi Gao,Xin Cai,Jihai Liao,Yueping Fang,Shengsen Zhang

DOI: https://doi.org/10.1021/acsami.1c11776

2021-08-11

Abstract:A copper (Cu) material is catalytically active for formaldehyde (HCHO) dehydrogenation to produce H2, but the unsatisfactory efficiency and easy corrosion hinder its practical application. Alloying with other metals and coating a carbon layer outside are recognized as effective strategies to improve the catalytic activity and the long-term durability of nonprecious metal catalysts. Here, highly dispersed CuNi alloy-carbon layer core-shell nanoparticles (CuNi@C) have been developed as a robust catalyst for efficient H2 generation from HCHO aqueous solution at room temperature. Under the optimized reaction conditions, the CuNi@C catalyst exhibits a H2 evolution rate of 110.98 mmol·h-1·g-1, which is 1.5 and 4.9 times higher than those of Cu@C and Ni@C, respectively, which ranks top among the reported nonprecious metal catalysts for catalytic HCHO reforming at room temperature to date. Furthermore, CuNi@C also displays excellent stability toward the catalytic HCHO reforming into H2 in tap water owing to the well-constructed carbon sheath protecting CuNi nanocrystals from oxidation in an alkaline medium. Combined with density functional theory calculations, the superior catalytic efficiency of CuNi@C for H2 generation results from the synergistic contribution between the massive active species from HCHO decomposition on the Cu sites and the remarkable H2 evolution activity on Ni sites. The improved performance of CuNi@C highlights the enormous potential of advancing noble-metal-free nanoalloys as cost-effective and recyclable catalysts for energy recovery from industrial HCHO wastewater.
Highly exposed metal atomic active sites in Al2O3/CoNC: Modify reaction pathways by coupling oxygen species

Manyu Zhang,Zhijian Fu,Hui Chen,Jia Yu,Liwen Zhang,Chenghan Yang,Yubo Zhou,Yingjie Hua,Xuyu Wang,Hongbing Ji

DOI: https://doi.org/10.1016/j.jcis.2024.07.093

2024-07-14

Abstract:The catalytic oxidation of formaldehyde (HCHO) at ambient temperature is a highly efficient, cost-effective and environmentally friendly approach for formaldehyde removal. Reactive oxygen (O*) and reactive hydroxyl groups (OH*) are the main active species in the catalytic oxidation reaction of HCHO. Therefore, it is crucial to design catalysts that can simultaneously enhance the surface concentrations of O* and OH*, thereby improving their overall catalytic performance. The present study aimed to design an Al2O3/CoNC catalyst featuring layered carbon nitride coupled with metal oxides possessing domain-limited cobalt (Co) metal active sites, to efficiently remove HCHO (≈100 %, 100 ppm, RH=50 %, GSHV=20,000 mL/(g h)) and ensure stability (more than 90 % formaldehyde removal within 450 h) at ambient temperature. The characterization revealed that the interaction between Al2O3-supported metal and CoNC resulted in enhanced confinement of Co, leading to a higher abundance of edge structures exposing more active sites. Additionally, the presence of highly dispersed Co-NX active sites and increased oxygen vacancies effectively facilitated the adsorption and activation processes of HCHO and O2, as well as the adsorption and desorption dynamics of intermediates during the reaction. These factors collectively contributed to an improved catalytic activity. The results of in situ infrared spectroscopy revealed that the catalyst improved the adsorption and activation of O2 and H2O, leading to the rapid generation of substantial amounts of O* and OH*. This synergistic interaction between Al2O3 and CoNC plays a crucial role in the sustained production of O* and OH*, promoting efficient of intermediate decomposition, and ensuring excellent catalytic activity and stability for HCHO.
Efficient Decomposition of Formaldehyde on Ni−Al Hydrotalcite/AlOOH Nanocomposites Decorated with Pt Nanoparticles at Ambient Temperature

Lifan Qin,Hefa Cheng

DOI: https://doi.org/10.1002/cnma.202100206

IF: 3.82

2021-01-01

ChemNanoMat

Abstract:Nanocomposites of nickel-aluminum hydrotalcite (Ni-Al HT) and boehmite (AlOOH) decorated with Pt nanoparticles (NPs) were synthesized and evaluated for catalytic oxidation of formaldehyde at ambient temperature. Experimental results showed that Ni-Al HT modification improved the activity of Pt/AlOOH, and the nanocomposite with Ni/Al molar ratio of 1 : 9 (Pt/Ni1Al9) exhibited remarkable and stable catalytic activity. Characterization results indicated that Pt/Ni1Al9 had a larger specific surface area, higher degree of Pt NPs dispersion, and more surface active sites compared to the nanocomposites with other Ni/Al ratios. The enhanced catalytic activity of Pt/Ni1Al9 was attributed to the generation of more surface active oxygen species from the adsorbed oxygen molecules, which was activated by the electron transfer between Ni-Al HT and Pt/AlOOH, and the suitable interaction and synergistic effect among Ni-Al HT, Pt NPs, and AlOOH. These findings indicate that the nanocomposites of Ni-Al hydrotalcite and boehmite hold significant promises for removal of indoor formaldehyde.
Catalytic performance and mechanism of bismuth molybdate nanosheets decorated with platinum nanoparticles for formaldehyde decomposition at room temperature

Lifan Qin,Shengnan Huang,Hefa Cheng

DOI: https://doi.org/10.1016/j.jcis.2022.11.110

Abstract:Catalytic oxidation at room temperature is considered as a promising strategy for removal of formaldehyde (HCHO), a widely occurring indoor air pollutant. A series of Bi2MoO6 nanosheets were prepared via one-step hydrothermal synthesis in this study, followed by decoration with Pt nanoparticles (NPs). The catalyst with Bi2MoO6 support prepared at 180 °C exhibited high and stable activity in catalytic oxidation of HCHO at room temperature. The excellent catalytic performance was attributed to its large specific area and pore volume, high level of surface active oxygen species, high content of metallic Pt NPs, and abundant oxygen vacancies. The good synergy and interaction between Pt and Bi2MoO6 promoted electron transfer, and facilitated the adsorption and oxidation of HCHO. The electronic interaction between Pt NPs and Bi2MoO6 accelerated the activation of oxygen species due to weakening of the surface BiO or MoO bonds adjacent to Pt NPs. Infrared spectra indicated that dioxymethylene and formate species were the main intermediates of HCHO oxidation. Density functional theory calculations showed that the dehydrogenation of HCO2, with an energy barrier of 282.1 kJ/mol, was the rate-determining step in catalytic oxidation process. This study provides new insights on the construction of high-efficiency catalysts for indoor formaldehyde removal.
Efficient and Durable Oxidation Removal of Formaldehyde over Layered Double Hydroxide Catalysts at Room Temperature

Lvcun Chen,Kanglu Li,Ting Xue,Yan Yang,Zhengjun Gong,Fan Dong

DOI: https://doi.org/10.1021/acs.est.4c01606

IF: 11.4

2024-05-29

Environmental Science & Technology

Abstract:Room temperature catalytic oxidation (RTCO) using non-noble metals has emerged as a highly promising technique for removal of formaldehyde (HCHO) under ambient conditions; however, non-noble catalysts still face the challenges related to poor water resistance and low stability under harsh conditions. In this study, we synthesized a series of layered double hydroxides (LDHs) incorporating various dual metals (MgAl, ZnAl, NiAl, NiFe, and NiTi) for formaldehyde oxidation at ambient temperature....

environmental sciences,engineering, environmental
NaBH4 reduced Mn-doped cobalt tetroxide R-MnxCo3-xO4 catalysts with plentiful oxygen vacancies for HCHO oxidation at low temperature

Gang Yan,Xiaojun Du,Xiang-Wei Guo,Xuzheng Cao,Hongfei Shi

DOI: https://doi.org/10.1039/d4nj00742e

IF: 3.3

2024-04-05

New Journal of Chemistry

Abstract:Developing low-cost and efficient catalysts for the oxidation of formaldehyde (HCHO) is crucial for preservation of environment. The main challenge of this study is how to develop an efficient, stable, and inexpensive catalyst that can oxidize HCHO at low temperatures. Herein, the reduced Mn-doped cobalt tetroxide R-MnxCo3-xO4 catalyst was prepared by simple co-precipitation, annealing treatment followed by NaBH4 reduced. The prepared R-MnxCo3-xO4 showed remarkable enhanced activity for HCHO oxidation at low temperature. The R-MnCo2O4 catalyst can oxidize and decompose 79% of HCHO at low temperature 50 ° C, and exhibits excellent catalytic stability. The improved catalytic activity can be attributed to the increase in oxygen vacancy concentration and the improvement redox performance. The TGA test shows that the content of oxygen vacancies in the R-MnCo2O4 catalyst can reach 5.77% (atomic ratio). The H2-TPR and O2-TPD tests indicated that the surface oxygen vacancies can promote oxygen mobility and facilitate the formation of reactive oxygen species during formaldehyde catalytic oxidation process. This study reveals the importance of surface oxygen vacancies in improving the catalytic oxidation activity of catalysts, providing possibilities for the development of high-performance catalysts through atomic doping and reduction modification.

chemistry, multidisciplinary
Modulating the Coordination of Single Co Atoms to Trigger the Catalytic Oxidation of Formaldehyde at Room Temperature

Jianye Liu,Kaijun Liang,Defu Yao,Rakesh Chilivery,Dajun Fan,Wenbin Chen,Guanli Chen,Sha Li,Zhen Li,Muwei Ji,Yibing Song

DOI: https://doi.org/10.1021/acs.inorgchem.3c00091

IF: 4.6

2023-02-18

Inorganic Chemistry

Abstract:Designing efficient and stable non-precious metal catalysts remains a significant challenge for formaldehyde (HCHO) oxidation, which is an expected way to replace the employment of noble-metal catalysts. Herein, a series of atomically dispersed Co catalysts are optimized by evaporating nitrogen atoms and exploring their HCHO oxidation catalytic performance. The results show that the prepared temperature can effectively control the coordination regulation of the Co atomic site, which in turn...

chemistry, inorganic & nuclear
MnCo-Layered double hydroxides nanosheets supported Pd nanoparticles for complete catalytic oxidation of formaldehyde at room temperature

Juanjuan Gong,Xuyu Wang,Haibo W,Xuexue Dong,Jing Li,Fu Yang,Aihua Yuan,Hongbing Ji

DOI: https://doi.org/10.1016/j.apsusc.2022.154702

IF: 6.7

2022-12-30

Applied Surface Science

Abstract:Removal of gaseous formaldehyde by room-temperature catalytic oxidation has promising applications. The rational design of the structure of catalyst to improve the ability of activated key species (adsorbed oxygen and hydroxyl) through understanding the reaction mechanism can improve the catalytic activity. In this paper, Pd nanoparticles were deposited on pre-reduction uniform LDH nanosheets to prepare Pd-decorated sodium borohydride-reduced Mn/Co layered double hydroxides (Pd/LDH-NaBH4). The transition metal (Mn and Co) doping of Pd improved the catalyst's ability to activate oxygen and formaldehyde, and the support of LDHs increased the hydroxyl concentration of the catalyst. Pd/LDH-NaBH4 showed reduced valence of Pd, improved dispersion of Pd NPs, and retention of abundant hydroxyl groups on LDH. Characterizations revealed that the synergistic effect of the supported Pd NPs and LDH, as well as many oxygen vacancies, was responsible for the effective removal of HCHO by Pd/LDH-NaBH4 catalyst at ambient temperature. This study further developed a new catalyst for HCHO oxidation, which may provide a new idea for the removal mechanism of oxidized HCHO.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films
Catalytic oxidation of formaldehyde on nano-Co 3 O 4 , 2 DCo 3 O 4 , and 3 DCo 3 O 4 catalysts

Bingyang Bai,Junhua Li

2014-01-01

Abstract:Introduction Formaldehyde (HCHO) emitted from the widely used building and decorative materials is becoming a major indoor pollutant in airtight buildings, and it could cause serious and hazardous effects on human health. Thus it is essential for human health to remove indoor formaldehyde [1]. Currently, the catalytic materials used in HCHO catalytic oxidation are mainly oxide-supported precious metals [2]. Noble metal catalysts are superior, but the high cost is prohibitive. Metal oxide catalysts are cheap, exhibit sufficient activity and are more practical. Co3O4 is widely used in catalytic field [3], however, the Co3O4 with the different structures and the same components for HCHO oxidation is seldom reported. In this work, nano-Co3O4, 2D-Co3O4, and 3D-Co3O4 are prepared, and their HCHO catalytic activities are evaluated. Materials and Methods SBA-15 (p6mm) and KIT-6 (ia3d) mesoporous silica were synthesized under acidic conditions using tetraethoxysilane as the silica source and Pluronic P123 as the structuredirecting agent [4]. Nano-Co3O4 was prepared by the precipitation method [5]. In a typical synthesis of 2D-Co3O4 or 3D-Co3O4, 3.0 g of SBA-15 or KIT-6 molecular sieve was added to a Co(NO3)2·6H2O ethanol solution (0.84 mol/L, 30 ml). The samples were evaporated to dryness at 80 °C. The products were calcined at 200 °C for 6 h. The above steps about casting and evaporating were repeated. Finally, the materials were calcined at 450 °C for 6 h. The SBA-15 and KIT-6 hard templates were removed using a 2 mol/L NaOH solution. Centrifugal separation was used to eliminate sodium silicate, and the samples were dried at 100 °C. The obtained powder was 2D-Co3O4 or 3D-Co3O4. Results and Discussion
Low Temperature CO Oxidation and CH4 Combustion over Co3O4 Nanosheets

Fagen Wang,Linjia Zhang,Leilei Xu,Zhiyong Deng,Weidong Shi

DOI: https://doi.org/10.1016/j.fuel.2017.04.140

IF: 7.4

2017-01-01

Fuel

Abstract:Co3O4 nanomaterials were synthesized by hydrothermal method and were applied for low temperature CO oxidation and methane combustion. The addition of ethylene glycol and its concentration significantly influenced the size and shape of the Co3O4 oxides. Nanosheets of Co3O4 were synthesized in ethylene glycol solution and nanospheres were formed in water. The activity of oxygen species in the nanosheets and nanospheres were characterized by hydrogen/methane programmed reduction, oxygen programmed desorption and XPS. The results showed that the Co3O4 nanosheets exhibited more active oxygen species than the Co3O4 nanospheres, leading to the higher activity in the oxidative reactions. The study demonstrated the importance of active oxygen species in Co3O4 catalysts to achieve high catalytic performance towards the carbon monoxide and methane elimination at low temperatures. (C) 2017 Elsevier Ltd. All rights reserved.
Deactivation and Regeneration of Pt/Tio2 Nanosheet-Type Catalysts with Exposed (001) Facets for Room Temperature Oxidation of Formaldehyde

Longhui Nie,Peng Zhou,Jiaguo Yu,Mietek Jaroniec

DOI: https://doi.org/10.1016/j.molcata.2014.02.033

2014-01-01

Abstract:Formaldehyde (HCHO) is a major indoor air pollutant and long-term exposure to HCHO may cause health problems including nasal tumors and skin irritation. Room-temperature catalytic oxidation decomposition of HCHO is considered as the most promising strategy for the removal of HCHO due to its environmental-friendly reaction conditions and energy-saving consideration. In this work, surface-fluorinated anatase TiO2 nanosheets with dominant {001} facets (FTiO2-NS) were first prepared by a hydrothermal method using Ti(OC4H9)4 and HF as precursors. Then, Pt/FTiO2-NS catalyst with 0.5wt% Pt loadings was obtained by a combined NaOH-assisted impregnation of titania with Pt precursor and NaBH4-reduction route. The catalytic activity was evaluated by catalytic oxidation decomposition of HCHO vapor at room temperature. Fluoride poisoning (F-poisoning) phenomenon of Pt/FTiO2-NS was first observed for oxidative decomposition of HCHO. The mechanism of F-poisoning is mainly due to blocking of Pt catalytic active sites by strong interactions between Pt and highly electronegative F. In order to recover the catalytic performance, a simple regeneration method for the deactivated Pt/FTiO2-NS catalysts was proposed by NaOH washing.
Efficient HCHO Oxidation at Room Temperature Via Maximizing Catalytic Sites in 2D Coralloid 8-Mno2@go

Yiheng Li,Tao Dong,Pingli Huang,Jian Ji,Haibao Huang

DOI: https://doi.org/10.1016/j.apcatb.2023.123322

2024-01-01

Abstract:Airborne formaldehyde (HCHO) in indoor environments causes serious health problems and needs to be efficiently eliminated. However, the efficient and stable catalytic oxidation of HCHO can be hardly achieved at room temperature over transition metal oxides due to the limited exposure of active sites. Herein, 8-MnO2@GO catalysts were originally synthesized via a facile in situ growth of 8-MnO2 on the trace graphene oxide (GO) substrate (1%) and stably exhibited nearly 100% HCHO elimination at room temperature. 8-MnO2@GO showed the unique 2D coralloid structure with uniformly dispersed 8-MnO2 nanorod on planar-structured GO, which greatly enhanced the exposure of catalytic sites and mass transfer of reactants. The abundant surface reactive oxygen species (ROS) and hydroxyl (-OH) groups were rapidly generated from the activation of O2 and surface-adsorbed water over highly exposed catalytic sites. The ROS and -OH groups cooperated well cooperated to maintain the exceptional catalytic activity and stability towards HCHO degradation. In-situ DRIFTS results showed that catalytic HCHO oxidation predominantly follows the Langmuir-Hinshelwood (L-H) mechanism over the 8-MnO2@GO. This study presents a simple yet effective strategy for maximizing exposure to catalytic active sites and rational design of efficient catalysts for indoor HCHO elimination.
Improved Oxygen Activation over a Carbon/Co 3 O 4 Nanocomposite for Efficient Catalytic Oxidation of Formaldehyde at Room Temperature

Rong Li,Yu Huang,Dandan Zhu,Wingkei Ho,Junji Cao,Shuncheng Lee

DOI: https://doi.org/10.1021/acs.est.1c00490

2021-03-04

Abstract:Oxygen activation is a key step in the catalytic oxidation of formaldehyde (HCHO) at room temperature. In this study, we synthesized a carbon/Co3O4 nanocomposite (C-Co3O4) as a solution to the insufficient capability of pristine Co3O4 (P-Co3O4) to activate oxygen for the first time. Oxygen activation was improved via carbon preventing the agglomeration of Co3O4 nanoparticles, resulting in small particles (approximately 7.7 nm) and more exposed active sites (oxygen vacancies and Co3+). The removal efficiency of C-Co3O4 for 1 ppm of HCHO remained above 90%, whereas P-Co3O4 was rapidly deactivated. In static tests, the CO2 selectivity of C-Co3O4 was close to 100%, far exceeding that of P-Co3O4 (42%). Various microscopic analyses indicated the formation and interaction of a composite structure between the C and Co3O4 interface. The carbon composite caused a disorder on the surface lattice of Co3O4, constructing more oxygen vacancies than P-Co3O4. Consequently, the surface reducibility of C-Co3O4 was improved, as was its ability to continuously activate oxygen and H2O into reactive oxygen species (ROS). We speculate that accelerated production of ROS helped rapidly degrade intermediates such as dioxymethylene, formate, and carbonate into CO2. In contrast, carbonate accumulation on P-Co3O4 surfaces containing less ROS may have caused P-Co3O4 inactivation. Compared with noble nanoparticles, this study provides a transition metal-based nanocomposite for HCHO oxidation with high efficiency, high selectivity, and low cost, which is meaningful for indoor air purification.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.est.1c00490?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.est.1c00490</a>.Additional detail information including catalyst characterizations, low-concentration HCHO removal efficiency in different relative humidities, Co K-edge k3χ spectra, TG curves, N2 adsorption–desorption isotherms, SEM, TEM images and, EDS mapping, CV curves, and changes of surface OH and H2O peak intensity during in situ DRIFTS studies (<a class="ext-link" href="/doi/suppl/10.1021/acs.est.1c00490/suppl_file/es1c00490_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

environmental sciences,engineering, environmental
High catalytic activity for formaldehyde oxidation of an interconnected network structure composed of δ-MnO2 nanosheets and γ-MnOOH nanowires

Ying Tao,Rong Li,Ai-Bin Huang,Yi-Ning Ma,Shi-Dong Ji,Ping Jin,Hong-Jie Luo

DOI: https://doi.org/10.1007/s40436-020-00321-2

IF: 3.837

2020-08-28

Advances in Manufacturing

Abstract:Abstract Among the transition metal oxide catalysts, manganese oxides have great potential for formaldehyde (HCHO) oxidation at ambient temperature because of their high activity, nontoxicity, low cost, and polybasic morphologies. In this work, a MnO 2 -based catalyst (M-MnO 2 ) with an interconnected network structure was successfully synthesized by a one-step hydrothermal method. The M-MnO 2 catalyst was composed of the main catalytic agent, δ -MnO 2 nanosheets, dispersed in a nonactive framework material of γ -MnOOH nanowires. The catalytic activity of M-MnO 2 for HCHO oxidation at room temperature was much higher than that of the pure δ -MnO 2 nanosheets. This is attributed to the special interconnected network structure. The special interconnected network structure has high dispersion and specific surface area, which can provide more surface active oxygen species and higher surface hydroxyl groups to realize rapid decomposition of HCHO.

engineering, manufacturing,materials science, multidisciplinary

Alkali-Modified Non-Precious Metal 3D-Nico2o4 Nanosheets for Efficient Formaldehyde Oxidation at Low Temperature

Pt/NiCo2O4 nanowire arrays on Ni foam as catalysts for efficient formaldehyde oxidation at room temperature

Hierarchical Ni−Al Hydrotalcite Supported Pt Catalyst for Efficient Catalytic Oxidation of Formaldehyde at Room Temperature

Hierarchical nanostructures self-assembled from δ-MnO 2 ultrathin nanosheets and Mn 3 O 4 octahedrons for efficient room-temperature HCHO oxidation

An in Situ Dealloying and Oxidation Route to Co3O4 Nanosheets and Their Ambient‐Temperature CO Oxidation Activity

MnO2-decorated N-doped Carbon Nanotube with Boosted Activity for Low-Temperature Oxidation of Formaldehyde.

Exceptional formaldehyde oxidation at room temperature on Co single-atom functionalized TiO 2 nanowires via highly effective O 2 activation

A CuNi Alloy-Carbon Layer Core-Shell Catalyst for Highly Efficient Conversion of Aqueous Formaldehyde to Hydrogen at Room Temperature

Highly exposed metal atomic active sites in Al2O3/CoNC: Modify reaction pathways by coupling oxygen species

Efficient Decomposition of Formaldehyde on Ni−Al Hydrotalcite/AlOOH Nanocomposites Decorated with Pt Nanoparticles at Ambient Temperature

Catalytic performance and mechanism of bismuth molybdate nanosheets decorated with platinum nanoparticles for formaldehyde decomposition at room temperature

Efficient and Durable Oxidation Removal of Formaldehyde over Layered Double Hydroxide Catalysts at Room Temperature

NaBH4 reduced Mn-doped cobalt tetroxide R-MnxCo3-xO4 catalysts with plentiful oxygen vacancies for HCHO oxidation at low temperature

Modulating the Coordination of Single Co Atoms to Trigger the Catalytic Oxidation of Formaldehyde at Room Temperature

MnCo-Layered double hydroxides nanosheets supported Pd nanoparticles for complete catalytic oxidation of formaldehyde at room temperature

Catalytic oxidation of formaldehyde on nano-Co 3 O 4 , 2 DCo 3 O 4 , and 3 DCo 3 O 4 catalysts

Low Temperature CO Oxidation and CH4 Combustion over Co3O4 Nanosheets

Deactivation and Regeneration of Pt/Tio2 Nanosheet-Type Catalysts with Exposed (001) Facets for Room Temperature Oxidation of Formaldehyde

Efficient HCHO Oxidation at Room Temperature Via Maximizing Catalytic Sites in 2D Coralloid 8-Mno2@go

Improved Oxygen Activation over a Carbon/Co 3 O 4 Nanocomposite for Efficient Catalytic Oxidation of Formaldehyde at Room Temperature

High catalytic activity for formaldehyde oxidation of an interconnected network structure composed of δ-MnO2 nanosheets and γ-MnOOH nanowires