Abstract:Synthesis of catalysts with high catalytic degradation activity for formaldehyde (HCHO) at room temperature is highly desirable for indoor air quality control. Herein, a novel K-Mn3O4@CeO2 catalyst with excellent catalytic oxidation activity toward HCHO at near room temperature was reported. In particular, the K addition in K-Mn3O4@CeO2 considerably enhanced the oxidation activity, and importantly, 99.3 % conversion of 10 mL of a 40 mg/L HCHO solution at 30 °C for 14 h was achieved, with simultaneous strong cycling stability. Moreover, the addition of K species considerably influenced the chemical valence state of Mn from +4 (ε-MnO2) to +8/3 (Mn3O4) on the surface of CeO2, which obviously changed the tunnel structure and the number of oxygen vacancies. One part of K species is uniformly dispersed on K-Mn3O4@CeO2, and the other part exists in the tunnel structure of Mn3O4@CeO2, which is mainly used to balance the negative charge of the tunnel and prevent collapse of the structure, providing enough active sites for the catalytic oxidation of HCHO. We observed a phase transition from tunneled KMnO2 to Mn3O4 to tunneled MnO2 with the decreasing K+ content, in which K-Mn3O4@CeO2 exhibited higher HCHO oxidation activity. In addition, K-Mn3O4@CeO2 exhibited lower oxygen vacancy formation and HCHO adsorption energies in aqueous solution based on density functional theory calculations. This is because the K species provide more active oxygen species and richer oxygen vacancies on the surface of K-Mn3O4@CeO2, promote the mobility of lattice oxygen and the room-temperature reduction properties of oxygen species, and enhance the ability of the catalyst to replenish the consumed oxygen species. Finally, a possible HCHO catalytic oxidation pathway on the surface of K-Mn3O4@CeO2 catalyst is proposed.

MnO2-decorated N-doped Carbon Nanotube with Boosted Activity for Low-Temperature Oxidation of Formaldehyde.

High catalytic activity for formaldehyde oxidation of an interconnected network structure composed of δ-MnO2 nanosheets and γ-MnOOH nanowires

Enhanced formaldehyde oxidation over MnO2 and doped manganese-based catalysts: Experimental and theoretical Insights into mechanism and performance

NaBH4 reduced Mn-doped cobalt tetroxide R-MnxCo3-xO4 catalysts with plentiful oxygen vacancies for HCHO oxidation at low temperature

Excellent Stability for Catalytic Oxidation Formaldehyde over Defective Δ-Mno2 Nanoparticles at Room Temperature

Surface Lattice Oxygen Activation by Nitrogen-Doped Manganese Dioxide as an Effective and Longevous Catalyst for Indoor HCHO Decomposition

Tuning the nitrogen contents in carbon matrix encapsulating Co nanoparticles for promoting formaldehyde removal through Mott-Schottky effect

Critical review of catalytic degradation of formaldehyde via MnO2: From the perspective of process intensification

Effect of metal ion dopants on decomposition formaldehyde room-temperature catalyzed by oxygen-deficient M-MnOx (M=Ce, Co and Cu) materials

Oxygen vacancy-rich K-Mn3O4@CeO2 catalyst for efficient oxidation degradation of formaldehyde at near room temperature

Two-step hydrothermal synthesis of highly active MnOx-CeO2 for complete oxidation of formaldehyde

Mn/HZSM-5 catalyst with high content of Mn 4+ and surface hydroxyls for formaldehyde oxidation at room temperature

Evaluation of an ε-manganese (IV) oxide/manganese vanadium oxide composite catalyst enriched with oxygen vacancies for enhanced formaldehyde removal

Enhanced Active Oxygen Species Generation on Detective Δ-Mno2 Nanoparticles for Catalytic Formaldehyde Oxidation

One-step Synthesis of Nanocarbon-Decorated MnO 2 with Superior Activity for Indoor Formaldehyde Removal at Room Temperature

Facile In-Situ Synthesis of Manganese Dioxide Nanosheets on Cellulose Fibers and their Application in Oxidative Decomposition of Formaldehyde

Preparation of porous MnO2/CeO2 composite for the effective removal of formaldehyde from air

Efficient Formaldehyde Elimination Over Ag/MnO2 Nanorods: Influence of the Ag Loading

Synthesis and Catalytic Performance of Manganese Oxide Octahedral Molecular Sieve Nanorods for Formaldehyde Oxidation at Low Temperature

The Catalytic and Adsorptive Synergistic Effect of Oxygen-Vacancy-Rich MnO x /C Catalysts for HCHO Oxidation at Room Temperature

Highly exposed metal atomic active sites in Al2O3/CoNC: Modify reaction pathways by coupling oxygen species