Abstract:Thermal catalytic degradation of formaldehyde (HCHO) over manganese-based catalysts is garnering significant attention. In this study, both theoretical simulations and experimental methods were employed to elucidate the primary reaction pathways of HCHO on the MnO2(110) surface. Specifically, the effects of doping MnO2 with elements such as Fe, Ce, Ni, Co, and Cu on the HCHO oxidation properties were evaluated. Advanced characterization techniques, including X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer-Emmett-Teller (BET), and X-ray photoelectron spectroscopy (XPS), were employed to discern the physical properties and chemical states of the active components on the catalyst surface. The comprehensive oxidation pathway of HCHO on the MnO2(110) surface includes O2 adsorption and dissociation, HCHO adsorption and dehydrogenation, CO2 desorption, H2O formation and desorption, oxygen vacancy supplementation, and other elementary reactions. The pivotal rate-determining step was identified as the hydrogen migration process, characterized by an energy barrier of 234.19 kJ mol-1. Notably, HCHOO and *CHOO emerged as crucial intermediates during the reaction. Among the doped catalysts, Fe-doped MnO2 outperformed its counterparts doped with Ce, Ni, Co, and Cu. The optimal degradation rate and selectivity were achieved at a molar ratio of Fe: Mn = 0.1. The superior performance of the Fe-doped MnO2 can be ascribed to its large specific surface area, conducive pore structure for HCHO molecular transport, rich surface-adsorbed oxygen species, and a significant presence of oxygen vacancies.

Facile In-Situ Synthesis of Manganese Dioxide Nanosheets on Cellulose Fibers and their Application in Oxidative Decomposition of Formaldehyde

MnO2-decorated N-doped Carbon Nanotube with Boosted Activity for Low-Temperature Oxidation of Formaldehyde.

Control over the Morphology and Structure of Manganese Oxide by Tuning Reaction Conditions and Catalytic Performance for Formaldehyde Oxidation

Ultrathin Manganese Dioxide Nanosheets for Formaldehyde Removal and Regeneration Performance

Facile Preparation, Characterization, and Formaldehyde Elimination Performance of MnOx/natural Loofah Composites

High catalytic activity for formaldehyde oxidation of an interconnected network structure composed of δ-MnO2 nanosheets and γ-MnOOH nanowires

Enhanced formaldehyde oxidation over MnO2 and doped manganese-based catalysts: Experimental and theoretical Insights into mechanism and performance

In Situ Synthesis of Manganese Oxides on Polyester Fiber for Formaldehyde Decomposition at Room Temperature

Sepiolite-Supported Manganese Oxide as an Efficient Catalyst for Formaldehyde Oxidation: Performance and Mechanism

Manganese Oxyhydroxide And Oxide Nanofibers For High Efficiency Degradation Of Organic Pollutants

Review on Manganese Dioxide for Catalytic Oxidation of Airborne Formaldehyde

Facile Synthesis of Activated Carbon-Supported Porous Manganese Oxide via in situ Reduction of Permanganate for Ozone Decomposition

Synthesis and Catalytic Performance of Manganese Oxide Octahedral Molecular Sieve Nanorods for Formaldehyde Oxidation at Low Temperature

Scalable Synthesis of Water-Dispersible 2D Manganese Dioxide Monosheets.

One-step Synthesis of Nanocarbon-Decorated MnO 2 with Superior Activity for Indoor Formaldehyde Removal at Room Temperature

Logical Formulation and In-Situ Assembly of MnCo2O4@MnO2 Nanoflower Arrays on Nickel Foam As Monolithic Catalyst for Formaldehyde Degradation at Indoor Temperature

In Situ Synthesis Of A Stable Fe3o4@Cellulose Nanocomposite For Efficient Catalytic Degradation Of Methylene Blue

The Catalytic and Adsorptive Synergistic Effect of Oxygen-Vacancy-Rich MnO x /C Catalysts for HCHO Oxidation at Room Temperature

Manganese-doped Cobalt Tetroxide for Formaldehyde Oxidation

Communication—Hollow MnO X @nanoparticles Electrospun Fibers with High Porosity for Formaldehyde Removal at Room Temperature

Efficient MnOx supported on coconut shell activated carbon for catalytic oxidation of indoor formaldehyde at room temperature