Improving the Electrochemical Performance of LiNi1/3Co1/3Mn1/3O2 Cathode Material by LiF Modification

Sisi Zhou,Xianggong Zhang,Zhihao Zhang,Songting Liu,Rui Wang

DOI: https://doi.org/10.3390/coatings13040727

IF: 3.236

2023-04-04

Coatings

Abstract:LiNi1/3Co1/3Mn1/3O2 is a widely used commercial cathode material in the fields of consumer electronics and electric vehicles. However, its energy density still falls short of the standard and needs to be improved. The most effective method is to increase the cut-off voltage, but this will result in a drop in capacity. In this study, a LiF layer is coated on the surface of LiNi1/3Co1/3Mn1/3O2 via an in situ method. It is found that the LiF layer may protect materials from side reactions with electrolytes, improve the interfacial stability, and enhance the cyclic performance. The bare sample shows relatively poor cycling stability, with capacity retention rates of 65.9% (0.2 C) and 12.8% (5 C) after 100 cycles, while 1% LiF-coated NCM has higher cycling stability with capacity retention rates of 83.4% (0.2 C) and 73.3% (5 C) after 100 cycles, respectively. Our findings suggest that a LiF surface layer could be a useful means of boosting the electrochemical performance of NCM cathode materials.

materials science, multidisciplinary,physics, applied, coatings & films

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to improve the electrochemical performance of LiNi\(_{1/3}\)Co\(_{1/3}\)Mn\(_{1/3}\)O\(_2\) (abbreviated as NCM), which is a cathode material for lithium - ion batteries. Specifically, the author focuses on how to increase its energy density by increasing the cut - off voltage of the material while reducing the resulting capacity degradation problem. To achieve this goal, the researchers adopted a surface modification method, that is, a thin and uniform LiF layer was formed on the surface of NCM particles by in - situ thermal decomposition of LiPF\(_6\). Research shows that this LiF layer can protect the material from side reactions with the electrolyte, improve interface stability, and enhance cycling performance. The experimental results show that the NCM sample modified with 1% LiF exhibits the highest cycling stability and rate performance, and the capacity retention rates at 0.2C and 5C reach 83.4% and 73.3% respectively, which are significantly better than those of the unmodified sample. These findings indicate that the LiF surface layer is an effective method to improve the electrochemical performance of NCM cathode materials.