Investigating Thermal and Mechanical Characteristics of Die-Casting Aluminum Alloys: A Comprehensive Investigation via Thermal Analysis

Lu Zhang,Jiang Li

DOI: https://doi.org/10.1007/s40962-024-01258-z

2024-02-10

International Journal of Metalcasting

Abstract:In this study, the vacuum-assisted high-pressure die casting (VHPDC) process was used to produce 3-mm thin-walled AlSi9Cu3 alloy. The thermal and mechanical properties of the material were investigated using differential scanning calorimetry (DSC), a universal testing machine, a laser flash analyzer (LFA), and a thermal mechanical analyzer (TMA). A preliminary determination of the aging and solution temperature range was conducted via DSC. The thermal expansion of the as-cast (F) samples after heating to 480 °C for 6 h was measured using TMA, and further verified after heat treatment of the solution at 480 °C for 30 min through tensile testing. The thermal expansion dimension and thermal conductivity changes from 25 to 300 °C in the as-cast (F), T5, and T6 states were measured via TMA and LFA. The heat treatment process parameters of thin-walled die castings could be determined by combining the thermal analysis (DSC and TMA) and mechanical tensile test results. Furthermore, the heat treatment at 200 °C for 4 h and 480 °C for 30 min combined with 200 °C for 4 h achieved improved mechanical properties (tensile strength Rm ≥ 320 MPa), good dimensional stability and the thermal conductivity at 150 °C was higher than 150 W/(m °C).

metallurgy & metallurgical engineering