Mechanism of cryogenic, solid solution and aging compound heat treatment of die-cast Al alloys considering microstructure variation

Cheng Tao,Xiao-Nong Cheng,Zhi-Qiang Li,Guang-Lei Liu,Fu-Hai Xu,Shu-Kuan Xie,Zhong-Hua Kuang,Yong Guo,Hai-Xia Liu
DOI: https://doi.org/10.1007/s12598-023-02341-w
IF: 6.318
2023-08-08
Rare Metals
Abstract:To develop a new compound heat treatment process for improving the mechanical properties of die-cast Al alloys, this study investigated the effects of cryogenic, solution and aging compound treatment on the microstructure and mechanical properties of die-cast Al alloys. The characterization methods used were optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron backscatter diffraction (EBSD), and tensile tests; and the Image Pro Plus software was used for statistical analysis. The results indicated that compared with T6 heat treatment, the compound heat treatment process consisting of cryogenic treatment (−196 °C for 12 h), solid solution treatment (476 °C for 22 min), and aging (159 °C for 403 min) significantly enhanced the mechanical properties of the die-cast Al alloys. For instance, the tensile strength increased from 224.3 to 249.5 MPa; the hardness increased from HV 110.5 to HV 124.6, and the elongation increased from 6.28% to 7.72%, which in relative terms corresponds to 11.2%, 12.8% and 22.9%, respectively. The compound heat treatment process of the alloy led to significant refinement of its α-Al phases. In addition, Si phases tended to be more ellipsoidal or granular, while the tips of Fe-containing phases became rounded, which played a key role in enhancing the mechanical properties and microstructure stability of the alloys.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?