The synergistic effect between fluoridation degradation and dislocation sliding on stress corrosion failure of Monel 400 alloy in HF vapor

Hailong Dai,Shouwen Shi,Can Guo,Zuoliang Ning,Yue Kuang,Xu Chen

DOI: https://doi.org/10.1016/j.corsci.2023.111489

IF: 7.72

2023-09-02

Corrosion Science

Abstract:The stress corrosion mechanism of Monel 400 alloy in HF vapor were studied by the synergetic effect of HF vapor corrosion and dislocation sliding. Results show that the corrosion of HF vapor assisted by oxygen will worsen the fluorination effect and lead to serious fluorination degradation of Monel 400 alloy. The formation of CuF 2 will harm the Ni element in the matrix and lead to the dealloying phenomenon of denickelification. Dislocation sliding not only accelerates the corrosion degradation, but also tears denickelification layer easily, leading to transgranular cracks initiation. A law of crack initiation based on Schmid factor is given.

materials science, multidisciplinary,metallurgy & metallurgical engineering