Effect of irradiation damage defects on the impurity containing molten salt corrosion behavior in GH3535 alloy

Weichi Ji,Zhenbo Zhu,Hefei Huang,Bin Leng,Guanhong Lei,Yan Li
DOI: https://doi.org/10.1016/j.corsci.2023.111475
IF: 7.72
2023-08-28
Corrosion Science
Abstract:This study explores the corrosion response of irradiated nickel-based GH3535 alloy in impurity-enriched molten FLiNaK salt at 650 °C. Displacement damage resulting from Au ion irradiation formats dislocation loops, whose distribution is influenced by subsequent He ion irradiation and He bubble formation. Samples irradiated with Au ions exhibit a shallow corrosion layer with big-size and dense distributed Cr 2 O 3 particles, while a contrasting trend is observed in samples irradiated with He ions. Displacement damage decelerates Cr outward diffusion by promoting protective Cr 2 O 3 formation with SO 4 2- impurities, thereby inhibiting impurity-accelerated corrosion. However, the accelerating effect of He bubbles subsequently counteracts this inhibitory impact on corrosion.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?