Effect of Cr on the high-temperature corrosion of dissimilar AISI 904L and Inconel 625 joints employed in the coal-fired thermal power plant tubes
S. Senthur Prabu,S. M. Muthu,S. Sujai,K. Devendranath Ramkumar,D. T. Arunkumar,N. Beemkumar,S. Senthur PrabuS. M. MuthuS. SujaiK. Devendranath RamkumarD. T. ArunkumarN. Beemkumara School of Mechanical Engineering,VIT University,Vellore,Indiab Centre for Additive Manufacturing,Chennai Institute of Technology,Chennai,Indiac Department of Mechanical Engineering,Jain University,Bangalore,India
DOI: https://doi.org/10.1080/09603409.2024.2327156
2024-03-13
Materials at High Temperatures
Abstract:The hot corrosion behaviours of 5-mm-thick plates of dissimilar AISI 904L and Inconel 625 weldments produced by continuous current gas tungsten arc welding process using Ni-Cr-Mo-enriched filler wires (ERNiCrMo-4 and ERNiCrCoMo-1) were investigated. Optical microscopy was used to examine the microstructure of these weldments. The corrosion performance of the weldments and base metals was determined in the mixture of K 2 SO 4 + 60% NaCl molten salt (MS) and air oxidation conditions at 700°C for 50 cycles. The thermogravimetric plots derived the corrosion kinetics of the weldments. The microstructure and the elemental analysis of the scales formed on the corroded samples were evaluated by scanning electron microscopy and energy-dispersive spectroscopy. The phases developed on the oxide layers during the corrosion were analysed using X-ray diffraction. The fusion zones of ERNiCrCoMo-1 weldment and AISI 904L base metal were vulnerable to degradation in the MS environment, causing severe cracks and spallation compared to ERNiCrCoMo-1 weldment.
materials science, multidisciplinary,metallurgy & metallurgical engineering