Abstract:Due to their excellent attributes of high water permeance, good stability and antifouling properties, silicon carbide (SiC) membranes have achieved widespread application in industrial wastewater treatment facilities. However, the high sintering temperature (usually beyond 2000 °C) during the preparation of porous silicon carbide is a challenge for the transfer of the technology from the laboratory to industry. An efficient sintering additive method was proposed herein to address this issue. Inexpensive residues (containing oxides of sodium, aluminum and silicon) from an NaA zeolite production line were used as the sintering additives to make the SiC particles more tightly connected due to the formation of new phases. Thus, a SiC network could be formed during an in-situ reaction at lower sintering temperature (e.g., 1000 °C) in air without inert gas protection. The as-prepared SiC membranes exhibited a high pure water permeance of 3700 L m-2 h-1 bar-1 and open porosity of 46%. The mechanical strength of the membrane reached 45 MPa. After alkali corrosion or thermal shock resistance tests, the bending strength was maintained at least 38 MPa. The membrane with a mean pore size of 0.4 μm exhibited a high rejection rate to oil droplets (˃ 90%) in various oil-in-water emulsions with a high water permeance. Membrane cleaning with an ultrasonic treatment resulted in good stability in long-term filtration tests. The utilization of zeolite residues successfully reduced the operational cost of heating during ceramic membrane fabrication with recycled solid wastes. Hence, the proposed preparation method for SiC membranes has good sustainability and is scalable for oil-water separation applications.

Properties and performance of cordierite-bonded porous silicon carbide membrane prepared using waste fly ash and other oxide additives

Influence of additive contents on the properties of SiC ceramic membranes and their performance in oil‐water separation

Permeability Behavior and Wastewater Filtration Performance of Mullite Bonded Porous SiC Ceramic Membrane Prepared Using Coal Fly Ash as Sintering Additive

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Fabrication of Homogeneous Mullite-Based Fiber Porous Ceramics with High Strength and Porosity

One-step dip-coating method for preparation of ceramic nanofiber membrane with high permeability and low cost

Preparation of high performance porous SiC ceramic membrane support using zeolite and alumina as sintering additives

Processing and microstructure-permeation properties of silica bonded silicon carbide ceramic membrane

Silicon carbide ceramic membrane support sintered at 800 °C with low-temperature sintering aid

Extrusion of Silicon Carbide Based Tubular Membrane Incorporated With Coal Fly Ash and Performance Evaluation in Water Treatment

In-situ Synthesis and Properties of Cordierite-Bonded Porous SiC Membrane Supports Using Diatomite As Silicon Source

Porous ceramic membranes from coal fly ash with addition of various pore-forming agents for oil-in-water emulsion separation

Lower-temperature preparation of SiC ceramic membrane using zeolite residue as sintering aid for oil-in-water separation

Effects of chemical corrosion and thermal shock on the properties of mullite- and cordierite-bonded porous SiC ceramics prepared using waste fly ash

Preparation of porous mullite ceramic supports from high alumina fly ash

Compact SiOC Ceramic Composite Nanofiltration Membranes by Slow Dip Coating for Water Purification

Ceramic Processing of Silicon Carbide Membranes with the Aid of Aluminum Nitrate Nonahydrate: Preparation, Characterization, and Performance

Enhanced Performance of Fly Ash-Based Supports for Low-Cost Ceramic Membranes with the Addition of Bauxite

Mullite whisker-constructed ceramic membranes prepared from fly ash by in-situ catalytic reaction

Feasible recycling of industrial waste coal fly ash for preparation of anorthite-cordierite based porous ceramic membrane supports with addition of dolomite

Tuning Microstructures and Separation Behaviors of Pure Silicon Carbide Membranes