Abstract:Composite sandwich beams with a carbon fiber reinforced polymer (CFRP) square honeycomb core were designed and fabricated by using the interlocking method. The dynamic response and failure mechanism of fully-clamped and simply- supported sandwich beams subjected to low-velocity impact were investigated experimentally and the corresponding failure modes of the sandwich beams were obtained. Meanwhile, the damage evolvement process and the failure mechanism were analyzed in detail. Influences of the impact velocity, boundary conditions, the mass distributions of face sheets and the direction of the slots on the failure modes and load-carrying capacity of the sandwich beams were explored. The low-velocity impact experiments of composites specimens with two kinds of boundary conditions were carried out by using the drop-hammer impact test system. Three kinds of initial impact velocity were considered for the simply-supported and the fully- clamped sandwich beams sandwich beams, respectively. In the experiments, the time history curves of the impact load and the midspan deflection of the specimens were recorded by a load cell and a laser displacement sensor. Meanwhile, the deformation processes of the sandwich beams were captured by a high-speed camera. The experimental results show that the directions for the slots of the long ribs have significant influence on the failure modes of the sandwich beams. The sandwich core with the upward slots at the midspan has compression deformation whilst the cracking failure along the direction of the downward slots at the midspan is observed due to the tension, which results in the face-sheet debonding and rib fracture successively. It is found that for the same mass, the design of the thicker upper face sheet can enhance the impact resistance of the sandwich beams. The peak load and load-carrying capacity of the sandwich beams increase with increasing the impact velocity. The fully-clamped boundary conditions make the sandwich beams exhibit hardening post-failure behaviors obviously. After the initial failure at the midspan, the fully-clamped ends of the cores and the face-sheets of the sandwich beams experience the fracture failure.

Low-velocity impact of sandwich beams with fibre-metal laminate face-sheets considering local denting effect

Dynamic Response of Slender Multilayer Sandwich Beams with Fiber-Metal Laminate Face-Sheets Subjected to Low-Velocity Impact

Low-Velocity Impact Response of Fully Clamped Metal Foam Core Sandwich Beam Incorporating Local Denting Effect

Plastic behavior of sandwich beams with fiber metal laminate face-sheets and metal foam core: Combined local denting and overall deformation

Low-velocity Impact Response of Sandwich Beams with a Metal Foam Core: Experimental and Theoretical Investigations

Analytical and Numerical Investigation on Dynamic Behavior of Rectangular FML Sandwich Tubes with Metal Foam Core under Low-Velocity Impact

Low-velocity impact of clamped Y-shaped sandwich beams with metal foam core

Low-velocity Impact Response of Geometrically Asymmetric Slender Sandwich Beams with Metal Foam Core

Low-velocity Impact on Square Sandwich Plates with Fibre-Metal Laminate Face-Sheets: Analytical and Numerical Research

Dynamic Response of Slender Multilayer Sandwich Beams with Metal Foam Cores Subjected to Low-Velocity Impact

Low-Velocity Impact of Clamped Rectangular Sandwich Tubes with Fiber Metal Laminated Tubes

A Theoretical Study of Low-Velocity Impact of Geometrically Asymmetric Sandwich Beams

Low-velocity Impact of Rectangular Multilayer Sandwich Plates

Dynamic response of multilayer sandwich beams with foam-filled trapezoidal corrugated and foam cores under low-velocity impact

The Plastic Behavior in the Large Deflection Response of Fiber Metal Laminate Sandwich Beams under Transverse Loading

On Dynamic Response of Rectangular Sandwich Plates with Fibre-Metal Laminate Face-Sheets under Blast Loading

Low-velocity Impact and Minimum Mass Design of Physically Asymmetric Sandwich Beams with Metal Foam Core

Plastic analysis of metal foam core sandwich beam transversely loaded by a flat punch: Combined local denting and overall deformation

Dynamic Response of Fiber-Metal Laminates Sandwich Beams under Uniform Blast Loading

Deformation and Failure of Hybrid Composite Sandwich Beams with a Metal Foam Core under Quasi-Static Load and Low-Velocity Impact

Low-velocity impact response and failure mechanism of CFRP sandwich beams with a square honeycomb core fabricated by the interlocking method