Abstract:Composite sandwich beams with a carbon fiber reinforced polymer (CFRP) square honeycomb core were designed and fabricated by using the interlocking method. The dynamic response and failure mechanism of fully-clamped and simply- supported sandwich beams subjected to low-velocity impact were investigated experimentally and the corresponding failure modes of the sandwich beams were obtained. Meanwhile, the damage evolvement process and the failure mechanism were analyzed in detail. Influences of the impact velocity, boundary conditions, the mass distributions of face sheets and the direction of the slots on the failure modes and load-carrying capacity of the sandwich beams were explored. The low-velocity impact experiments of composites specimens with two kinds of boundary conditions were carried out by using the drop-hammer impact test system. Three kinds of initial impact velocity were considered for the simply-supported and the fully- clamped sandwich beams sandwich beams, respectively. In the experiments, the time history curves of the impact load and the midspan deflection of the specimens were recorded by a load cell and a laser displacement sensor. Meanwhile, the deformation processes of the sandwich beams were captured by a high-speed camera. The experimental results show that the directions for the slots of the long ribs have significant influence on the failure modes of the sandwich beams. The sandwich core with the upward slots at the midspan has compression deformation whilst the cracking failure along the direction of the downward slots at the midspan is observed due to the tension, which results in the face-sheet debonding and rib fracture successively. It is found that for the same mass, the design of the thicker upper face sheet can enhance the impact resistance of the sandwich beams. The peak load and load-carrying capacity of the sandwich beams increase with increasing the impact velocity. The fully-clamped boundary conditions make the sandwich beams exhibit hardening post-failure behaviors obviously. After the initial failure at the midspan, the fully-clamped ends of the cores and the face-sheets of the sandwich beams experience the fracture failure.

Experimental and theoretical study on the response of the X-frame CFRP sandwich beam under the local impulsive loading

Dynamic Behavior of CFRP-Strengthened Reinforced Concrete Beams Without Stirrups under Impact Loading

Analysis of the Dynamic Response in Blast-Loaded CFRP-Strengthened Metallic Beams

Experimental and numerical study on the ballistic impact resistance of the CFRP sandwich panel with the X-frame cores

The Structural Response of Clamped Sandwich Beams Subjected to Impact Loading

The influence of asymmetric faces on low-velocity impact failure of CFRP/aluminum foam composite sandwich beams

Low-velocity Impact Behavior of X-Frame Core Sandwich Structures – Experimental and Numerical Investigation

The Mechanical Response of Metallic Sandwich Beams under Foam Projectile Impact Loading

Deformation and Failure of Hybrid Composite Sandwich Beams with a Metal Foam Core under Quasi-Static Load and Low-Velocity Impact

The impact and post-impact flexural behaviors of CFRP/aluminum-honeycomb sandwich

Low-velocity impact response and failure mechanism of CFRP sandwich beams with a square honeycomb core fabricated by the interlocking method

Impulsive Response of Composite Sandwich Structure with Tetrahedral Truss Core

Low-velocity Impact Response of Sandwich Beams with a Metal Foam Core: Experimental and Theoretical Investigations

Experimental and Numerical Investigations on Impact Response of Reinforced Concrete Beams with a Sandwich Panel Protective Layer

Low-velocity impact properties of foam-filled composite lattice sandwich beams: Experimental study and numerical simulation

On low-velocity impact response of foam-core sandwich panels

Quasi-static and Low-Velocity Impact Behaviors of Steel-Aluminum Foam Sandwich Beams

Dynamic Response of Fiber-Metal Laminates Sandwich Beams under Uniform Blast Loading

Dynamic response and failure of carbon/epoxy composite sandwich subjected to underwater impulsive loading

Numerical Simulation on Impact Test of CFRP Strengthened Reinforced Concrete Beams

Three-point bending behaviors of the foam-filled CFRP X-core sandwich panel: Experimental investigation and analytical modelling