Abstract:Composite sandwich beams with a carbon fiber reinforced polymer (CFRP) square honeycomb core were designed and fabricated by using the interlocking method. The dynamic response and failure mechanism of fully-clamped and simply- supported sandwich beams subjected to low-velocity impact were investigated experimentally and the corresponding failure modes of the sandwich beams were obtained. Meanwhile, the damage evolvement process and the failure mechanism were analyzed in detail. Influences of the impact velocity, boundary conditions, the mass distributions of face sheets and the direction of the slots on the failure modes and load-carrying capacity of the sandwich beams were explored. The low-velocity impact experiments of composites specimens with two kinds of boundary conditions were carried out by using the drop-hammer impact test system. Three kinds of initial impact velocity were considered for the simply-supported and the fully- clamped sandwich beams sandwich beams, respectively. In the experiments, the time history curves of the impact load and the midspan deflection of the specimens were recorded by a load cell and a laser displacement sensor. Meanwhile, the deformation processes of the sandwich beams were captured by a high-speed camera. The experimental results show that the directions for the slots of the long ribs have significant influence on the failure modes of the sandwich beams. The sandwich core with the upward slots at the midspan has compression deformation whilst the cracking failure along the direction of the downward slots at the midspan is observed due to the tension, which results in the face-sheet debonding and rib fracture successively. It is found that for the same mass, the design of the thicker upper face sheet can enhance the impact resistance of the sandwich beams. The peak load and load-carrying capacity of the sandwich beams increase with increasing the impact velocity. The fully-clamped boundary conditions make the sandwich beams exhibit hardening post-failure behaviors obviously. After the initial failure at the midspan, the fully-clamped ends of the cores and the face-sheets of the sandwich beams experience the fracture failure.

Dynamic response and failure of CFRP Kagome lattice core sandwich panels subjected to low-velocity impact

Experiment and finite element analysis of lattice reinforced composite sandwich panels subjected to low-velocity impact

Experimental and Numerical Study on the Low-Velocity Impact Behavior of Foam-Core Sandwich Panels

On Quasi-Static and Dynamic Compressive Behaviors of Interlocked Composite Kagome Lattice Structures

Impact responses and residual flexural properties of narrow CFRP laminates

High Velocity Impact Response of Composite Lattice Core Sandwich Structures

Damage behavior and failure mechanism of composite sandwich panel subjected to localized impact: A comprehensive study

Low-velocity impact response and failure mechanism of CFRP sandwich beams with a square honeycomb core fabricated by the interlocking method

Dynamic Response of Foam Core Sandwich Panel with Composite Facesheets During Low-Velocity Impact and Penetration

The influence of asymmetric faces on low-velocity impact failure of CFRP/aluminum foam composite sandwich beams

Experimental investigation on response mechanism and impact resistance of glass fiber reinforced polymer X‐type foldcore sandwich panel subjected to low‐velocity impact experiments

Response of the orthogonal corrugated sandwich panel under low-velocity impact with different shaped impactors

Damage Mechanisms and Analytical Model of CFRP Laminate under Low-Velocity Normal and Oblique Impacts

Experimental and Numerical Study of Low-Velocity Impact Damage in Sandwich Panel with UHMWPE Composite Facings

Experimental and Simulation Study on Failure of Thermoplastic Carbon Fiber Composite Laminates under Low-Velocity Impact

Experimental and numerical investigations on the dynamic response of woven carbon fiber reinforced thick composite laminates under low-velocity impact

Low-Velocity Impact Behavior and Damage Characteristics of CFRP Laminates

Experimental and numerical simulation of dynamic response of U-type corrugated sandwich panels under low-velocity impact

Experimental and numerical study on the ballistic impact resistance of the CFRP sandwich panel with the X-frame cores

On low-velocity impact response of foam-core sandwich panels

Lattice Truss Core Sandwich Structures With Al Lattice Truss Core And Cfrp Composite Fachesheets Under Impact Loads