Abstract:ZrO 2 ceramics are commonly known as 'hard and brittle' materials due to their exceptional properties, such as high hardness, heat resistance, chemical stability, and low thermal conductivity. However, the hole processing technique for ZrO 2 ceramics often results in significant tool wear and compromises the quality of the holes. This study investigates the removal mechanism of ZrO 2 ceramic materials by using carbide tools, diamond-coated carbide tools, and micro-sintered tools. It also analyzes the impact of processing parameters on the wear mechanism of different tools and the quality of hole processing in ZrO 2 ceramics. The findings revealed that at high spindle speed (8000 r/min) and low feed rate (1 mm/min), the diamond coating on the rake surface of the diamond-coated carbide tool tends to peel off, leading to the formation of sharp edges on the flank surface. This phenomenon results in a reduction in thrust forces. Moreover, it is observed that as the number of hole machining operations increases, the peeling of the diamond coating on the tool flank becomes more severe. The increase in feed rate causes the diamond coating peeling area on the rake face of the tool to expand toward the chisel edge and even reach the thinned edge area near the chisel edge. When the feed rate of carbide tools increases, the wear degree of the chisel edge gradually increases, while the wear degree of the main cutting edge corner position gradually decreases. At low spindle speeds, the main cutting edge breaks and the cutter head is also damaged and deformed. The main wear mechanisms of micro-sintered tools involve shedding, fragmentation, wear, and adhesion of diamond abrasive grains. The bottom surface of the tool tends to accumulate a significant amount of flaky adhesion, which dulls the tool and increases thrust force. In contrast to carbide tools, diamond-coated carbide tools offer improved hole exit quality. However, micro-sintered tools often exhibit large volumes of flaking at the hole exits, resulting in shell-like stripes on the peeled surface.

Cutting performance and wear mechanism of zirconia toughened alumina ceramic cutting tools formed by vat photopolymerization-based 3D printing

Vat photopolymerization-based 3D printing of complex-shaped and high-performance Al2O3 ceramic tool with chip-breaking grooves: Cutting performance and wear mechanism

Realization of complex-shaped and high-performance alumina ceramic cutting tools via Vat photopolymerization based 3D printing: A novel surface modification strategy through coupling agents aluminic acid ester and silane coupling agent

Fabrication of Complex-Shaped Zirconia Ceramic Parts Via a DLP-stereolithography-based 3D Printing Method

Study on milling performances of 3Y-TZP ceramics using PCD and PCBN tools

Comparative study of tool wear mechanisms in drilling ZrO2 ceramics using various tool types

Preparation of Al2O3/Ti(C,N)/ZrO2/CaF2@Al(OH)3 Ceramic Tools and Cutting Performance in Turning

Theoretical and Experimental Investigation on Inclined Ultrasonic Elliptical Vibration Cutting of Alumina Ceramics

Mechanical properties and cutting performance of laminated graphene composite ceramic tools

Preparation of excellent performance ZTA ceramics and complex shaped components using digital light processing 3D printing technology

Microstructure, mechanical properties, friction and wear performance, and cytotoxicity of additively manufactured zirconia-toughened alumina for dental applications

Evaluation of Polycrystalline Diamond Tools in Milling of Pre-Sintered and Fully-Sintered Zirconia Ceramics

Towards high strengthening efficiency of equiaxed and platelet-shaped alumina reinforced zirconia ceramics with textured microstructure using DLP-based stereolithography

Study on helical milling of small holes in zirconia ceramics with PCD tools

Mechanical properties and wear behaviors of Cu-doped zirconia-toughened alumina ceramics

Wear mechanism and cutting performance evaluation of fine ceramic tools

The Rising Crack Resistance Curve Behavior and Mechanism of La2O3 Doped Zirconia Toughened Alumina Composites Prepared Via Vat Photopolymerization Based 3D Printing

R-curve of La2O3 doped Zirconia Toughened Alumina Composites Prepared via Stereolithography based 3D Printing

Preparation and cutting performance study of YSZ-toughened PcBN superhard tools

Preparation of ZTA composite ceramics derived from sol–gel method by DIW printing

Micromilling of high-aspect-ratio ceramic thin walls with customized micro PCD end mills