Abstract:PURPOSE The clinical failures of zirconia dental restorations are often caused by extrinsic artifacts introduced by processing. The aim of this study was to investigate the micro-defects and residual stresses generated during the multistep process of zirconia dental restorations. MATERIALS AND METHODS Thermal spray granulated 3Y-TZP powders were dry pressed by two tools exhibiting distinctly different Young's moduli, cold isostatic pressed (CIP-ed), and pressure-less fully sintered. The green bodies pressed by a stiff tool were treated with different procedures: direct milling (green milling) followed by fully sintering; half-sintering and milling (raw milling) with or without fully sintering; and fully sintering followed by grinding. The fully sintered 3Y-TZP crowns were clinically adjusted using both a diamond bur and SiC bur, respectively. Phase composition and microstructure of the pressed, milled, and ground surfaces were studied by XRD and SEM. RESULTS Tetragonal phase was the main phase of all detected 3Y-TZP specimens. Excessive residual stresses introduced by raw milling and grinding were confirmed by a strained T (111) peak, monoclinic phase, and obviously changed I(002)t /I(200)t ratio. The residual stresses would form a compressive stress layer, while it was too shallow to inhibit crack propagation even for ground specimens. Large voids with high-coordination numbers were the common packing micro-defects. Once formed, they were barely healed by CIP-ing and sintering. A stiff pressing tool was confirmed to be useful for reducing the surface packing voids. Milling removed the surface voids, but was no help for the interior ones. Raw milling introduced more serious chippings, most originating from the existing packing voids, than green milling due to its brittle failure and was less recommended for production. Grinding dense 3Y-TZP caused surface grain refinement and much more severe micro-defects, especially when clinical adjustment was applied by diamond bur compared to SiC bur. CONCLUSIONS Micro-defects and residual stresses are introduced and accumulated through the entire production chain and determine the final microstructure of zirconia dental restorations. Several procedural improvements are offered and expected to reduce processing micro-defects.

Study on milling performances of 3Y-TZP ceramics using PCD and PCBN tools

Evaluation of Polycrystalline Diamond Tools in Milling of Pre-Sintered and Fully-Sintered Zirconia Ceramics

Wear Behaviors of Pcd Tools in Turning Granite

A Machining Science Approach to Dental Cutting of Glass Ceramics Using an Electric Handpiece and Diamond Burs

Cutting characteristics of dental glass ceramics during in vitro dental abrasive adjusting using a high-speed electric handpiece

Effect of grinding parameters on surface integrity and flexural strength of 3Y-TZP ceramic

Surface Properties of Dental 3Y-TZP with Different Treatments

Optimization of Machining Parameters for Milling Zirconia Ceramics by Polycrystalline Diamond Tool

Study on helical milling of small holes in zirconia ceramics with PCD tools

Preparation and cutting performance study of YSZ-toughened PcBN superhard tools

Micromilling of high-aspect-ratio ceramic thin walls with customized micro PCD end mills

Temperature field simulation and optimization of processing parameters for laser-assisted machining of 3Y-TZP ceramics

Helical Milling of Small Holes in Fully-Sintered Zirconia Ceramic with PCD Tools

Cutting performance and wear mechanism of zirconia toughened alumina ceramic cutting tools formed by vat photopolymerization-based 3D printing

Experimental investigation of coatings efficiency in micro-ball-end milling of pre-sintered 5Y-TZP ceramic

Comparative study of tool wear mechanisms in drilling ZrO2 ceramics using various tool types

Cutting Performance and Wear/Damage Characteristics of PCBN Tool in Hard Milling

Effect of Multistep Processing Technique on the Formation of Micro-Defects and Residual Stresses in Zirconia Dental Restorations.

Evaluation of milling performance of 50-μm D-shaped carbide tool, polycrystalline diamond-coated carbide tool, and polycrystalline diamond tool

Y-TZP ceramic processing from coprecipitated powders: a comparative study with three commercial dental ceramics

Cutting performance and wear behavior of diamond, coated cemented carbide and PCBN tools during milling of C f /SiC composites