Abstract:While the addition of WC increases the hardness and wear resistance of coatings, an excessive WC content can also induce crack initiation and propagation, increasing brittleness and leading to premature failure. Therefore, in this study, WC particles were incorporated into nickel-based coatings by plasma-arc surfacing to optimize their content and distribution, balancing their tensile properties and wear resistance. The coatings were comprehensively evaluated through microstructural analysis, hardness testing, wear resistance assessment, and tensile testing. The results show that as the mass fraction of WC increased from 45% to 65%, the increase in carbon significantly promoted the formation of M7C3, M6C, and M23C6 carbides and suppressed the formation of the γ-phase. The microstructural analysis showed that the content of massive carbides increased significantly with the increasing WC content, and the XPS analysis further confirmed that the changes in the WC and Cr7C3 phases were particularly pronounced in the high-WC coating. The 65% WC coating showed higher hardness (a 232 increase in HV1.0), a lower and more stable coefficient of friction (0.42), and better wear resistance than the 45% WC coating, with a wear rate of 3.329 × 10−6 mm3/(N·m)−1, which was 3.709 × 10−6 mm3/(N·m)−1 lower than that of the 45% WC coating. The conventional tensile test results show that the maximum stress and strain of the 45% WC coating were 71% and 36% higher than those of the 65% WC coating, respectively. In addition, the 45% WC coating exhibited better ductility and quasi-cleavage characteristics, whereas the 65% WC coating showed typical brittle cracking behavior. The results of the field tensile tests also showed that the fracture time of the 65% WC coating was 27 s shorter than that of the 45% WC coating. Overall, the 45% WC coating had a good combination of strength and toughness.

Evaluation of Steel and Tungsten Carbide Cobalt (WC 8Co) 5.56 x 45 mm Caliber Projectile Penetration into Silicon Carbide (SiC) Experiment and Numerical Simulation

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Study of Armor-Piercing Self-Sharpening Properties of 88Wc-12Co Material

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Tungsten carbide core 12.7x99 mm AP projectiles ballistic behavior against high hardness steel armor

Cold-sprayed Cu Matrix Composite Coatings with Core-Shell Structured Co@WC Reinforcements on Q235 Steel

Design for Manufacturing of Cemented Carbide Coated Components Toward High Wear and Impact Resistance Performance

Preparation of Ultra-Fine WC-Co Cermet and Its Wear Behavior

Optimizing Wear Resistance and Tensile Strength of Nickel-Based Coatings through Tungsten Carbide Reinforcement

Effect of Spherical WC Content on the Microstructure and Properties of SiCp Aluminium Composite Material

Ballistic Resistance of Silicon-Carbide-Based Ceramic and Ultrahigh-Molecular-Weight Polyethylene Composite Armor

Study on the Penetration Performance of a 5.8 mm Ceramic Composite Projectile

Friction and wear behavior of Ni-based alloy coatings with different amount of WC–TiC ceramic particles

Numerical simulation of the penetration resistance of ceramic composite armor with corrugated structure

Ballistic performance of spherical fragments penetrating PCrNi3MoV target plates

Microstructure and wear resistance of bimodal cemented carbide coating prepared by direct laser powder deposition

WC/Ni Cemented Carbide Coating and Its Wear Resistance Synthesized by Laser Powder Feeding Cladding

A Morphological Study and Effect of Intermediate Phase Formation on Hard and Wear Resistant SiC-Co Composite Coating on Low Carbon Steel via Arc Based Heat Source

Study on transition from dwell/interface defeat to penetration of long-rod projectile impacting silicon carbide

Influence of WC-12Co reinforcement on sliding wear performance of stainless steel-based MMC processed in a microwave oven

Effect of WC-12Co on the mechanical and wear performance of laser melting deposition nickel-based alloy