Abstract:Carbon-fiber reinforced composites are made up of three different phases. Tensile or compressive deformation in the longitudinal (fiber) orientation is controlled by the fibers, leading to a linear stress strain response which ends abruptly when the fibers fail by tensile fracture or kinking in compression. Conversely, major non-linear deformations can develop under transverse compression or in-plane shear because deformation is controlled by the polymeric matrix and the interphase.In this paper, first the V-notched rail shear test was used to research the mechanical properties of composite under in-plane shear loading, and the fracture surfaces of failed specimens were examined using scanning electron microscopy (SEM). The broken samples showed a large residual shear displacement. For [0/90](8s) cross-ply laminate V-notched beam test, the failure mode is the interactions of intralaminar and interlaminar failure. The intralaminar interfacial debonding, matrix cracking and interlaminar degradation occurs in succession. Then a representative volume element (RVE) of fiber random distribution was established, with two dominant damage mechanisms-matrix plastic deformation and interfacial debonding included in the simulation by the extended Drucker-Prager model and cohesive zone model respectively. The simulation results clearly reveal the damage process of the composites and the interactions of different damage mechanisms. It can be concluded that the in-plane shear fracture initiates as interfacial debonding and evolves as a result of interactions between interfacial debonding and matrix plastic deformation. The progressive damage process and final failure mode of in-plane shear model which are based on constitute are very consistent with the observed result under SEM of V-notched rail shear test. Also a transverse shear model was established as contrast in order to comprehensively understand the mechanical properties of composite materials under shear loading, and the progressive damage process and final failure mode of composite under transverse shear loading were researched.

Interface fracture progression of composite T-stiffened skins fabricated by co-bonding and co-curing under tensile loading: an experimental investigation

Computational modelling of postbuckling behavior of composite T-stiffened panels with different bonding methods

Experimental Investigation of the Compaction and Tensile Strength of Co-cured Skin-to-Stiffener Structures

Investigation of the out-of-plane load-bearing capacity of T1100/5405 composite T-stiffened panels

Experimental and Numerical Study on Failure Behaviors of Composite Grid Stiffeners under Tensile and Flexural Loading

Investigation into the Failure of Aircraft Stringer–skin Composite Structure under Bending Load

Failure Mechanism Study on Omega Stringer Debonding

An insight into the mechanical behavior and failure mechanisms of T-stiffened composite structures with through-interface debonding defects

Deformation and Fracture Mechanisms of Automated Fiber Placement Pre-Preg Laminates under Out-of-plane Tensile Loading

Experimental and Numerical Studies on the Failure Mechanism of the Composite Scarf Joints with Bonding Flaws

Evaluation of Carbon Fiber/epoxy Interfacial Strength in Transverse Fiber Bundle Composite: Experiment and Multiscale Failure Modeling

Tensile Failure Behaviors of Adhesively Bonded Structure Based on In Situ X-ray CT and FEA

Experimental and Numerical Investigation of Curve Section Stringer/skin Runout Under Tensile Load

Experimental Research on Fiber Compaction of L-shaped Stiffeners in Stiffened Skins by Autoclave Process

Stiffener debonding mechanisms in post-buckled CFRP aerospace panels

Finite Element-Based Phase-Field Simulation of Interfacial Damage in Unidirectional Composite under Transverse Tension

Fracture toughness and fiber bridging mechanism for mode-I interlaminar failure of spread-tow woven composites

Microscopic Progressive Damage And Failure Analysis Of Carbon-Fiber Reinforced Composite Under Shear Loading

A Study of Failure Strength for Fiber-Reinforced Composite Laminates with Consideration of Interface

Investigations on the Mechanical Properties of Composite T-Joints with Defects under Bending Loading

Failure in co-cured composite joints enhanced with J-272 film