Abstract:To develop the full application potential of composite materials, research on the post-buckling behavior of composite stiffened panels is of great significance. In this paper, the impact and compression after impact (CAI) behaviors of four different types of composite stiffened panels were studied by numerical simulation and experimental methods. The low-velocity impact damage simulated dynamically was introduced as the initial state in the compression simulation, and a two-dimensional shell model with Hashin failure criteria and stiffness degradation was adopted to estimate the failure load of composite stiffened panels under impact and CAI. The error between simulation results and test results was less than 10%, showing that the method used in this study achieved considerable accuracy in experimental results. Analysis of the impact test results revealed that the extent of damage is related to many factors, including the cross-sectional size of stiffeners, the spacing of stiffeners, and the material and thickness of the skin. In addition, the influence of fatigue damage on residual strength after impact was also studied experimentally, with results showing that the buckling and failure loads decreased by about 5% under 106 flight fatigue loads. However, there were obvious fluctuations in the load-displacement curves, which may have been caused by debonding between the stiffeners and the skin. Experimental results and the simulation matrix show that the post-buckling ratio increased with the increase of the stiffness ratio, then was stable after 2.0. Furthermore, the thinner the skin, the greater the post-buckling ratio. The experimental and simulation results provide an important reference for the structural design and failure-mechanism analysis of composite stiffened panels.

Computational modelling of postbuckling behavior of composite T-stiffened panels with different bonding methods

Design and optimization of composite sub-stiffened panels

Viscoelastic Bilinear Cohesive Model and Parameter Identification for Failure Analysis of Adhesive Composite Joints

An insight into the mechanical behavior and failure mechanisms of T-stiffened composite structures with through-interface debonding defects

Analysis and experimental evaluation framework for buckling and post-buckling of composite stiffened panels

Experimental and Numerical Analysis for the Post-Buckling Behavior of Stiffened Composite Panels with Impact Damage

An Experimental and Numerical Study on Impact and Compression after Impact of Stiffened Composite Panels

Numerical and experimental investigation of pre-damaged composite stiffened panel under axial compression

Experimental and numerical research on the analysis methods for buckling and post-buckling of inclined stiffened panel under shear load

Compressive buckling and post-buckling behaviors of J-type composite stiffened panel before and after impact load

Investigation of the out-of-plane load-bearing capacity of T1100/5405 composite T-stiffened panels

Experiment and Analysis of Hat-Stringer-stiffened Composite Curved Panels under Axial Compression

Experimental and Numerical Study on Failure Behaviors of Composite Grid Stiffeners under Tensile and Flexural Loading

Development of a numerical methodology for the analysis of the post-buckling and failure behavior of butt-joint stiffened thermoplastic composite panels

Numerical simulation and experiment validation of variable stiffness composite laminates with open holes under unidirectional tension

Numerical and Experimental Analysis of Delamination in the T-Stiffener Integrated Composite Structure

Stiffener debonding mechanisms in post-buckled CFRP aerospace panels

Modeling on the Effect of Automated Fiber Placement Induced Gaps in Curved Composite Laminates

Experimental and Numerical Investigation of Stiffened Composite Curved Panel under Shear and In-Plane Bending

Experimental and numerical research on the calculation methods for buckling and post-buckling of aircraft tail inclined stiffened panel under compression load

Experimental and numerical investigation of damage evolution in carbon fiber reinforced polymer stiffened panel in post-buckling regime