Abstract:The paper presents study of failure initiation and complex failure mechanisms in bolted joints for fiber reinforced composite laminates using two different progressive damage models simulated through combination of FEA package ABAQUS® and FORTRAN. Maximum stress failure criteria and Yamda-Sun failure criteria are used along with different (compatible) sudden material degradation rules for identification of initial damage as well as detailed study of damage progression in the composite laminates with single bolted and double bolted joints having different geometries and different bolt arrangements. Selection of numerical models was based upon possibly simple and conservative approaches to save computation time as well as to predict safe values of joint strength. Both numerical models, programmed in FORTRAN, were simulated with and without assembly clearance as well as with different design parameters including margin distance, end distance, pitch distance, array pitch distance and the models found to be capable of tracing failure onset in all FE models and provided a very good understanding of failure mechanisms. Static strength prediction by both numerical models had an excellent agreement with each other for all the specimens. Though the static strength prediction by proposed PDMs is reasonably less from experimental value but the error in simulated values and experimental data is found to be very stable. Apart from the stability of error, excellent agreement has been found in the tendency of numerical model predictions to the scattered experimental data. The study also has a great potential to provide a strong basis for a very realistic and computationally inexpensive advanced PDM for bolted joints in composite Laminates as well as an easy and simple tool for comparing different laminate geometries and bolt arrangements.

Development of a numerical methodology for the analysis of the post-buckling and failure behavior of butt-joint stiffened thermoplastic composite panels

Computational modelling of postbuckling behavior of composite T-stiffened panels with different bonding methods

Experimental and Numerical Investigations of Compression Stability of Stiffened Composite Panel with Ply Interleaving

Experimental and numerical investigation of damage evolution in carbon fiber reinforced polymer stiffened panel in post-buckling regime

Experiment and simulations of stiffened panel buckling with composite damage and interfacial delamination

A Post-Buckling Compressive Failure Analysis Framework for Composite Stiffened Panels Considering Intra-, Inter-Laminar Damage and Stiffener Debonding

Simulation and experimental studies of the repaired composite laminate

Design and optimization of composite sub-stiffened panels

An Effective Progressive Damage Analysis Method for Failure Analysis of Composite Scarf Joint

Physically based failure analysis method for laminated composites

Experiments and Simulations of the Mechanical Performance of Repaired Panels

Effects of debonding defects on the postbuckling and failure behaviors of composite stiffened panel under uniaxial compression

EXPERIMENT STUDIES AND FEM SIMULATION OF REPAIRED COMPOSITE LAMINATES

Experimental and Numerical Analysis for the Post-Buckling Behavior of Stiffened Composite Panels with Impact Damage

Numerical and experimental investigation of pre-damaged composite stiffened panel under axial compression

Analysis and experimental evaluation framework for buckling and post-buckling of composite stiffened panels

A Novel Methodology to Research the Residual Compressive Mechanical Properties of Composite Stiffened Panel after Low Velocity Impact Based on Quantification Damage Simulation

A Failure Mechanism Based Model for Numerical Modeling the Compression-after-impact of Foam-Core Sandwich Panels

Experimental and Numerical Analyses of Stiffened Composite Panels with Delamination under a Compressive Load

Failure Analysis of Single and Double Bolted Joints for Composite Laminates

Experimental and Numerical Analysis of Repaired Stiffened Carbon Fiber-Reinforced Plastics Panels under Compression