Abstract:To understand the effect of CaCl2 addition on the dephosphorization ability of steelmaking slags, laboratory experiments were carried out to study the phosphorus distribution between CaO–SiO2–FeOx–P2O5–CaCl2 slags and carbon-saturated iron at steelmaking temperature. The phosphorus distribution ratio between slag and pure iron foil (\( L_{\text{P}}^{{{\text{Fe-}}\gamma }} \)) was measured by equilibrium experiments and converted into the phosphorus distribution ratio between slag and carbon-saturated iron (\( L_{\text{P}}^{{\text{Fe}}{-}{\text{C}}} \)) using thermodynamic calculations. The influential mechanism of CaCl2 was also discussed based on the phases in the slags. It was found that the addition of CaCl2 is beneficial for the improvement of \( L_{\text{P}}^{{{\text{Fe}}{-}{\text{C}}}} \). In the slag with basicity (R = [w(CaO)/w(SiO2)]) of 1.0, the P content in the liquid slag was increased by the addition of CaCl2. When the basicity is sufficiently high (e.g., R≥1.5), the addition of CaCl2 enhances the generation of P-rich solid phases, including both 2CaO·SiO2–3CaO·P2O5 (C2S–C3P) and Ca5Cl(PO4)3. Compared with CaCl2-free slags, CaCl2 addition in BOF slags doesn't evidently change the effects of slag basicity and FeOx content. With the increase of slag basicity (1.0 to 2.0), the amount of C2S–C3P solid solution in the slag climbs obviously, resulting in a higher \( L_{\text{P}}^{{{\text{Fe}}{-}{\text{C}}}} \) both in CaCl2-added slags and CaCl2-free slags, while \( L_{\text{P}}^{{{\text{Fe}}{-}{\text{C}}}} \) increases first and then decreases when the FeOx content varies from 15 to 35 pct in this study.

Effect of highly oxidizing converter dephosphorization slag on dephosphorization behaviour of molten steel

Study on Efficient Dephosphorization in Converter Based on Thermodynamic Calculation

Factors Influencing Dephosphorization of Low Carbon Steel in Converter

Effect of CaO-MgO-FeO-SiO2-xNa2O Slag System on Converter Dephosphorization

Effect of Temperature on Dephosphorization of Hot Metal in Double‐Slag Converter Steelmaking Process by High‐Temperature Laboratorial Experiments

Behavior of Carbothermal Dephosphorization of Phosphorus-Containing Converter Slag and Its Resource Utilization

Dephosphorization in New Double Slag Converter Steelmaking Process with High‐Temperature Laboratorial Experiments

Kinetics of Dephosphorization at Different Slag Basicities in the Double Slag Converter Steelmaking Process

Phosphorus Migration Behavior in the Process of Converter Slag Gasification Dephosphorization

Influence of the Basicity on Phosphorus Enrichment Properties of Decarbonization Slag in Low‐Carbon Double Slag Converter Steelmaking Process with Industrial Experiments, Mineralogy, and Ion–molecule Coexistence Theory

Dephosphorization of high silicon hot metal based on double slag converter steelmaking technology

Dephosphorization Kinetics of Hot Metal at Low Slag Basicity and Low Temperature under the Different Fe2O3 Addition Amounts

Research on mechanism change of temperature effect on dephosphorization in the bottom-blown O 2 -CaO process of semi-steelmaking

Leaching behavior and microstructure of phosphorus in converter slag

Study on the recovery of phosphorus and iron from molten modified high-phosphorus industrial slag by carbothermal reduction

A Kinetic Study on Selective Leaching of Phosphorus from Dephosphorization Slag

Study on the Effect of Different Factors on the Change of the Phosphorus-Rich Phase in High Phosphorus Steel Slag

Dephosphorisation behaviour of blast oxygen furnace (BOF) slag due to carbothermal reduction

Effect of CaCl2 Addition on Phosphorus Distribution Between CaO–SiO2–FeOx–P2O5 Slag and Carbon-Saturated Iron at Steelmaking Temperature

Investigation of P2O5 on the Break Temperature and Phase Composition of Slag from the Double Slag Converter Steelmaking Process

Separation of Phosphorus from Phosphorus-concentrated Steelmaking Slag