Effect of CaCl2 Addition on Phosphorus Distribution Between CaO–SiO2–FeOx–P2O5 Slag and Carbon-Saturated Iron at Steelmaking Temperature

Ziwen Yan,Zhiyin Deng,Miaoyong Zhu

DOI: https://doi.org/10.1007/s11663-021-02236-0

2021-06-11

Metallurgical and Materials Transactions B

Abstract:<p class="a-plus-plus">To understand the effect of CaCl<sub class="a-plus-plus">2</sub> addition on the dephosphorization ability of steelmaking slags, laboratory experiments were carried out to study the phosphorus distribution between CaO–SiO<sub class="a-plus-plus">2</sub>–FeO<sub class="a-plus-plus"><em class="a-plus-plus">x</em></sub>–P<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub>–CaCl<sub class="a-plus-plus">2</sub> slags and carbon-saturated iron at steelmaking temperature. The phosphorus distribution ratio between slag and pure iron foil (<span class="a-plus-plus inline-equation id-i-eq1"><span class="a-plus-plus equation-source format-t-e-x">\( L_{\text{P}}^{{{\text{Fe-}}\gamma }} \)</span></span>) was measured by equilibrium experiments and converted into the phosphorus distribution ratio between slag and carbon-saturated iron (<span class="a-plus-plus inline-equation id-i-eq2"><span class="a-plus-plus equation-source format-t-e-x">\( L_{\text{P}}^{{\text{Fe}}{-}{\text{C}}} \)</span></span>) using thermodynamic calculations. The influential mechanism of CaCl<sub class="a-plus-plus">2</sub> was also discussed based on the phases in the slags. It was found that the addition of CaCl<sub class="a-plus-plus">2</sub> is beneficial for the improvement of <span class="a-plus-plus inline-equation id-i-eq3"><span class="a-plus-plus equation-source format-t-e-x">\( L_{\text{P}}^{{{\text{Fe}}{-}{\text{C}}}} \)</span></span>. In the slag with basicity (<em class="a-plus-plus">R</em> = [<em class="a-plus-plus">w</em>(CaO)/<em class="a-plus-plus">w</em>(SiO<sub class="a-plus-plus">2</sub>)]) of 1.0, the P content in the liquid slag was increased by the addition of CaCl<sub class="a-plus-plus">2</sub>. When the basicity is sufficiently high (<em class="a-plus-plus">e.g.</em>, <em class="a-plus-plus">R</em>≥1.5), the addition of CaCl<sub class="a-plus-plus">2</sub> enhances the generation of P-rich solid phases, including both 2CaO·SiO<sub class="a-plus-plus">2</sub>–3CaO·P<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub> (C<sub class="a-plus-plus">2</sub>S–C<sub class="a-plus-plus">3</sub>P) and Ca<sub class="a-plus-plus">5</sub>Cl(PO<sub class="a-plus-plus">4</sub>)<sub class="a-plus-plus">3</sub>. Compared with CaCl<sub class="a-plus-plus">2</sub>-free slags, CaCl<sub class="a-plus-plus">2</sub> addition in BOF slags doesn't evidently change the effects of slag basicity and FeO<sub class="a-plus-plus"><em class="a-plus-plus">x</em></sub> content. With the increase of slag basicity (1.0 to 2.0), the amount of C<sub class="a-plus-plus">2</sub>S–C<sub class="a-plus-plus">3</sub>P solid solution in the slag climbs obviously, resulting in a higher <span class="a-plus-plus inline-equation id-i-eq4"><span class="a-plus-plus equation-source format-t-e-x">\( L_{\text{P}}^{{{\text{Fe}}{-}{\text{C}}}} \)</span></span> both in CaCl<sub class="a-plus-plus">2</sub>-added slags and CaCl<sub class="a-plus-plus">2</sub>-free slags, while <span class="a-plus-plus inline-equation id-i-eq5"><span class="a-plus-plus equation-source format-t-e-x">\( L_{\text{P}}^{{{\text{Fe}}{-}{\text{C}}}} \)</span></span> increases first and then decreases when the FeO<sub class="a-plus-plus"><em class="a-plus-plus">x</em></sub> content varies from 15 to 35 pct in this study.</p>