Abstract:To understand the effect of CaCl2 addition on the dephosphorization ability of steelmaking slags, laboratory experiments were carried out to study the phosphorus distribution between CaO–SiO2–FeOx–P2O5–CaCl2 slags and carbon-saturated iron at steelmaking temperature. The phosphorus distribution ratio between slag and pure iron foil (\( L_{\text{P}}^{{{\text{Fe-}}\gamma }} \)) was measured by equilibrium experiments and converted into the phosphorus distribution ratio between slag and carbon-saturated iron (\( L_{\text{P}}^{{\text{Fe}}{-}{\text{C}}} \)) using thermodynamic calculations. The influential mechanism of CaCl2 was also discussed based on the phases in the slags. It was found that the addition of CaCl2 is beneficial for the improvement of \( L_{\text{P}}^{{{\text{Fe}}{-}{\text{C}}}} \). In the slag with basicity (R = [w(CaO)/w(SiO2)]) of 1.0, the P content in the liquid slag was increased by the addition of CaCl2. When the basicity is sufficiently high (e.g., R≥1.5), the addition of CaCl2 enhances the generation of P-rich solid phases, including both 2CaO·SiO2–3CaO·P2O5 (C2S–C3P) and Ca5Cl(PO4)3. Compared with CaCl2-free slags, CaCl2 addition in BOF slags doesn't evidently change the effects of slag basicity and FeOx content. With the increase of slag basicity (1.0 to 2.0), the amount of C2S–C3P solid solution in the slag climbs obviously, resulting in a higher \( L_{\text{P}}^{{{\text{Fe}}{-}{\text{C}}}} \) both in CaCl2-added slags and CaCl2-free slags, while \( L_{\text{P}}^{{{\text{Fe}}{-}{\text{C}}}} \) increases first and then decreases when the FeOx content varies from 15 to 35 pct in this study.

Effect of Basicity on the Solid Solution Behavior of Phosphorus and In Situ Separation of nC2S–C3P Solid Solution from Molten Steelmaking Slag via Super-Gravity

Solidification Structure of Low Carbon Steel Strips with Different Phosphorus Contents Produced by Strip Casting

Study on the Effect of Different Factors on the Change of the Phosphorus-Rich Phase in High Phosphorus Steel Slag

Separation and recovery of phosphorus from steelmaking slag via a selective leaching–chemical precipitation process

Thermodynamic Analysis of Mineral Phase Composition of Steel Slag System

Separation of Phosphorus from Phosphorus-concentrated Steelmaking Slag

Wet magnetic separation of phosphorus containing phase from modified BOF slag

Distribution and enrichment of phosphorus in solidified BOF steelmaking slag

A Kinetic Study on Selective Leaching of Phosphorus from Dephosphorization Slag

Influence of the Basicity on Phosphorus Enrichment Properties of Decarbonization Slag in Low‐Carbon Double Slag Converter Steelmaking Process with Industrial Experiments, Mineralogy, and Ion–molecule Coexistence Theory

Dissolution kinetics of P-bearing steelmaking slag in the citric acid solution

Effect of CaCl2 Addition on Phosphorus Distribution Between CaO–SiO2–FeOx–P2O5 Slag and Carbon-Saturated Iron at Steelmaking Temperature

Leaching behavior and microstructure of phosphorus in converter slag

A review on the P enrichment and recovery from steelmaking slag: Towards a sustainable P supply and comprehensive utilization of industrial solid wastes

Effect of highly oxidizing converter dephosphorization slag on dephosphorization behaviour of molten steel

Effect of low basicity refining slag on evolution and removal of oxide inclusions in 55SiCrA spring steel

Recovery of phosphorus from chemical-enhanced phosphorus removal sludge: Influence of sodium sulfide dosage on phosphorus fractionation, sludge dewaterability, and struvite product

A novel process for the direct utilization of copper slag and phosphate rock by compound modification and coreduction

Phosphorus partitioning and recovery of low-phosphorus iron-rich compounds through physical separation of Linz-Donawitz slag

Behavior of Carbothermal Dephosphorization of Phosphorus-Containing Converter Slag and Its Resource Utilization

Efficient extraction of phosphate from dephosphorization slag by hydrochloric acid leaching