Abstract:Cementitious composites blended with high Belite sulfoaluminate cement and medium-heat Portland cements were optimized to achieve both favorable 3D printability and durability performance. The influence of the hybrid cement ratio on the rheology and the hardened properties, such as mechanical properties, drying shrinkage, and carbonization resistance, was systematically investigated. The results revealed that the mixture incorporated with 80% CSA-HB cement exhibited excellent early strength, and a 1d compressive strength higher than 30 MPa was achieved. Hybrid mixing of CSA-HB and P·MH reduces the super-early age hydration heat by 37.8%. Meanwhile, the 28-day carbonization depth of the mixture with 80% P·MH cement was 52.4% lower than that comprising a high content of CSA-HB. The designed mixtures were compatible with the printing process and validated by the printing practice of 9.4 m-span arch components using a large-scale robotic printer.

What problem does this paper attempt to address?

The paper primarily explores the development and performance evaluation of cement-based composites optimized for large-scale 3D printing applications. Specifically, the study aims to improve the printability and durability of 3D printed concrete by mixing high-belite calcium sulfoaluminate cement (CSA-HB) and moderate-heat Portland cement (P·MH). ### Research Background - **3D Concrete Printing Technology**: 3D concrete printing (3DCP) is an emerging and promising technology that has garnered widespread attention in the construction industry for its potential to reduce labor, construction time, and costs, while enhancing design flexibility and environmental sustainability. - **Material Requirements**: For 3DCP, it is typically necessary to reduce the amount of aggregate and increase the proportion of cementitious materials to meet the extrusion requirements of large-scale 3D printing processes. However, the extensive use of cementitious materials and the need for rapid setting and early strength characteristics can lead to an increased rate of early hydration heat release, making the material prone to microcracks and severe autogenous shrinkage under thermal stress conditions, which significantly impacts the durability and safety of the structure. ### Research Objectives - **Optimization of Cement-Based Composites**: By mixing CSA-HB cement and P·MH cement, the aim is to obtain cement-based composites that possess both good 3D printability and excellent durability. - **Performance Evaluation**: The study systematically investigates the effects of different mixing ratios on the rheological properties of the composites and their hardened properties (such as mechanical performance, drying shrinkage, and carbonation resistance). - **Practical Validation**: The compatibility of the designed mixtures with the printing process was validated by using a large robotic printer to print an arch component with a span of 9.4 meters. ### Key Findings - **Effect of Mixing Ratios**: The mixture containing 80% CSA-HB cement exhibited excellent early strength, with a 1-day compressive strength exceeding 30 MPa. - **Control of Hydration Heat**: The mixture of CSA-HB and P·MH can reduce the ultra-early hydration heat release by 37.8%. - **Reduction in Carbonation Depth**: The mixture containing 80% P·MH cement had a 28-day carbonation depth that was 52.4% lower than that of the mixture with a high proportion of CSA-HB. - **Printing Practice**: The designed mixture was suitable for the printing process and was validated by printing an arch component with a span of 9.4 meters. In summary, this study addresses the issues present in traditional cement-based composites during the 3D printing process by mixing different types of cement, thereby enhancing the overall performance of the material. It provides theoretical basis and technical support for the practical application of 3D concrete printing technology.

Cementitious composites blending with high belite sulfoaluminate and medium-heat Portland cements for largescale 3D printing

Properties and Microstructures of 3D Printable Sulphoaluminate Cement Concrete Containing Industrial By-Products and Nano Clay

3D Printing of Fiber-Reinforced Calcined Clay-Limestone-Based Cementitious Materials: From Mixture Design to Printability Evaluation

Study of 3D printed concrete with low-carbon cementitious materials based on its rheological properties and mechanical performances

Mix Design and 3D Printing Correlation Performance of Pcc-Based 3DPM

Inclined 3D concrete printing: build-up prediction and early-age performance optimization

Mechanical Performance of Commercially Available Premix UHPC-Based 3D Printable Concrete

Effects of oyster shell derivatives on performance enhancement of biomass-based 3D printed concrete

Effect of supplementary cementitious materials on properties of 3D printed conventional and alkali-activated concrete: A review

Factors Influencing the Properties of Extrusion-Based 3D-Printed Alkali-Activated Fly Ash-Slag Mortar

Improving printability of limestone-calcined clay-based cementitious materials by using viscosity-modifying admixture

PVA Fibre Reinforced High-Strength Cementitious Composite for 3D Printing: Mechanical Properties and Durability

Effect of different grade levels of calcined clays on fresh and hardened properties of ternary-blended cementitious materials for 3D printing

Thermally stimulated stiffening and fly ash's alkaline activation by Ca(OH) 2 addition facilitates 3D-printing

Strength and Proportioning Design of 3D Printed Concrete (3DPC) Based on Aggregate Gradation Optimization

A new strategy to enhance 3D printability of cement-based materials: In-situ polymerization

Development of Ultra-High-Performance Silica Fume-Based Mortar Incorporating Graphene Nanoplatelets for 3-Dimensional Concrete Printing Application

The synergistic effect of greenhouse gas CO 2 and silica fume on the properties of 3D printed mortar

Effects of additives on the mechanical properties, rheology, and printing properties of Pcc-based 3DPMs

D-optimal design of experiments applied to 3D high-performance concrete printing mix design

Modification effect of nanosilica and polypropylene fiber for extrusion-based 3D printing concrete: Printability and mechanical anisotropy