Abstract:Although the use of 3D printing in civil engineering has grown in popularity, one of the primary challenges associated with it is the absence of steel bars inside the printed mortar. As a result, developing 3D printing mortar with ultra-high compressive, flexural, and tensile strengths is critical. In the present study, an ultra-high-performance mortar incorporating silica fume (SF) and graphene nanoplatelets (GNPs) was developed for 3D printing application. The concrete mixture added SF to the concrete mixture in the range between 0% and 20%, while GNPs were added as a partial replacement by cement weight from 0.5% to 2%. The flowability and the machinal properties of the proposed mortar, including compressive (CS), tensile (TS), and flexural strength (FS), were investigated and assessed. Microstructure analysis involving FESEM and EDX was also investigated and evaluated, while response surface methodology (RSM) was considered to predict and optimize the optimum value of GNPs and SF. Workability results show that the flowability is reduced when the amount of graphene increases. Based on the predicted and experimental results, ultra-high-strength mortar can be developed by including 1.5% of GNPs and 20% of SF, in which the CS jumped from 70.7 MPa to 133.3 MPa at the age of 28 days. The FS and TS were 20.66 MPa and 14.67 MPa compared to the control mix (9.75 MPa and 6.36 MPa), respectively. This favorable outcome was credited to the pozzolanic activity of SF and the effectiveness of GNPs in compacting the pores and bridging the cracks at the nanoscale level, which were verified by FE-SEM and EDX. In addition, the developed quadratic equations proved their accuracy in predicting and optimizing the mechanical properties with low error (less than 0.09) and high correlation (R2 > 0.97). It can be concluded that the current work is an important step forward in developing a 3D printing mortar. The lack of reinforcement in the printed mortar structure has been a considerable difficulty, and the SF and GNPs have increased the compressive, flexural, and tensile strengths of the mortar. Thus, these improvements will encourage the industry to utilize sustainable materials to produce more affordable housing.

The synergistic effect of greenhouse gas CO 2 and silica fume on the properties of 3D printed mortar

The Synergy Effect of Limestone Powder and Mineral Admixtures on the Mechanical Property of Mortar

Improving mechanical properties of 3D printed mortar by exploiting synergistic effects of fly ash microsphere and nano-silica

Microstructure Refinement of Calcium-Sulfate-aluminate and Portland Cement (CSA-PC) Hybrids with Accelerated CO2 Curing (ACC)

Development of Ultra-High-Performance Silica Fume-Based Mortar Incorporating Graphene Nanoplatelets for 3-Dimensional Concrete Printing Application

Rheological behaviour, setting time, compressive strength and microstructure of mortar incorporating supplementary cementitious materials and nano-silica

A new strategy to enhance 3D printability of cement-based materials: In-situ polymerization

Effect of Nanostructured Silica Additives on the Extrusion-Based 3D Concrete Printing Application

Effect of nano-SiO2/CaSO4 whisker–silica fume on the strength, drying shrinkage, and capillary water absorption of cement mortar

Mechanical Performance Optimization in Spray-Based Three-Dimensional-Printed Mortar Using Carbon Fiber

Examining the early-stage performance and mechanical performance of limestone powder-silica fume binary cement-based materials

Systematic approach for printability evaluation and mechanical property optimization of spray-based 3D printed mortar

Effect of CO2-mixing dose and prolonged mixing time on fresh and hardened properties of cement pastes

Factors Influencing the Properties of Extrusion-Based 3D-Printed Alkali-Activated Fly Ash-Slag Mortar

Modification effect of nanosilica and polypropylene fiber for extrusion-based 3D printing concrete: Printability and mechanical anisotropy

Effect of supplementary cementitious materials on properties of 3D printed conventional and alkali-activated concrete: A review

Carbon dioxide as an admixture for better performance of OPC-based concrete

Cementitious composites blending with high belite sulfoaluminate and medium-heat Portland cements for largescale 3D printing

Comparative Evaluation of the Applicability of 3D Printing Mortar with Different Waste Powders

A novel method for improving the printability of cement-based materials: Controlling the releasing of capsules containing chemical admixtures

Investigation on Hydration and Mechanical Properties of Mortar Containing Limestone Powder and Fly Ash Based on the Coupled Chemical–Thermal–Mechanical Method