Abstract:The crack growth behavior of Hastelloy X under creep-fatigue interaction at high temperature is investigated by a nonlinear creep-fatigue interaction damage model. Multiaxial stress is considered both in the fatigue and creep damage models. The effect of the variance of fatigue damage parameters is analyzed in a quantitative method and some linear effects were observed. The influence of hold time, crack depth ratio and load level on the crack growth behavior are studied and results under different hold time indicate that the increase of hold time, crack depth ratio and load level enhances the creep damage and accelerates the time-dependent crack growth rate. When the hold time varies from 1 to 60 min, the creep damage always dominates the damage accumulation, which can explain the overlap of the curves between da/dt and (Ct)avg observed in the experiment very well. The damage contributions of creep, fatigue, and their interaction are quantized thanks to the independent damage model for each part: (1) when the hold time increases from 1 min to 60 min, the creep damage ratio rises from 70% to 99% and the interaction damage ratio decreases from 25% to 1%. (2) when the crack depth ratio increases from 0.35 to 0.5, the creep damage ratio rises from 80% to 90% and the interaction damage ratio decreases from 15% to 10%; (3) when the load level increases from 4200 N to 5000 N, the creep damage ratio rises from 75% to 90% and the interaction damage ratio decreases from 25% to 10%. It is also shown the increase of load level and crack depth ratio lead to the increase of equivalent stress and therefore enhances the creep damage and accelerates the crack growth rate.

Effect and mechanism of constraint on creep crack growth behavior of GH3535 alloy

An Investigation of the Effect of High-Temperature Cyclic Straining and Creep Loading on Tensile Mechanical Properties of GH4145/SQ Alloy

Effect of constraint on creep fracture toughness of a Cr-Mo-V steel

Effects of Tensile/compressive Overloads on Fatigue Crack Growth Behavior of an Extra-Low-interstitial Titanium Alloy

Creep crack growth of GH3535 alloy at elevated temperatures

Inconsistent creep between dendrite core and interdendritic region under different degrees of elemental inhomogeneity in nickel-based single crystal superalloys

Research on Multiaxial Creep Properties of P92 Steel Based on Improved KR Creep Constitutive Model

Characterization of creep constraint effect for brazed joint specimens at crack tip by new constraint parameter A

A new creep-fatigue crack growth model and a correlation of the creep-fatigue crack growth rate with unified constraint parameter

Impact of out‐of‐plane constraint on creep crack growth behavior of M174+ aluminum alloys by nano‐computed tomography (CT)

Constraint modified time dependent failure assessment diagram (TDFAD) based on <i>C</i>(<i>t</i>)-<i>A</i><sub>2</sub>(<i>t</i>) theory for creep crack

Modeling and effect analysis on crack growth behavior of Hastelloy X under high temperature creep-fatigue interaction

Characterization of Mismatch Constraint Effect for the Central Crack Plate under Biaxial Loading

Modelling short crack growth under creep-fatigue interaction for different dwell times

Dependence of creep crack propagation on columnar grain orientation in cast HK40 tube

Characterizations of Material Constraint Effect for Creep Crack in Center Weldment under Biaxial Loading

A Creep Constitutive Model, Based on Deformation Mechanisms and Its Application to Creep Crack Growth

Effect of pre-straining treatment on high temperature creep behavior of Ni-based single crystal superalloys

Mismatch Constraint Effect for Bimaterial Interfacial Creep Crack

3D front tip fields in creeping solids under constraint effects: a higher-order asymptotic solution

Effects of nonproportional loading and residual stress on creep crack tip fields