Abstract:The crack growth behavior of Hastelloy X under creep-fatigue interaction at high temperature is investigated by a nonlinear creep-fatigue interaction damage model. Multiaxial stress is considered both in the fatigue and creep damage models. The effect of the variance of fatigue damage parameters is analyzed in a quantitative method and some linear effects were observed. The influence of hold time, crack depth ratio and load level on the crack growth behavior are studied and results under different hold time indicate that the increase of hold time, crack depth ratio and load level enhances the creep damage and accelerates the time-dependent crack growth rate. When the hold time varies from 1 to 60 min, the creep damage always dominates the damage accumulation, which can explain the overlap of the curves between da/dt and (Ct)avg observed in the experiment very well. The damage contributions of creep, fatigue, and their interaction are quantized thanks to the independent damage model for each part: (1) when the hold time increases from 1 min to 60 min, the creep damage ratio rises from 70% to 99% and the interaction damage ratio decreases from 25% to 1%. (2) when the crack depth ratio increases from 0.35 to 0.5, the creep damage ratio rises from 80% to 90% and the interaction damage ratio decreases from 15% to 10%; (3) when the load level increases from 4200 N to 5000 N, the creep damage ratio rises from 75% to 90% and the interaction damage ratio decreases from 25% to 10%. It is also shown the increase of load level and crack depth ratio lead to the increase of equivalent stress and therefore enhances the creep damage and accelerates the crack growth rate.

Dependence of creep crack propagation on columnar grain orientation in cast HK40 tube

An Investigation of the Effect of High-Temperature Cyclic Straining and Creep Loading on Tensile Mechanical Properties of GH4145/SQ Alloy

Inconsistent creep between dendrite core and interdendritic region under different degrees of elemental inhomogeneity in nickel-based single crystal superalloys

Effect and mechanism of constraint on creep crack growth behavior of GH3535 alloy

A Creep Constitutive Model, Based on Deformation Mechanisms and Its Application to Creep Crack Growth

Constraint modified time dependent failure assessment diagram (TDFAD) based on <i>C</i>(<i>t</i>)-<i>A</i><sub>2</sub>(<i>t</i>) theory for creep crack

Creep Behaviours of Cr25Ni35Nb and Cr35Ni45Nb Alloys Predicted by Modified Theta Method

Effect of constraint on creep fracture toughness of a Cr-Mo-V steel

Impact of out‐of‐plane constraint on creep crack growth behavior of M174+ aluminum alloys by nano‐computed tomography (CT)

Creep Behaviors Calculated by Varying Material Constants Obtained from Different Stress Regions for a Closed-End P91 Pipe

The development of creep damage constitutive equations for high Cr steel

Change of Grain Orientation and Effect of Grain Size on It in Creep Deformed Hastelloy X

On the influence of grain morphology on creep deformation and damage mechanisms in directionally solidified and oxide dispersion strengthened superalloys

Creep crack growth of GH3535 alloy at elevated temperatures

Creep crack growth prediction using a damage based approach

Modeling and effect analysis on crack growth behavior of Hastelloy X under high temperature creep-fatigue interaction

Creep-Fatigue Crack Initiation Simulation of a Modified 12% Cr Steel Based on Grain Boundary Cavitation and Plastic Slip Accumulation

High-Temperature Creep Behavior of a Nickel-Based Single-Crystal Superalloy with Small-Angle Deviation from [111] Orientation

Modelling short crack growth under creep-fatigue interaction for different dwell times

High temperature strain characteristics and life prediction of Sanicro25 alloy under stress-controlled cyclic loading

Influence of crystal orientations on the creep fracture of a nickel-based single crystal superalloy