Abstract:In this study, Hybrid-controlled creep-fatigue (HCCF) tests were conducted on TP321 austenitic stainless steel under a variety of test conditions. The effects of strain amplitude, holding time, holding stress and temperature on the creep-fatigue behavior of TP321 austenitic stainless steel were not only analyzed in detail but also revealed the creep-fatigue damage interactive mechanism. The results demonstrated that a rise in test temperature and load holding time markedly induced creep deformation, resulting in a notable reduction in failure life. Additionally, an increase in test temperature led to the cessation of the cyclic hardening phenomenon. Secondly, the analysis of fracture morphology and X-ray computed tomography (X-CT) scanning results demonstrated that the transgranular cracks expanded inwards and connected with the intergranular voids under creep-fatigue interaction, forming a mixed intergranular and transcrystalline fracture mode. The presence of large creep cavities impeded the propagation of fatigue cracks when creep damage was the dominant phenomenon. Subsequently, the damage evolution mechanism was elucidated through microstructural analysis, which revealed that the impact of the slip bands on the triangular grain boundaries and the precipitation of carbides facilitated the nucleation of voids and the internal formation of intergranular microcracks, thereby causing creep-fatigue damage interaction. Finally, the TP321 austenitic stainless steel creep-fatigue damage interactive mechanism diagram was proposed in conjunction with the fracture morphological characteristics and microstructure.

Constraint modified time dependent failure assessment diagram (TDFAD) based on <i>C</i>(<i>t</i>)-<i>A</i><sub>2</sub>(<i>t</i>) theory for creep crack

A new creep-fatigue crack growth model and a correlation of the creep-fatigue crack growth rate with unified constraint parameter

Effect of constraint on creep fracture toughness of a Cr-Mo-V steel

Fatigue-Creep Interaction Of P92 Steel And Modified Constitutive Modelling For Simulation Of The Responses

Modelling short crack growth under creep-fatigue interaction for different dwell times

Characterization of creep constraint effect for brazed joint specimens at crack tip by new constraint parameter A

Research on Fatigue-Creep Interaction Damage of Steel 1.25Cr0.5mo

Evaluation of the Effect of Various Prior Creep-Fatigue Interaction Damages on Subsequent Tensile and Creep Properties of 9%cr Steel

A Robust Life Prediction Model for a Range of Materials under Creep-Fatigue Interaction Loading Conditions

Effect and mechanism of constraint on creep crack growth behavior of GH3535 alloy

Influences of T-Stress on Constraint Effect in Mismatched Modified Boundary Layer Model for Creep Crack

A Modified Microstructure-Based Creep Damage Model for Considering Prior Low Cycle Fatigue Damage Effects

Numerical Investigations on the Effects of T-stress in Creep Crack

Numerical Investigations on the Effects of T-Stress in Mode I Creep Crack

A Creep Constitutive Model, Based on Deformation Mechanisms and Its Application to Creep Crack Growth

Assessment of Creep Behavior Using a Damage-Coupled Model for Martensitic Stainless Steel

3D front tip fields in creeping solids under constraint effects: a higher-order asymptotic solution

An Insight into the Creep-Fatigue Damage Localization in Welded Joints Based on Crystal Plasticity Finite Element Method

Dai, Yanwei and Liu, Yinghua and Chen, Haofeng (2016) Influences of T- stress on constraint effect in mismatched modified boundary layer model for creep crack. In: ASME 2016 Pressure Vessels and Piping

Creep-fatigue interactive behavior and damage mechanism of TP321 stainless steel under hybrid-controlled conditions

Theoretical Analysis and Engineering Implications for the High Order Term Solutions of the Mode II Type Creep Crack