Abstract:TiAl alloy is one of the most attractive candidates for a new generation of high-temperature structural materials and has broad application prospects in the aerospace field. As a typical intermetallic material, TiAl is inevitably difficult to process using conventional methods. Election beam selective melting (EBSM) is an effective method of addictive manufacturing to prepare TiAl alloy with a complex structure. However, the microstructure of TiAl alloy formed using EBSM often contains defects such as pores, which seriously reduces the mechanical properties of the material. In this work, the effects of EBSM and post-processing procedures on the microstructure and mechanical properties of Ti-48Al-2Cr-2Nb alloy were studied. The results show that the microstructure of Ti-48Al-2Cr-2Nb alloy formed using the EBSM process was dense and composed of equiaxed γ-phase and double-phase regions. A large number of dislocations that formed due to thermal stress were clearly observed inside the Ti-48Al-2Cr-2Nb alloy. When the EBSM process parameters were 13.5 mA, 4.0 m/s, and 40.50 J/mm3, as the current intensity increased, the Al content decreased, the content of α2 phase increased, and the microstructure of the material was coarse. The results of the tensile test fracture morphology indicate that the Ti-48Al-2Cr-2Nb alloy exhibited brittle fracture during tensile deformation, lacking the typical yield deformation of metal materials. As the energy density of the EBSM process increased, the mechanical properties of the Ti-48Al-2Cr-2Nb alloy first increased and then decreased. The samples prepared with an energy density of 34.50~40.50 J/mm3 had excellent mechanical properties, of which the maximum tensile strength and maximum elongation reached 643 MPa and 2.09%, respectively. The phase composition of the Ti-48Al-2Cr-2Nb alloy after hot isostatic pressing (HIP) treatment remained unchanged from the EBSM samples, but there was a slight difference in content. There was an increase in the amount of γ phase and a decrease in B2 phase, accompanied by the generation of a massive γ phase after HIP treatment. Moreover, the number of dislocations inside the material increased. The Ti-48Al-2Cr-2Nb alloy after HIP treatment exhibited obvious plastic deformation characteristics, with a tensile strength of 679 MPa and elongation of 2.5%. A heat treatment of 900 °C/5 h was performed on the Ti-48Al-2Cr-2Nb alloy after HIP. The dislocation density of the Ti-48Al-2Cr-2Nb alloy decreased, and the B2 phase transformed from massive to lamellar.

Bi-modally grained Ti-based alloys fabricated by semi-solid sintering based on the hypoeutectic transformation

A new insight into high-strength Ti 62 Nb 12.2 Fe 13.6 Co 6.4 Al 5.8 alloys with bimodal microstructure fabricated by semi-solid sintering

Selective laser melting processing of heterostructured Ti6Al4V/FeCoNiCrMo alloy with superior strength and ductility

TiAl Alloy Fabricated Using Election Beam Selective Melting: Process, Microstructure, and Tensile Performance

Achieving Equiaxed Transition and Excellent Mechanical Properties in a Novel Near-β Titanium Alloy by Regulating the Volume Energy Density of Selective Laser Melting

Additive manufacturing of fine-grain fully lamellar titanium aluminide alloys

Enhanced strength of dual-phase Ti6242 alloy via a heterogeneous microstructure

Enhanced Mechanical Properties of Ti-5Al-5Mo-5V-3Cr-1Zr by Bimodal Lamellar Precipitate Microstructures Via Two-Step Aging

Ultrahigh strength and large plasticity of nanostructured Ti62Nb12.2Fe13.6Co6.4Al5.8 alloy obtained by selectively controlled micrometer-sized phases

Achieving superior strength-ductility combination in the heterogeneous microstructured Ti64 alloy via multi-eutectoid elements alloying with CoCrFeNiMn during laser powder bed fusion

Peritectic Solidification Kinetics and Mechanical Property Enhancement in a Rapidly Solidified Ti–48 at% Al–8 at% Nb Alloy via Hierarchical Twin Microstructure

Homogeneous α-precipitation and enhanced plasticity in Ti–6Cr–5Mo–5V–4Al high-strength metastable titanium alloy with heterogenous β-structure

Micro-mechanism and mechanical properties of solid-powder hot isostatic pressing diffusion-bonded Ti2AlNb alloy

α′′ phase-assisted nucleation to obtain ultrafine α precipitates for designing high-strength near-β titanium alloys

Microstructure refinement and improvement of mechanical properties of Ti46Al8Nb0.9B alloys by electromagnetic cold crucible continuous solidification

Hierarchical microstructure of a titanium alloy fabricated by electron beam selective melting

Solidification and microstructure investigation on as-cast and annealed hypoeutectic Ti–Fe alloys

Regulation on Microstructures and Properties of Hypereutectic Al–3.5Fe–2.5Ni Alloy by Controlled Diffusion Solidification

Solidification characterization and its correlation with the mechanical properties and functional response of NiTi shape memory alloy manufactured by electron beam freeform fabrication

Semisolid forming microstructure of Al-Cu5-Ti-Mn alloy

Thermomechanical characterization and conventional rolling of a novel β-solidifying γ-TiAl alloy with excellent comprehensive properties