Abstract:The non-oxide-reinforced phase AlN-SiC solid solution with high performance was successfully synthesized in the resin-bonded Al-Si-SiC composites under flowing nitrogen at 1300 °C. The AlN-SiC solid solution was synthesized by three paths of liquid-solid, gas-solid and gas-gas reactions through modulation of Al/Si ratio, and controllable microstructure of AlN-SiC solid solution was attained. The phase composition and microstructure of the sintered samples were characterized by XRD and SEM, combined with thermodynamics, the formation mechanism of AlN-SiC solid solution was investigated and the reaction model was established. Al was not detected while Si was detested by XRD. Granular, short columnar and whisker-like AlN-SiC solid solution were generated and their positions varied. As the temperature increases, the partial pressure of oxygen decreases due to the oxidation of Al, Si and SiC on the surface of the sample, inside the sample, the active oxidation takes place, generating Al2O(g), SiO(g) and CO(g). Due to the low oxygen partial pressure, Al is preferentially nitrided to form a thin AlN layer on its surface. The AlN layer is broken as the temperature increases, then liquid Al with carbon from resin begins to flow, leaving the residual shell of AlN in situ. When it flows to the surface of Si, Al-Sialloy is formed locally inside the Si particles under the wetting effect of C, then hexagonal AlN-SiC solid solution is formed inside the Si shell. Part of SiO(g) + CO(g) diffuses into the interior of the AlN residual shell and reacts by aggregation to form a granular AlN-SiC solid solution in the shell wall; others diffuses into the pores of the sample for vapor deposition, and finally forms stacked hexagonal flaky whiskers. The in-situ generated of AlN-SiC solid solution with multiple morphologies in the composite plays a joint toughening effect, which can significantly enhance the comprehensive performance of the composite. In this experiment, the synthesis of AlN-SiC solid solution without sintering aids under normal pressure at a low temperature. It is expected to be applied to the blast furnace and to realize the longevity of blast furnace.

Surface modification of aluminum and silicon carbide during the nitrogen-induced self-forming Al composite (NISFAC) manufacturing process

Aluminum Matrix Composites Manufactured using Nitridation-Induced Self-Forming Process

Phase evolution mechanism of SiC-Al-Si composite under flowing nitrogen at 1600 °C

Formation mechanism of AlN-SiC solid solution with multiple morphologies in Al-Si-SiC composites under flowing nitrogen at 1300 °C

Thermal expansion behavior of nitrogen-processed Al6061/SiC composites

Experimental Investigation of Aluminum Nitride Ceramics Based on Compliant Finishing Process

Formation mechanism of Al4SiC4 in Al–SiC composite under flowing nitrogen at 1300 °C

Fabrication of novel AlN-SiC-C refractories by nitrogen gas-pressure sintering of Al4SiC4

Synthesis of SiC-AlN Ceramic Alloy Powder by the Direct Reactions Between the Constituent Elements.

Processing and properties of nanophase SiC/Si3N4 composites

Effect of Si3N4 mesophase on the formation of Al2OC-AlNss in resin-bonded Al–Al2O3 composites

Synthesis mechanism of AlN–SiC solid solution reinforced Al2O3 composite by two-step nitriding of Al–Si3N4–Al2O3 compact at 1500 °C

In-situ induce reinforcement in WAAM of Al-matrix composite using active N 2 as shielding gas followed by friction stir processing

Preparation of Si3N4–TiN–SiC composite by partial substitution of Ti–Si–Fe alloy for Si under N2 atmosphere

Preparation of AlN Matrix Composites Using an Infiltration and Reaction Approach

In-situ Induce Reinforcement in WAAM of Al-matrix Composite Using Active N2 As Shielding Gas Followed by Friction Stir Processing

Effect of SiC nanoparticle on microstructure and mechanical properties of graphene nanosheet (GNS) reinforced aluminum composites

Pressureless Infiltration and Resulting Mechanical Properties of Al-AlN Preforms Fabricated by Selective Laser Sintering and Partial Nitridation

Carbothermally prepared nanophase SiC/ Si3N4 composite powders and densified parts

Surface modification and ablation behaviors of nitrogen-doped C/C-ZrC-SiC composites via hot isostatic pressing

Synthesis of Oxynitride Composites during Combustion of a Ferrosilicon–Natural Mineral–Aluminum Mixture in Nitrogen