Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

Features of Nanosize Boehmite Hydrothermal Synthesis

Size and Morphology Controlled Synthesis of Boehmite Nanoplates and Crystal Growth Mechanisms

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Direct Continuous Hydrothermal Synthesis of High Surface Area Nanosized Titania

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

Facile Synthesis of Hierarchical Flower-Like Γ-Alooh Films Via Hydrothermal Route on Quartz Surface

Nanostructured ceramic powders by hydrothermal synthesis and their applications

Effects of KOH and Temperature on Hydrothermal Synthesis of Α-Feooh Nanowire

Hierarchical nanoarchitectonics of boehmite: The preparation of three-dimensional flower-like via hydrothermal method without surfactants

Hydrothermal Preparation Of Boehmite Nanorods By Selective Adsorption Of Sulfate

Nanoscale magnesium hydroxide and magnesium oxide powders: Control over size, shape, and structure via hydrothermal synthesis

Synthesis of Nanosized Pseudoboehmite and γ-Al2O3 by Control Precipitation Method

Synthesis of Al2O3 nanopowders using inorganic salt and its physical chemistry

Morphology Evolution in Hydrothermal Synthesis of Mesoporous Alumina

Synthesis of Nanosized Pseudoboehmite and γ-Al<sub>2</sub>O<sub>3</sub> by Control Precipitation Method

Morphological Controlled Growth of Nanosized Boehmite with Enhanced Aspect Ratios in an Organic Additive-Free Cationic–Anionic Double Hydrolysis Method

New sol-gel route using inorganic salt for synthesizing Al2O3 nanopowders

Hydrothermal-carbothermal synthesis of highly sinterable AlN nanopowders

Reactive phase behavior of aluminum nitrate in high temperature and supercritical water

Different nanostructures of boehmite fabricated by hydrothermal process: effects of pH and anions

Hydrothermal synthesis of boehmite nanorods from alumina sols