Abstract:The mechanical behavior of ceramic composite armor is related to the type of projectile and the material properties of each component under high-speed impact. There exists a coupling effect between the ceramic, backing material, and the projectile during the impact process. Especially for brittle projectiles, there is a clear correlation between the damage evolution and the backing material. This study investigates the mechanical behavior and ballistic response of B4C ceramic composite armor resisting T12A steel projectiles using three different backing materials: Q235 steel, Kevlar, and UHMWPE laminates. Experiments and numerical simulations were conducted. The results show that the Rosin-Rammler distribution model can well describe the mass distribution of fragments of the brittle T12A steel projectile. The protective performance of ceramics against the T12A steel projectile depends on the dwell time, where the Q235 steel backing plate can prolong the interaction time between the projectile and the ceramic, leading to more erosion and fracture of the projectile. The fiber laminate primarily absorbs the remaining kinetic energy of the projectile through its own tensile and shear failure, without causing damage to the projectile. Due to its lower shear strength, the Kevlar laminate is quickly penetrated by the residual projectile, while the UHMWPE laminate undergoes more tensile deformation at the sublayer interface due to its higher tensile strength, absorbing more kinetic energy from the projectile. Furthermore, both the projectile and B4C ceramics fail due to the complex stress caused by compression waves and tensile waves. When the backing plate is Q235 steel, the peak stress inside the projectile is higher, resulting in more severe fragmentation of the projectile. However, the peak stress inside the ceramic remains relatively similar regardless of the different backing materials.

Dynamic Response Behaviours of Al2O3 Ceramics with Different Grain Sizes under SHPB Compression Loading

Plastic Deformation and Sintering of Alumina under High Pressure

Dynamic Response of Ceramic Shell for Titanium Investment Casting under High Strain-Rate SHPB Compression Load

Experimental and Numerical Investigation of the Ballistic Response of Alumina 99.7% Covered with Aluminum 6061-T6 Face Sheets

Investigation of the effect of the grain sizes on the dynamic strength of the fine-grained alumina ceramics obtained by Spark Plasma Sintering

Compressive properties and failure mechanisms of AlON ceramics under different strain rates

Experimental and theoretical investigation of failure mechanism in Al 2 O 3 /SiC composite under plane shock waves

Dynamic behaviour of YAG transparent ceramic under ramp wave and shock compression loading up to 20 GPa

Experimental study on dynamic response of micron aluminum powder

Dynamic deformation of Al under shock loading

Computational investigation of the dynamic response of silicon carbide ceramic under impact loading

Influence of Tungsten Carbide Particles on Resistance of Alumina Matrix Ceramics to Thermal Shock

Effect of laser shock on the compacting characteristics and rebound behavior of composite powders (Al2O3/Al) with different alumina contents

Influence of a Piezoelectric Secondary Phase on Thermal Shock Resistance of Alumina‐Matrix Ceramics

Role of composition and microstructure in the abrasive wear of high-alumina ceramics

Wave propagation through alumina-porous alumina laminates

Dynamic response of a Li2O-Al2O3-SiO2 transparent glass-ceramic under shock compression

Impact-abrasive wear resistance of high alumina ceramics and ZTA

Influence of sintering process on microstructure and mechanical properties of alumina ceramics: Spark plasma and microwave hybrid sintering

Coupling Effect of Brittle Projectiles and Ceramic Composite Armor with Different Backings

Numerical modeling of dynamic response and microcracking in shock-loaded polycrystalline transparent ceramic