Abstract:Herein, a stable LiNbO3 (LN) sol, with different Zn2+ contents, is prepared using ethanol niobium, lithium acetate and zinc acetate as starting materials, absolute ethanol as a solvent, and acrylic acid and benzoyl acetone (BzAcH) as additives. The influence of Zn2+ content on LN crystal structure, light transmittance and J-V curve characteristics is studied in detail. XRD results reveal that Zn2+ doping, with a molar content of less than 5%, does not influence the crystal structure of LN. SEM indicates that the grain size of LN films gradually increases with the increase of doping content. The surface quality of LN films becomes worse when the doping content of Zn2+ reaches 5%. Moreover, light transmittance tests show that the maximum light transmittance is attained at the doping amount of 3%. J-V curves demonstrate that Pt/LN/LNO(LaNiO3) structure shows excellent resistance switching (RS) effect due to the formation of Schottky barrier at the Pt/LN interface, which initially becomes prominent with the increase of Zn2+ content, followed by a gradual decrease. On the other hand, In/LN/LNO structure exhibits poor RS effect due to the unobvious Schottky barrier at In/LNO interface. Furthermore, J-V curves at different temperatures demonstrate that the RS effect of Pt/LN/LNO structure tends to deteriorate, while the refractive index of LN film increases with the decrease of temperature. Herein, the abovementioned RS phenomenon is analyzed and explained in terms of the relationship between interfacial barrier and doping amount of Zn2+, migration of oxygen vacancies, and the relationship between insulation property of LN films and temperature. The research results are of experimental and theoretical significance for practical applications of LN films.

Characterization and doping effects study of high hole concentration Li-doped ZnO thin film prepared by sol–gel method

Preparation and Characterization of Mg-doped ZnO Thin Films by Sol–gel Method

Preparation and Characterization of Na-doped ZnO Thin Films by Sol–gel Method

Surface Morphology and Optical Properties of Na-doped ZnO Thin Films

Surface Topography and Optical Properties of Al-doped ZnO Thin Films by Sol-gel Process

Enhanced photo-induced hydrophilicity of the sol-gel-derived ZnO thin films by Na-doping

Influence of Dopant Content on Morphology and Optical Constants of ZnO:Na Films by Sol-Gel Method

Effect of Magnesium Doping on the Light-Induced Hydrophilicity of Zno Thin Films

Hydrogen‐assisted Nitrogen‐acceptor Doping in ZnO

Unintentionally Doped Hydrogen Removal Mechanism in Li Doped ZnO

Optical properties of p-type ZnO doped by lithium and nitrogen

Realization of p-type ZnO films via monodoping of Li acceptor

Effect of Li Doping on Structural, Optical, and Optoelectrical Characteristics of ZnSnO 3 Thin Films Prepared by Nebulizer Spray Pyrolysis

Control of P- and N-Type Conductivities in Li-Doped Zno Thin Films

Hole Transport Properties of P-Type Polycrystalline ZnO Film Using a Dual-Acceptor Doping Method with Lithium and Nitrogen

Fabrication of P-Type Li-Doped Zno Films by Pulsed Laser Deposition

P-Type Behavior of Nitrogen Doped, Lithium Doped, and Nitrogen-Lithium Codoped Zn0.11mg0.89o Thin Films

Acceptor Formation Mechanisms Determination from Electrical and Optical Properties of P-Type ZnO Doped with Lithium and Nitrogen

Preparation and Characterization of p-Type ZnO Using Li-N Dual-Acceptor Doping Method by Pulsed Laser Deposition

Low-resistivity, Stable P-Type ZnO Thin Films Realized Using a Li–N Dual-Acceptor Doping Method

J-V characteristics of sol-gel-prepared Zn2+ doped LiNbO3