Abstract:Silicon (Si) chips of 5 mm × 5 mm were bonded directly to copper (Cu) substrates using solid-state process at 300 °C without using any die-attach materials. A static pressure of 6.9 MPa was applied. To deal with the large mismatch in coefficient of thermal expansion (CTE) between Si and Cu, graded circular micro-trenches were fabricated on the Cu substrates. The micro-trenches provide space for Cu material to move into during the bonding process where the Cu surface incurs plastic deformation to conform to Si bottom surface for intimate contact. The micro-trenches also help relax stresses on the bonding interface caused by the fact that Cu contracts significantly more than Si during cooling down. The results obtained are encouraging, implying that the concept of using micro-trenches work. Scanning electron microscopy (SEM) images on cross sections of bonded structures show that Si chips were well bonded to Cu substrates without voids or defects on the interface and without any cracks on Si chip. Shear test were performed on six samples. It turned out that, of all six samples, the Si chip fractured first and the entire Si bottom surface was stilled well bonded to the Cu substrate. The average breakage force of Si chips on six samples is 13.5 Kgf. The breakage force of the joint cannot be determined but is certainly higher than 13.5 Kgf, which is more than twice of the specification American Military Standard. The new chip bonding structure with solid-state process reported in this paper eliminates the use of die-attach materials and the thermal resistance associated with the die-attach. It also removes the operating temperature limit constrained by the melting temperature of die-attach materials. We except this new bonding structure design to be a valuable alternative to high power and high temperature devices.

Solid state bonding of silicon chips to copper substrates using silver with cavities

Solid-state bonding of silicon chips to copper substrates with graded circular micro-trenches

Low-Temperature and Low-Pressure Fine-Pitch Micro Cu Bump Bonding Using Stress Migration of a Sputtering Ag Layer

Bonding of Cu to Cu bulks through the low temperature sintering of Ag nanoparticle paste

Low-Temperature Cu-Cu Bonding Using Silver Nanoparticles Fabricated by Physical Vapor Deposition

Low Temperature Cu/SiO2 Hybrid Bonding with Protruding Copper Pads

SiC Chip Attachment Sintered by Nanosilver Paste and Their Shear Strength Evaluation

Bonding of copper to silicon chips using vapor-deposited tin film

High reliable and high bonding strength of silver sintered joints on copper surfaces by pressure sintering under air atmosphere

Fluxless bonding of Si chips to aluminum boards using electroplated Sn solder

Heterogeneous Bonding with Nanostructured Silver Langmuir-Blodgett Film

High-Pressure-Assisted Large-Area (>2400 mm2) Sintered-Silver Substrate Bonding for SiC Power Module Packaging

20 μm Copper Micro-Bump Bonding Through a Silver Metallization for Advanced Packaging Under a Low Pressure Condition

Copper Bonding Silicon Nitride Substrate Using Atmosphere Plasma Spray

Low Temperature Au/Sn Solid-Liquid Diffusion Chip-to-Chip Bonding for MEMS Encapsulation

Experimental studies on application of silver paste in thermosonic flip-chip bonding

Cu-Cu joining using citrate coated ultra-small nano-silver pastes

A Cu Pillar Bump Bonding Method Using Au-Sn Alloy Cap as the Interconnection Layer

Low Temperature Cu-Cu Bonding Using Ag Nanoparticles By Pvd

Mechanical properties and microstructure of large-area diamond/silicon bonds formed by pressure-assisted silver sintering for thermal management

Double layered sintered silver die bonding technology with superior mechanical reliability