Abstract:Dense layered material Ti3SiC2 was fabricated by hotpressed TiH2, Si and C powders. The Vickers indentations were made at loads of 0.5~30 kg to measure hardness. The results show that the hardness decreased with the increasing of loads. At the load of 30 kg, the hardness value was stable to 4 GPa. Most importantly, no indentation cracks were observed even at 30 kg load. This property should be due to the multiply energy absorbinggrain delamination, crack deflection, grain deformation, et al. The flexural strength and fracture toughness were 270 MPa and 6.8 MPa·m1/2, respectively, by means of the three point bending test and single edge notched beam test. The fracture surfaces show the obvious layered nature in the observation of scanning electron microscope (SEM). Larger Ti3SiC2 grains are prone to delamination and intragranular fracture, but smaller grains are more easily pulled out. Crack propagation is parallel to the basal plane of Ti3SiC2 resulting in the grain delamination. Crack propagation will be deflected inner of grains when it is normal to the basal plane, and the crack propagation path was prolonged and the spreading energy was dissipated. The morphology of the crack propagation path is similar to that of synthetic multilayered composites. The main mechanisms of improving fracture toughness are crack deflection, crack pinning, grain pull out, and grain delamination. Moreover, the authors found the samples for the single edge notched beam (SENB) test without breaking pieces after unloading. The feature indicates that Ti3SiC2 is a damage tolerance material and has plastic property like as the ductile metals at the room temperature. 

Toughening mechanisms of Ti3SiC2- and TiB2- toughened SiC matrix prepared via reactive melt infiltration

Microstructures and mechanical properties of in-situ SiC-TiB2 ceramic composites fabricated by reactive melt infiltration

Novel Ti3SiC2-(Ti, Zr)B2 Toughened (ti, Zr)C-based Composites with Enhanced Mechanical Properties Fabricated by Dual in Situ Reactions Hot-Pressing at Low Temperature

Study on the toughening mechanism of in-situ synthesis (TixZr1−x)B2 in solid-state sintered SiC composite ceramics

Synthesis, Microstructure and Mechanical Properties of Reaction-Infiltrated TiB2–SiC–Si Composites

Synthesis of Ti<sub>3</sub>SiC<sub>2</sub> from TiC and Si and its toughening mechanism with incorporated carbon fibers

Investigation on Fracture Toughness of Aluminum Matrix Composites Reinforced with in Situ Titanium Diboride Particles

Fabrication of Ti 3SiC 2 modified C/C-SiC composites by liquid silicon infiltration

Damage Behavior and Toughening Mechanism of SiCf/SiC-Ti3SiC2 Composites: A Combination of Digital Image Correlation and Acoustic Emission

Microstructure and Mechanical Properties of Si3N4f/BN/Si3N4 Composites by Joint Processes of PIP and CVI

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF Ti3SiC2 CERAMICS

Solidification Microstructure, Fracture Behavior and In-Situ Toughening of TiC-TiB2 Fine-grained Composite Ceramics

Toughening Effect and Mechanism of Thermo-compressed Composite Si3N4/MoSi2

In Situ Toughened Two-Phase B-12(C, Si, B)(3)-SiC Ceramics Fabricated Via Liquid Silicon Infiltration

Preparation and toughness mechanism of in-situ Ti3AlC2 enhanced and toughened TiAl3 matrix composites

Fracture Behavior of SiC-TiB2 Composite Measured by Different Test Methods

Microstructure and mechanical properties of MoSi2-based composite strengthened and toughened by Si3N4(p) and SiC(w)

Mechanical properties and microstructure of a Si3N4/Ti3SiC2 multilayer composite

Spark plasma sintering of TiC-based composites toughened by submicron SiC particles

Preparation and toughness mechanism of in-situ Ti<sub>3</sub>AlC<sub>2</sub> enhanced and toughened TiAl<sub>3</sub> matrix composites

Developing High Toughness and Strength Al/TiC Composites Using Ice-Templating and Pressure Infiltration