Abstract:In this paper, a time-dependent tensile constitutive model of long-fiber-reinforced unidirectional ceramic-matrix minicomposites is developed considering the interface and fiber oxidation. The relationship between the time-dependent tensile behavior and internal damage is established. The damage mechanisms of time-dependent matrix cracking, fiber/matrix interface debonding, fiber failure, and the oxidation of the interface and fiber are considered in the analysis of the time-dependent tensile stress–strain curve. The fracture mechanic approach, matrix statistical cracking model, and fiber statistical failure model are used to determine the time-dependent interface debonding length, matrix crack spacing, and the fiber failure probability considering the time-dependent interface and fiber oxidation. The effects of the fiber volume, fiber radius, matrix Weibull modulus, matrix cracking characteristic strength, matrix cracking saturation spacing, interface shear stress, interface debonding energy, fiber strength, fiber Weibull modulus, and oxidation time on the time-dependent tensile stress–strain curves, matrix cracking density, interface debonding, and fiber failure are discussed. The experimental time-dependent tensile stress–strain curves, matrix cracking, interface debonding, and fiber failure of four different unidirectional SiC/SiC minicomposites for different oxidation time are predicted. The composite tensile strength and failure strain increase with the fiber volume, fiber strength, and fiber Weibull modulus, and decrease with the oxidation time; the fiber/matrix interface debonding length increases with the fiber radius and oxidation time and decreases with the interfacial shear stress and interface debonding energy; the fiber/matrix interface oxidation ratio increases with the interfacial shear stress, interface debonding energy, and oxidation time and decreases with the saturation matrix crack spacing.

Failure Modeling of SiC/SiC Mini-Composites in Air Oxidizing Environments

A Progressive Oxidative Damage Model of C/SiC Composites under Stressed Oxidation Environments

Simulation of Mechanical Behaviors of Ceramic Composites Under Stress-Oxidation Environment While Considering the Effect of Matrix Cracks

Molecular dynamics simulation on PyC interfacial failure mechanism and shear strength of SiC/SiC composites

Failure Evaluation of a SiC/SiC Ceramic Matrix Composite During In-Situ Loading Using Micro X-ray Computed Tomography

Non-Destruction Evaluation Method for Long-Term Oxidation Behavior of SiC/SiC Composites with Different Preforms in Wet Oxygen

The oxidation life analysis method for SiC/SiC composite components based on an equivalent diffusion coefficient model

A Monte Carlo finite element simulation of damage and failure in SiC/Ti–Al composites

Stress‐Oxidation Behavior of a Carbon/Silicon Carbide Composite in a High‐Temperature Combustion Environment

Damage Evolution and Life Prediction of Cross-Ply C/SiC Ceramic-Matrix Composite under Cyclic Fatigue Loading at Room Temperature and 800 °C in Air

Oxidation behavior of 3D SiCf/SiBCN composites at 800–1200 °C

A Modified Iosipescu Method to Study In-Plane Shear Strength of C/SiC Composites at Elevated Temperatures in Air

Fatigue Life Prediction of 2D Woven Ceramic-Matrix Composites at Room and Elevated Temperatures

Multi-scale modeling and tensile failure prediction of 3D needled C/C-SiC composites considering real microstructure

Oxidation Kinetics and Its Impact on the Strength of Carbon Short Fiber Reinforced C/SiC Ceramics

A time-dependent tensile constitutive model for long-fiber-reinforced unidirectional ceramic-matrix minicomposites considering interface and fiber oxidation

Corrosion behavior of precracked SiCf/SiC composites under 1200–1300°C Na2SO4‐wet‐oxygen environment

Multiscale Failure Mechanism Analysis of SiC Fiber-Reinforced TC17 Composite Subjected to Transverse Tensile Loading at Elevated Temperature

An analytical model for the high temperature fracture strength of SiC fiber reinforced ceramic matrix composites considering oxidation and residual thermal stresses

Discrete Element Simulation of Transverse Cracking During the Pyrolysis of Carbon Fibre Reinforced Plastics to Carbon/Carbon Composites

Investigation on crack propagation of SiCf/SiC composite via PF-CZM method