Abstract:One of the most important requirements for a metallic biomaterial is the mechanical biocompatibility, which means excellent mechanical properties—high strength and fatigue strength, but low elastic modulus, to be mechanically harmonized with hard tissues. In order to improve the mechanical and biocompatible performance of the Ti-25.5Nb-4.5Ta-8.0Zr wt% alloy, the influence of cold plastic deformation and solution treatment on its properties were investigated. The Ti-25.5Nb-4.5Ta-8.0Zr wt% alloy was fabricated by melting in a cold crucible furnace (in levitation) and then subjected to several treatment schemes, which include cold rolling and different solution treatments. Microstructural and mechanical characteristics of specimens in as-cast and thermo-mechanically processed condition were determined by SEM microscopy and tensile testing, for different structural states: initial as-cast/as-received, cold rolled and solution treated at different temperatures (800, 900, and 1000 °C) and durations (5, 10, 15, and 20 min), with water quenching. It was concluded that both cold rolling and solution treatment have important positive effects on structural and mechanical properties of the biomaterial, increasing mechanical strength and decreasing the elastic modulus. Samples in different structural states were also corrosion tested and the results provided important information on determining the optimal processing scheme to obtain a high-performance biomaterial. The final processing route chosen consists of a cold rolling deformation with a total deformation degree of 60%, followed by a solution heat treatment at 900 °C with maintenance duration of 5 min and water quenching. By applying this thermo-mechanical processing scheme, the Ti-25.5Nb-4.5Ta-8.0Zr wt% alloy showed an elastic modulus of 56 GPa (5% higher than in the as-cast state), an ultimate tensile strength of 1004 MPa (41.8% higher than in the as-cast state), a yield strength of 718 MPa (40.6% higher than in the as-cast state), and increased corrosion resistance (the corrosion rate decreased by 50% compared to the as-cast state).

Damage behavior of orthopedic titanium alloys with martensitic microstructure during sliding wear in physiological solution

Sliding and Fretting Wear Behavior of Biomedical Ultrafine-Grained TiNbZrTaFe/Si Alloys in Simulated Physiological Solution

Dry sliding wear of MA/PM Al-10Ti alloy

Friction and wear of titanium alloys sliding against metal, polymer, and ceramic counterfaces

Wear characteristics of Ti–Nb–Ta–Zr and Ti–6Al–4V alloys for biomedical applications

Microstructure and Sliding Wear Behavior of PM Alloy Al10Ti after Thermal Exposure

Correlation between the characteristics of the thermo-mechanical mixed layer and wear behaviour of Ti–6Al–4V alloy

Dry Sliding Wear Behavior of Experimental Low-Cost Titanium Alloys

Wear Behavior of Ti-xNb Biomedical Alloys by Ball Cratering

Impact of scandium on mechanical properties, corrosion behavior, friction and wear performance, and cytotoxicity of a β-type Ti–24Nb–38Zr–2Mo alloy for orthopedic applications

Effect of milling time on sliding friction and wear behavior of hot isostatically pressed titanium alloys Ti-6Al-4X(X=V, Nb Fe) for biomedical applications

The influence of laser texturing on the tribological behavior of titanium alloy Ti6Al4V in medical applications

Wear and surface degradation of commercial ZTA femoral heads under boundary lubrication conditions

Microstructure and Wear Resistance of Ti-3zr-2sn-3mo-15nb (tlm) Alloy

Sliding Wear Behavior of Intermetallic Ti-45Al-2Nb-2Mn-(at%)-0.8vol%TiB2 Processed by Centrifugal Casting and Hot Isostatic Pressure: Influence of Microstructure

Thermal effects on wear behavior of additively manufactured NiTi shape memory alloys

Microstructure and Wear Behavior of Heat-Treated Mg-1Zn-1Ca Alloy for Biomedical Applications

Effect of Heat Treatment on the Dry Sliding Wear Behavior of the Mg-3Zn-0.4Ca Alloy for Biodegradable Implants

Effects of Cold Rolling Deformation and Solution Treatment on Microstructural, Mechanical, and Corrosion Properties of a Biocompatible Ti-Nb-Ta-Zr Alloy

Behavior of Eutectic Ti–Si–Zr Titanium Alloys in Different Friction Conditions

The tribological difference between biomedical steels and CoCrMo-alloys