The influence of laser texturing on the tribological behavior of titanium alloy Ti6Al4V in medical applications

Anna Woźniak,Oktawian Bialas,Marcin Adamiak,Branislav Hadzima,Janusz Szewczenko

DOI: https://doi.org/10.1007/s43452-024-00960-3

IF: 4.042

2024-05-11

Archives of Civil and Mechanical Engineering

Abstract:This paper analyzes the tribological behavior of the Ti6Al4V ELI alloy subjected to laser texturization for medical purposes. Laser texturing enables one to observe specific patterns of the material surface at established depths. Microtexturing of the samples was performed using a 355 nm picosecond laser. The influence of the microtexturing process (depending on the process parameters) on the geometric parameters of the proposed laser texturing pattern was evaluated. Selected samples were subjected to tribological testing using the ball-on-plate technique in dry and lubricant-sliding methods (in Ringer solution). The wear properties were evaluated by comparing the coefficient friction, wear volumes, and wear ratio. A scanning electron microscope characterized the morphologies of the wear scar and the wear mechanism. The experimental results show that the surface texturing and the changes in microgrooves can reduce wear. The results indicate, that samples after laser texturing were characterized by 15% higher microhardness, compared to those in the initial state. It was found, a 26% reduction in friction coefficient and 29% in the wear volume compared to the smooth, untextured surface samples under lubricated conditions. The decrease in value of the coefficient friction and wear volume for the samples after the laser texturing process is an effect of synergistic of entrapped wear debris in micro-grooves and increased hardness for samples after laser textured.

engineering, mechanical,materials science, multidisciplinary, civil

What problem does this paper attempt to address?

This paper attempts to solve the problem of tribological properties of titanium alloy Ti6Al4V in medical applications. Specifically, the main objective of the research is to improve the wear - resistant properties of Ti6Al4V alloy through laser surface treatment technology, so as to enhance its application effect in the biomedical field. The paper mentions that although titanium and its alloys are widely used in the biomedical field due to their excellent corrosion resistance, the ability to form a spontaneous oxide layer and satisfactory mechanical properties, their main drawback is poor tribological properties (including fretting wear), which has a significant impact on the lifespan of implants during the use of implants. Therefore, by changing the surface characteristics of materials through laser texturing technology, wear can be reduced, and the hardness and friction properties of materials can be improved, thereby prolonging the service life of implants and reducing damage to surrounding tissues.

To achieve this goal, the research team used a 355 - nm picosecond laser system to perform micro - texturing on the Ti6Al4V alloy and evaluated the influence of micro - textures on the geometric parameters of the material surface under different processing parameters. Subsequently, through the ball - on - plate friction test method, tribological property tests were carried out on the treated samples under dry and lubricated conditions (using Ringer's solution), including the comparison of friction coefficient, wear volume and wear rate. The experimental results show that after laser texturing treatment, the hardness of the samples increased by 15%, the friction coefficient decreased by 26%, and the wear volume decreased by 29%. These improvements are mainly attributed to the synergetic effect of wear debris trapped in the micro - grooves and the increase in hardness of the samples after laser texturing treatment.