Investigations on femtosecond laser-induced surface modification and periodic micropatterning with anti-friction properties on Ti6Al4V titanium alloy

PAN Xinlei,HE Weifeng,CAI Zhenbing,WANG Xuede,LIU Ping,LUO Sihai,ZHOU Liucheng,Xinlei PAN,Weifeng HE,Zhenbing CAI,Xuede WANG,Ping LIU,Sihai LUO,Liucheng ZHOU
DOI: https://doi.org/10.1016/j.cja.2021.01.003
IF: 5.7
2022-04-01
Chinese Journal of Aeronautics
Abstract:Titanium alloys have a wide application in aerospace industries as it has greater strength and low density, but it has poor tribological properties. To improve its friction and wear performance, in present work, a femtosecond laser is used to directly irradiate the Ti6Al4V titanium alloy surface in air conditioning, which results in localized ablation and the formation of periodic microstructures but also a strong pressure wave, propagating the material inside. Through the optimization of processing parameters, surface modification and periodic micropatterning with effective anti-friction properties were successfully induced on the surface. After a treatment of femtosecond laser-induced surface modification (FsLSM), the surface microhardness was improved by 16.6% and compressive residual stress reached -746 MPa. Besides, laser-induced periodic surface structures (LIPSS) with a titanium oxide outer coating were fabricated uniformly on the titanium alloy surface. Rotary ball-on-disk wear experiments revealed that the average coefficient of friction (COF) and wear mass loss of the specimen with FsLSM treatment were largely reduced by 68.9% and 90% as compared to that of untreated specimens, respectively. It was analyzed that the reason for the remarkable wear resistance was attributed to the comprehensive action of the generation of LIPSS, the titanium oxide outer coating, high amplitude compressive residual stress and gradient grain size distribution on the subsurface during the laser surface treatment. Since the findings here are broadly applicable to a wide spectrum of engineering metals and alloys, the present results offer unique pathways to enhancing the tribological performance of materials.
engineering, aerospace
What problem does this paper attempt to address?
This paper attempts to solve the problem of poor friction and wear properties of titanium alloys in industrial applications such as aerospace. Specifically, the researchers directly irradiate the surface of Ti6Al4V titanium alloy with femtosecond lasers to achieve surface modification and periodic micropatterning, thereby significantly improving the anti - friction properties of the material. By optimizing the processing parameters, surface modification and periodic micropatterns with effective anti - friction characteristics are successfully induced on the surface of the titanium alloy. The experimental results show that after femtosecond laser surface modification (FsLSM), the microhardness of the material surface is increased by 16.6%, and the compressive residual stress reaches - 746 MPa. In addition, the rotating ball - disk wear experiment shows that compared with the untreated samples, the average coefficient of friction (COF) and wear mass loss of the samples treated with FsLSM are reduced by 68.9% and 90% respectively. The research analysis believes that the significant improvement in wear resistance is attributed to the combined effects of the generation of LIPSS, the titanium oxide outer coating, the high - amplitude compressive residual stress, and the subsurface gradient grain size distribution during the laser surface treatment process. These findings not only have an important impact on titanium alloys, but may also be widely applicable to other engineering metals and alloys, providing a unique way to improve the tribological properties of materials.