Abstract:In this study, we develop a roasting method for removing arsenic from sulfide copper-arsenic-containing materials. The object of the study was fine dust from copper smelting production of the following composition (wt%): 34.89 – Zn; 20.02 – Cu; 17.74 – Pb; 17.07 – Fe; 7.12 – As; 0.92 – Sb; 0.69 – Sn; 0.63 – Ca; 0.42 – Mo; and 0.34 – K. The chemical composition of the materials was analyzed using an SHIMADZU EDX-7000 energy dispersive X-ray fluorescence spectrometer and a Bruker D8 Advance diffractometer. The roasting process was carried out in a laboratory tube furnace at a temperature of 550–800°C for 60–120 minutes with the addition of 25–50% of FeS 2 to the charge. Optimal conditions for reducing residual arsenic in the calcine to less than 0.3 wt% were identified: a temperature of 750–800°C, a duration of 1.5–2.0 h (in an inert atmosphere), and the use of 30 wt% of pyrite concentrate in the charge. Arsenic removal to the gas phase reached 91–96%. It is shown that in order to reduce the processing temperature to 600°C, it is necessary to add a reducing agent (coke fines) to the mixture of copper smelting dust with pyrite or increase the proportion of pyrite in the test charge to 50 wt% and hold the mixture for 1.5–2.0 h under inert atmosphere (argon and nitrogen) or low-oxygen blast. Arsenic removal to the gas phase reached 97%. X-ray spectral analysis of the residue deposited on the cooled ends of quartz tubes following the release of gases formed during roasting revealed that this material is predominantly (up to 93%) composed of arsenic. The resulting calcine contained 94 wt% of iron, zinc, copper and lead compounds. Therefore, the calcine obtained during the roasting of fine dust from copper smelting production is suitable for returning to the copper production process.

Removal of Copper from Fe–Cu Alloy by Using Iodine

Cu Evaporation from Liquid Iron Alloy in Stream

Experimental Study on Separation of Iron and Arsenic from Copper Sulfate Solution

In Situ XANES Studies on Extracted Copper from Scrap Cu/ITO Thin Film in an Ionic Liquid Containing Iodine/Iodide

Recovery of Cu-Fe Alloy from Copper Smelting Slag

Removal of arsenic from dusts produced during the pyrometallurgical refining of copper by vacuum carbothermal reduction

Iron and copper recovery from copper slags through smelting with waste cathode carbon from aluminium electrolysis

Removal of Arsenic During Iron Extraction from Waste Copper Slag

Co-treatment of copper electrolytic sludges and copper scraps for the recycled utilization of copper and arsenic

Iodine-Based Sensitization of Copper Alloys to Enable Self-Terminating Etching for Support Removal and Surface Improvements of Additively Manufactured Components

Reduction of Copper Smelting Slag by Carbon for Smelting Cu-Fe Alloy

Comparative Analysis of Lead Removal from Liquid Copper by ICF and CCF Refining Technologies

Leaching and removal of arsenic with waste acids from arsenic pre-removed dusts discharged from furnaces for pyrometallurgical refining of copper

Differential Removal of Copper and Iron from Acidic Polymetallic Aqueous Solutions

Effect of roasting parameters on arsenic removal from copper smelting dust

An efficient approach to utilize copper smelting slag: Separating nonferrous metals and reducing iron oxide at high temperature

Phase Transformation of Impurity Elements and High-efficiency Impurity Removal in Complex Copper Concentrate Smelting Process

Breaking the Fe3O4-wrapped copper microstructure to enhance copper–slag separation

An approach of cobalt recovery from waste copper converter slags using pig iron as capturing agent and simultaneous recovery of copper and tin

A Novel Method to Remove Iron Impurity from Aluminum

Recovery of copper from refining slags of copper fire anode furnace by waste acid leaching and CaO roasting process